UNIVERSITÉ CATHOLIQUE DE LOUVAIN
ECOLE POLYTECHNIQUE DE LOUVAIN
Octobre 2019
Crystal plasticity modelling of thermomechanical fatigue
in ITER relevant tungsten
Dissertation présentée par
Aleksandr Zinovev
Ingénieur,
pour l’obtention du grade de
docteur en Sciences de l’Ingénieur
Composition du jury
Pr. Laurent DELANNAY (promoteur) UCLouvain, Belgique
Pr. Thomas PARDOEN UCLouvain, Belgique
Dr. Dmitry TERENTYEV SCK•CEN, Belgique
Pr. Aude SIMAR UCLouvain, Belgique
Pr. Marc SEEFELDT KU Leuven, Belgique
Pr. Reinhard PIPPAN ÖAW, Autriche
Pr. Hervé JEANMART (Président du jury) UCLouvain, Belgique
The research was performed at:
Belgian Nuclear Research Centre SCK•CEN
Institute for Nuclear Materials Science Boeretang 200
2400 Mol, Belgium https://sckcen.be/
Université catholique de Louvain Institute of Mechanics, Materials
and Civil Engineering Av. Georges Lemaître 4
1348 Louvain-la-Neuve, Belgium https://uclouvain.be/
The work was supported by:
EUROfusion Boltzmannstr. 2
85748 Garching, Germany https://www.euro-fusion.org/
SCK•CEN Academy for Nuclear Science and Technology
Boeretang 200
2400 Mol, Belgium https://academy.sckcen.be/
Email: aleksandr.zinovev@sckcen.be
i
Acknowledgments
I wish to express my deepest gratitude to my SCK•CEN mentor Dr. Dmitry
Terentyev for giving me the opportunity to carry out this joint Ph.D. project,
invaluable help and support from day one, introduction to the world of fusion,
fruitful scientific discussions and encouragement to keep on going.
I gratefully thank my university promoter Prof. Laurent Delannay for a solid
support, clear guidance and regular meetings in person, his scientific passion, a
lot of patience and immense knowledge that he readily shared, motivating me to
grow as a researcher. The software developed by him played a key role in the
CPFEM simulations that I carried out.
My acknowledgements go to SCK•CEN and the SCK•CEN Academy for providing
the opportunity to do this doctoral research and for the funding of participation
in conferences, which played a significant role in disseminating my scientific
results and building the collaboration network.
The project has been carried out within the framework of the EUROfusion
Consortium. I acknowledge the funding received from the Euratom research and
training programme 2014–2018 and 2019-2020 under grant agreement No
633053.
I would also like to address my sincere gratitude to Prof. Reinhard Pippan, Prof.
Marc Seefeldt, Prof. Thomas Pardoen, Prof. Aude Simar and Prof. Hervé Jeanmart,
who have kindly accepted to review my thesis, for their questions and feedback,
which have helped me greatly in improving the manuscript.
Special thanks to Odette Wouters, Kirsten Huysmans, Els Jansen, Astrid Leduc,
Laurence Bertrand, Emilie Brichart and Christine Vergeynst for handling the
practical matters and paperwork with the highest efficiency.
Many people from SCK•CEN have significantly contributed to my work, and I am
grateful to Dr. Giovanni Bonny, Dr. Nicolas Castin, Dr. Alexander Bakaev, Dr.
Serguei Gavrilov, Dr. Petr Grigorev, Dr. Andrii Dubinko, Dr. Konstantza
Lambrinou, Dr. Anastasiia Bakaeva and Chao Yin for showing me around,
especially in the beginning of my project, for the scientific (and not-so-scientific)
discussions we have had, for efficient team-work related to our publications and
for a positive environment to work in, which truly contributed to my pleasure to
come to work every day.
ii
My sincere thanks goes to Prof. Sergey Dmitriev from Institute for Metals
Superplasticity Problems (Russia) for leading me into the realm of
computational science during my master’s studies and for the wise advice to do
an internship in this field in Belgium, which was crucial in my final decision to
enrol in the Ph.D. program at SCK•CEN and UCLouvain.
Last but not least, this work would certainly be impossible without the support I
was receiving from my family, the love and endless patience of my dear Izas, and
the fun my friends were sharing during all these not so easy years. Thank you all
very much for giving me confidence in my endeavour.
Mol, October 2019
Aleksandr Zinovev
iii
Abstract
This work contributes to a better understanding of the micromechanics of
tungsten during cyclic heat loads of plasma-facing components in the ITER fusion
reactor. Colossal energy will have to be extracted from the reaction chamber and
the temperature of the walls will oscillate together with periodical changes of
plasma intensity. This research addresses thermomechanical fatigue, i.e.
microscopic cracking due to repeated cycles of thermal expansion and
compression. The effect of neutron irradiation damage is not accounted for, but
the proposed model applies to thermal shock tests, which are used for the
qualification of ITER-relevant tungsten grades.
The computational model relies on crystal plasticity theory in order to account
for the anisotropy of individual grains. The sensitivity of the mechanical
response to strain rate and temperature is reproduced by considering thermally
activated dislocation slip. The influence of internal stresses during repeated
elastic-plastic transients is investigated using a simplified modelling of the
kinematic hardening due to dislocation pile ups at grain boundaries. The model
is implemented as a user-defined material law for the Abaqus finite element
code, allowing crystal plasticity based finite element modelling (CPFEM). Fatigue
indicators are defined to predict the onset of damage whereas cohesive elements
are used to simulate the propagation of intergranular cracks.
Based on an inverse finite element analysis, it is shown that experimental tensile
test data can be reproduced with a limited set of parameters and then applied to
as-received and recrystallized tungsten up to 1700 °C. Recrystallized tungsten
shows significant asymmetry in the mechanical response during the heating and
cooling phases. CPFEM predicts substantial inter- and intragranular
heterogeneity and the fatigue indicator values probed at grain boundaries
depend largely on the amplitude of backstresses. The occurrence of
intergranular cracks is influenced by grain shape as well as the orientation with
regard to the thermal flux. Experimentally observed foil delamination is properly
reproduced only when accounting for crystalline anisotropy. The model
predictions agree qualitatively with the outcome of thermal shock tests.
v
Contents
Acknowledgments ..................................................................................... i
Abstract ...................................................................................................... iii
Contents ....................................................................................................... v
List of publications ................................................................................. ix
Publications on this topic ........................................................................... ix
Publications on other topics ...................................................................... ix
List of acronyms ...................................................................................... xi
List of figures .......................................................................................... xiii
List of tables ............................................................................................ xxi
Chapter 1. Introduction ..................................................................... 1
1.1 Context .................................................................................................... 1
1.1.1 Energy demand in the world ............................................................................. 1 1.1.2 Nuclear fusion .......................................................................................................... 3
1.1.2.1 Fusion in a nutshell ........................................................................................ 3 1.1.2.2 Commercially attractive fusion reaction and fuel ............................ 5 1.1.2.3 How to achieve fusion on Earth? ............................................................. 6 1.1.2.4 Achievements and records in fusion ...................................................... 8
1.1.3 ITER operational conditions .............................................................................. 9 1.1.3.1 The role of divertor ........................................................................................ 9 1.1.3.2 Selected plasma scenario and the plasma-wall interaction ...... 11
1.2 Tungsten as a material for fusion reactors .............................. 12
1.2.1 ITER-specification tungsten ........................................................................... 13 1.2.1.1 Tungsten in the recrystallized state .................................................... 15
1.2.2 Mechanical properties under monotonic loading ................................. 16 1.2.3 Mechanical response of tungsten under cyclic loading ...................... 18
1.2.3.1 Overview of heat load tests ..................................................................... 18 1.2.3.2 High heat flux test ........................................................................................ 20 1.2.3.3 Thermal shock test ...................................................................................... 20
vi
1.3 Overview of techniques ................................................................... 22
1.3.1 Numerical analyses of heat load tests ........................................................ 22 1.3.2 Consideration of cyclic deformation under J2 plasticity theory ...... 24
1.3.2.1 The Bauschinger effect .............................................................................. 24 1.3.2.2 J2 plasticity model ........................................................................................ 24 1.3.2.3 Isotropic and kinematic hardening ...................................................... 25
1.3.3 Deformation of polycrystals at the microscale ....................................... 28 1.3.3.1 What is crystal plasticity? ........................................................................ 28 1.3.3.2 Relevant application of CPFEM in literature ................................... 30 1.3.3.3 Kocks-Mecking model of plasticity ...................................................... 31
1.3.4 Tensile tests ........................................................................................................... 32 1.3.5 Scanning electron microscope and electron backscatter diffraction
..................................................................................................................................... 35 1.3.6 Transmission electron microscope ............................................................. 35
1.4 Outline of the thesis and the addressed questions ............... 36
Chapter 2. Applicability of the Kocks-Mecking model to
temperature- and strain rate-sensitive uniaxial deformation of
ITER-specification tungsten ............................................................... 39
2.1 Introduction ........................................................................................ 39
2.2 Plasticity model and numerical techniques ............................ 41
2.2.1 Temperature- and strain-rate dependent hardening law ................. 41 2.2.2 Finite element simulation of tensile test beyond the onset of
deformation instability ..................................................................................... 44 2.2.3 Optimisation algorithm ..................................................................................... 45
2.2.3.1 Basics of downhill simplex method ..................................................... 45 2.2.3.2 IFEA based on the downhill simplex method .................................. 46
2.3 Results ................................................................................................... 49
2.3.1 Experimental tensile tests ............................................................................... 49 2.3.2 Results of inverse finite element analysis ................................................ 52
2.3.2.1 As-received tungsten.................................................................................. 52 2.3.2.2 Recrystallized tungsten ............................................................................. 54
2.4 Discussion ............................................................................................ 59
2.4.1 Strain-rate sensitivity ........................................................................................ 59 2.4.2 Deformation stage IV ......................................................................................... 60
2.4.2.1 Deviation from the Voce equation ........................................................ 60 2.4.2.2 What is deformation stage IV? ............................................................... 61 2.4.2.3 Evidence of deformation stage IV in tungsten ................................ 63
2.4.3 Individual curve fitting with the iterative algorithm ........................... 65
2.5 Conclusion ............................................................................................ 70
vii
Chapter 3. Development of a crystal plasticity model
accounting for backstresses ............................................................... 71
3.1 Introduction ........................................................................................ 71
3.2 Context .................................................................................................. 73
3.3 Workflow of the suggested two-scale simulation scheme .. 74
3.4 Crystal plasticity framework......................................................... 75
3.4.1 What is crystal plasticity theory? ................................................................. 75 3.4.2 Traditional crystal plasticity for polycrystals ......................................... 76 3.4.3 Mathematical formulation of the grain-level plasticity law ............. 77
3.5 Identification of material parameters ....................................... 81
3.6 Results ................................................................................................... 85
3.6.1 Identification of model parameters based on uniaxial tensile tests
..................................................................................................................................... 85 3.6.1.1 As-received tungsten.................................................................................. 85 3.6.1.2 Recrystallized tungsten ............................................................................. 87
3.6.2 Isothermal mechanical cycles ........................................................................ 89 3.6.2.1 As-received tungsten.................................................................................. 89 3.6.2.2 Recrystallized tungsten ............................................................................. 90
3.6.3 Macroscopic thermal shock simulation ..................................................... 90 3.6.4 Microscopic thermal shock simulation ...................................................... 93
3.6.4.1 As-received tungsten.................................................................................. 93 3.6.4.2 Recrystallized tungsten ............................................................................. 94
3.7 Discussion ............................................................................................ 96
3.7.1 Effect of kinematic hardening ........................................................................ 96 3.7.2 Note on the mixed hardening case............................................................... 98
3.8 Conclusion ......................................................................................... 100
Chapter 4. Damage evolution and failure of tungsten at the
microscopic level in thermomechanical fatigue conditions. . 101
4.1 Introduction ..................................................................................... 101
4.1.1 The need of CPFEM .......................................................................................... 101 4.1.2 Overview of CPFEM theory .......................................................................... 102 4.1.3 Indicators of fatigue ........................................................................................ 102 4.1.4 Overview of the chapter ................................................................................ 105
4.2 FEA setup ........................................................................................... 106
4.2.1 Crystal plasticity — standalone and CPFEM ........................................ 106 4.2.2 Cohesive elements............................................................................................ 107 4.2.3 Analysis of mesh sensitivity ......................................................................... 109
viii
4.2.4 Mesh of polycrystals used in the work.................................................... 114
4.3 Analysis of fatigue damage in recrystallized tungsten using
cohesive elements .......................................................................... 115
4.3.1 Results ................................................................................................................... 116 4.3.2 A note on the stress in cohesive elements ............................................. 122 4.3.3 Conclusions of the section ............................................................................ 123
4.4 Analysis of fatigue damage in as-received tungsten using the fatigue indicator ...................................................................... 124
4.4.1 Results ................................................................................................................... 124
4.5 The effect of crystalline anisotropy on grain delamination
............................................................................................................... 129
4.6 Discussion ......................................................................................... 134
4.6.1 Taylor-based CP and CPFEM simulations of thermal shock .......... 134 4.6.2 Cohesive elements and fatigue indicator ............................................... 134 4.6.3 The use of tensile tests to derive the threshold fatigue indicator
.................................................................................................................................. 135
4.7 Conclusion ......................................................................................... 136
Chapter 5. Conclusions and perspectives ................................ 139
5.1 Summary and conclusions .......................................................... 139
5.2 Perspectives ..................................................................................... 141
Bibliography ......................................................................................... 143
ix
List of publications
Publications on this topic
1) A. Zinovev, D. Terentyev, L. Delannay, Finite element analysis of heat
load of tungsten relevant to ITER conditions, Phys. Scr. T170 (2017) 014002.
doi:10.1088/0031-8949/2017/T170/014002.
2) A. Zinovev, D. Terentyev, A. Dubinko, L. Delannay, Constitutive law for
thermally-activated plasticity of recrystallized tungsten, J. Nucl. Mater. 496
(2017) 325–332. doi:10.1016/j.jnucmat.2017.09.044.
Publications are under preparation about
the use of inverse finite element analysis to process experimental stress-
strain curves with low uniform elongation (Chapter 2)
improvement of the CP model to account for continuously evolving
temperature, non-zero athermal stress of BCC metals and the effect of
backstresses (Chapter 3)
application of CPFEM to investigate the damage accumulation under
conditions of thermal shock (Chapter 4)
Publications on other topics
3) D. Terentyev, A. Zinovev, G. Bonny, Displacement cascades in Fe-Ni-Mn-
Cu alloys: RVP model alloys, J. Nucl. Mater. 475 (2016) 132–139.
doi:10.1016/j.jnucmat.2016.04.005.
4) G. Bonny, D. Terentyev, J. Elena Gonzales, A. Zinovev, B. Minov, E.E.
Zhurkin, Assessment of hardening due to dislocation loops in bcc iron: Overview
and analysis of atomistic simulations for edge dislocations, J. Nucl. Mater. 473
(2016) 283–289. doi:10.1016/j.jnucmat.2016.02.031.
5) A. V. Zinovev, M.G. Bapanina, R.I. Babicheva, N.A. Enikeev, S. V. Dmitriev,
K. Zhou, Deformation of nanocrystalline binary aluminum alloys with
segregation of Mg, Co and Ti at grain boundaries, Phys. Met. Metallogr. 118
(2017) 65–74. doi:10.1134/S0031918X16110144.
6) P. Grigorev, A. Zinovev, D. Terentyev, G. Bonny, E.E. Zhurkin, G. Van
Oost, J.-M. Noterdaeme, Molecular dynamics simulation of hydrogen and helium
trapping in tungsten, J. Nucl. Mater. 508 (2018) 451–458.
doi:10.1016/j.jnucmat.2018.05.052.
x
7) D. Terentyev, J. Riesch, S. Lebediev, T. Khvan, A. Zinovev, M. Rasiński, A.
Dubinko, J.W. Coenen, Plastic deformation of recrystallized tungsten-potassium
wires: Constitutive deformation law in the temperature range 22–600 °C, Int. J.
Refract. Met. Hard Mater. 73 (2018) 38–45. doi:10.1016/j.ijrmhm.2018.01.012.
8) X. Xiao, D. Terentyev, A. Ruiz, A. Zinovev, A. Bakaev, E.E. Zhurkin, High
temperature nano-indentation of tungsten: Modelling and experimental
validation, Mater. Sci. Eng. A. 743 (2019) 106–113.
doi:10.1016/j.msea.2018.11.079.
9) A. Bakaeva, V. Makhlai, D. Terentyev, A. Zinovev, S. Herashchenko, A.
Dubinko, Correlation of hardness and surface microcracking in ITER
specification tungsten exposed at QSPA Kh-50, J. Nucl. Mater. 520 (2019) 185–
192. doi:10.1016/j.jnucmat.2019.04.008.
10) X. Xiao, D. Terentyev, A. Bakaev, A. Zinovev, A. Dubinko, E.E. Zhurkin,
Crystal plasticity finite element method simulation for the nano-indentation of
plasma-exposed tungsten, J. Nucl. Mater. 518 (2019) 334–341.
doi:10.1016/j.jnucmat.2019.03.018.
11) A. Bakaev, A. Zinovev, D. Terentyev, G. Bonny, C. Yin, N. Castin, Yu.
Mastrikov, E. Zhurkin, Interaction of carbon with microstructural defects in a W-
Re matrix: an ab initio assessment, J. Appl. Phys. 126 (2019) 075110.
doi:10.1063/1.5094441.
12) A. V. Zinovev, A. M. Iskandarov, S. V. Dmitriev, A. I. Pshenichnyuk,
Criteria of instability of copper and aluminium perfect crystals subjected to
elastic deformation in the temperature range 0 – 400 K, Lett. Mater. 9(3) (2019)
265–269. doi:10.22226/2410-3535-2019-3-265-269.
xi
List of acronyms
ASTM standards Standards developed by ASTM International, an
organization formerly known as American Society for
Testing and Materials
BCC Body-Centred Cubic (lattice type)
BR2 The Belgian Reactor 2
CE Cohesive Element
CP Crystal Plasticity
CPFEM Crystal Plasticity based Finite Element Modelling
CRSS Critical Resolved Shear Stress
CZ Cohesive Zones
DBTT Ductile-to-Brittle Transition Temperature
DFR Double-Forged Recrystallized (tungsten grade)
dpa Displacements Per Atom
EBSD Electron Backscatter Diffraction
EDM Electrical Discharge Machining
ELM Edge-Localised Mode (plasma instability type)
ESS European Spallation Source
FCC Face-Centred Cubic (lattice type)
FEA Finite Element Analysis
FEM Finite Element Method
FIP Fatigue Indicator Parameter
GB Grain Boundary
HPT High Pressure Torsion
IGP ITER-Grade Plansee (tungsten grade)
IFEA Inverse Finite Element Analysis
ITER (“The way” in Latin) is the largest tokamak under
construction, formerly known as “International
Thermonuclear Experimental Reactor”
JET Joint European Torus
xii
MRI Magnetic Resonance Imaging
PFC Plasma-Facing Components
QSPA Quasistationary Plasma Accelerator
RVE Representative Volume Element
S-S curve Stress-Strain curve
SCK•CEN Studiecentrum voor Kernenergie•
Centre d’étude de l’Energy Nucleaire
SEM Scanning Electron Microscopy
SOL Scrape-Off Layer
TEM Transmission Electron Microscopy
TSL Traction-Separation Law
UMAT A User-defined MATerial subroutine for the standard
finite element solver Abaqus
UTS Ultimate Tensile Strength
XFEM eXtended Finite Element Method
XRD X-Ray Diffraction
xiii
List of figures
Figure 1.1. Nuclear binding energy per nucleon as a function of the atomic mass
[1]. ............................................................................................................................................................ 4
Figure 1.2. Potential energy as a function of the distance between two charged
nuclei [6]. .............................................................................................................................................. 5
Figure 1.3. Fusion cross-section of various fusion reactions as a function of
kinetic energy of an incident D or p+ on a stationary target [7]. ................................. 6
Figure 1.4. Magnetic fields in a tokamak. From left to right: toroidal component,
poloidal component and resulting helical magnetic lines [10]. ................................... 7
Figure 1.5. a) A schematic picture of ITER’s vacuum chamber [10,19]. Tungsten
is shown with red colour. Black lines represent an example of magnetic field lines
in the core plasma and a separatrix. The light pink region between the separatrix
and the walls of the chamber represents the divertor plasma layer. b) A divertor
cassette and its parts [20]. c) A plasma-facing unit: tungsten monoblocks
assembled on a cooling pipe [21]. .......................................................................................... 10
Figure 1.6. The monoblock geometry, the cross-section of the CuCrZr cooling
pipe and the Cu interlayer. Note the bevelling of 0.5 mm introduced to reduce
thermal load on the right edge of the monoblock by shadowing it with a
neighbouring monoblock to the right. Dimensions are in mm [22]. ....................... 10
Figure 1.7. Schematic representation of the normal operation with temperature
excursions during transient heat loading. Lower temperature range is defined by
the DBTT, while the upper range is limited by the recrystallization temperature
[1]. ......................................................................................................................................................... 11
Figure 1.8. Schematic view of a typical W monoblock indicating its
microstructure and typical dimensions [31]. .................................................................... 13
Figure 1.9. a) A fabricated bar of tungsten with indicated macroscopic directions;
b) a TEM image of microstructure of as-received tungsten; c) an EBSD map of as-
received tungsten; d) an EBSD map of recrystallized tungsten. ............................... 14
Figure 1.10. Metallographic cross-section in the centre of tungsten mock-up
subjected to 20 MW m-2 in a high heat flux test, showing the layer recrystallized
due to high thermal load [34]. .................................................................................................. 15
Figure 1.11. Divertor mock-up after exposure to a high heat flux [34]. ................ 19
Figure 1.12. Damage mapping of tungsten samples exposed to ELM-like thermal
shocks. Plain-coloured symbols stand for samples with 100 thermal shock
xiv
pulses. Symbols with a black centre stand for samples exposed to 1000 pulses
[26]. ...................................................................................................................................................... 21
Figure 1.13. Illustration of the Bauschinger effect in reversed loading. The yield
stress in compression is lower than the stress achieved prior the load reversal.
[90]. ...................................................................................................................................................... 24
Figure 1.14. Effect of strain hardening on the yield locus. The cross-section of the
locus in the x – y plane is shown. The isotropic model (a) corresponds to an
expansion of the locus. The kinematic hardening model (b) corresponds to a
translation of the locus in the direction of the loading path [89]. ............................ 26
Figure 1.15. Linear arrays of edge dislocations piled-up against barriers under
an applied shear stress [100]. ............................................................................................. 27
Figure 1.16. Comparison between a strain controlled fatigue test and a
monotonic tensile test of polished forged tungsten at 480 °C [59]. ........................ 28
Figure 1.17. (a) Sketch of a miniaturized dog-bone-shape tensile sample, and (b)
photo of a sample before and after tensile test. ............................................................... 33
Figure 1.18. A sample in the furnace of the Instron machine. The thermocouple
wires are attached to the gauge section of the sample. ................................................ 33
Figure 1.19. Examples of two main types of stress-strain curves encountered in
the present work: a) low uniform elongation, “early necking”, b) high uniform
elongation. The thick lines highlight the range of applicability of the standard
approach to extract true stress and strain.......................................................................... 34
Figure 2.1. A tensile sample used in FE analysis a) in the non-deformed state; b)
at the onset of deformation instability. Colours represent the von Mises stress,
ranging from 0 (in the grips) to 400 MPa (in the centre). ........................................... 45
Figure 2.2. Flowchart of the iterative algorithm for the plasticity model fitting to
multiple stress-strain curves simultaneously. .................................................................. 47
Figure 2.3. Illustration for the evaluation of the objective function. The sum of
squares of differences is calculated at a discrete set of strain values, marked with
circles. Both the engineering stress (a) and the stress-strain slope (b) contribute
to the total value of the objective function. The arrows indicate that as the
simulation result approaches the target, the objective function decreases. ....... 48
Figure 2.4. The evolution of a) input true S-S curves, b) output engineering S-S
curves in several iterations of the search algorithm. ..................................................... 49
Figure 2.5. Engineering stress-strain curves for as-received IGP tungsten. Solid
lines highlight the range of uniform deformation. .......................................................... 50
Figure 2.6. Engineering stress-strain curves for the recrystallized tungsten. .... 51
Figure 2.7. a) Yield stress and ultimate tensile strength as well as b) uniform
elongation and total elongation of both grades of tungsten tested at 6·10-4 s-1. 51
xv
Figure 2.8. The best fit of equation (2.1) to the yield stress of as-received IGP
tungsten at different temperatures and strain rates...................................................... 52
Figure 2.9. True stress-strain curves of as-received IGP tungsten obtained with
the help of IFEA of tensile test.................................................................................................. 53
Figure 2.10. Engineering stress-strain curves obtained in the last iteration of the
IFEA of tensile test for as-received IGP W, compared to the experimental data.
................................................................................................................................................................ 53
Figure 2.11. Yield stress of recrystallized W. Symbols represent experimental
data, and lines highlight its evolution with temperature at given strain rates,
obtained using two different fitting functions. ................................................................. 55
Figure 2.12. Experimental true stress-strain curves of recrystallized tungsten.
................................................................................................................................................................ 56
Figure 2.13. Hardening rate derived from experimental true stress-strain curves
of recrystallized IGP tungsten .................................................................................................. 56
Figure 2.14. Experimental and fitted true stress-strain curves for recrystallized
IGP tungsten at strain rate 6·10-4 s-1. ..................................................................................... 58
Figure 2.15. Experimental and simulated engineering stress-strain curves at
500 °C and 600 °C for recrystallized tungsten. ................................................................. 58
Figure 2.16. Illustration of rate sensitivity of tungsten (other than IGP) in a wide
range of strain rate, showing the true stress at 4% of strain as a function of strain
rate [146]. .......................................................................................................................................... 59
Figure 2.17. Strain rate sensitivity for Cu deformed in compression at 25°C,
shown as the stress at 15% of strain as a function of strain rate. [101]. .............. 60
Figure 2.18. Hardening rate as a function of true stress indicates the presence of
deformation stages III and IV (solid line). Hardening rate derived from the
standard Voce equation is shown by the dashed line for clarity. ............................. 61
Figure 2.19. (a) Engineering stress-strain curves and (b) hardening rate for
different grades of recrystallized tungsten obtained by uniaxial tensile tests at
500 °C [1,26]..................................................................................................................................... 62
Figure 2.20. TEM micrographs showing dislocation tangles (a, b) and dislocation
cells (c), probed by TEM at 20% (a, b) and 28%(c) of plastic strain in the DFR
tungsten. The grain refinement was observed in the tests performed at 500 °C
and 600 °C after 20% plastic strain. Zones I in the images show examples of the
grain interior, while zones II correspond to dislocation tangles where the
dislocation density was measured [120]............................................................................. 64
Figure 2.21. Dislocation density predicted by the model superimposed on the
experimental data from [115]. ................................................................................................. 65
Figure 2.22. Flowchart of the iterative algorithm for the Voce equation fitting to
a single stress-strain curve. ....................................................................................................... 66
xvi
Figure 2.23. Engineering stress-strain curves, as a result of FE simulation of a
tensile test, using the best constitutive laws obtained with the help of individual
curve fitting. Dashed lines show corresponding experimental results. ................ 67
Figure 2.24. The Voce parameters 0 (a) and sat (b) as a function of
temperature, obtained in the IFEA of individual experimental S-S curves. ......... 68
Figure 2.25. The Voce parameters 0 (a) and sat (b) as a function of
temperature, obtained in the IFEA of multiple experimental S-S curves. ............ 69
Figure 3.1. Stress-strain loops obtained in low cycle fatigue tests of forged
tungsten at 500 °C (other than IGP) [59] and the results of fitting of a J2
Armstrong-Frederick model of kinematic hardening. ................................................... 72
Figure 3.2. Schematic representation of the three types of samples used in the
thermal shock experiment [26]. .............................................................................................. 73
Figure 3.3. On the evaluation of the objective function. The squares of differences
between experimental and simulated values of stress are summed over three
points per curve and then are summed over all 15 stress-strain curves. ............. 83
Figure 3.4. Illustration of construction of the three cases of hardening. .............. 84
Figure 3.5. True deformation curves obtained in simulations of tensile test with
the crystal plasticity model and the best parameter sets for three hardening
cases. .................................................................................................................................................... 86
Figure 3.6. Evolution of dislocation density in the simulated polycrystal of as-
received tungsten with the best parameter sets for three hardening cases. ...... 87
Figure 3.7. True stress-strain curves obtained in uniaxial tension with the CP
model of recrystallized tungsten (dashed) superimposed on the experimental
curves (solid). .................................................................................................................................. 88
Figure 3.8. True stress-strain curves at high temperature and the limiting values
of strain rate, demonstrating the applicability domain of the model of
deformation of recrystallized tungsten. ............................................................................... 88
Figure 3.9. Stress-strain loops obtained in simulations of mechanical isothermal
cyclic loading of as-received tungsten. ................................................................................. 89
Figure 3.10. Stress-strain loops obtained in simulations of mechanical isothermal
cyclic loading of recrystallized and as-received tungsten. .......................................... 90
Figure 3.11. FE mesh of the sample studied in JUDITH1 facility for a macroscopic
thermo-mechanical simulation. The colour indicates temperature field at the end
of heat flux exposure, with the blue colour corresponding to the base
temperature, 400 °C, and the red - to the maximal attained temperature ~750 °C.
................................................................................................................................................................ 91
Figure 3.12. Evolution of temperature and the von Mises strain in the centre of
the heated area exposed to an ELM-like thermal shock of 190 MW m-2. .............. 91
xvii
Figure 3.13. Normal stress components in the centre of the sample exposed to
380 MW m-2 as a function of (a) time and (b) temperature. The only non-zero
components are S11 and S22, indicating a plane-stress state. .................................. 92
Figure 3.14. Schematic view of the simulation box in the initial and deformed
state. The thermal strain is denoted as . .......................................................................... 93
Figure 3.15. The mechanical response of as-received tungsten (isotropic
hardening only) to thermal shocks of different power density in terms of the in-
plane stress vs. the out-of-plane strain. ............................................................................... 94
Figure 3.16. The mechanical response of recrystallized tungsten to thermal
shocks of different power density in terms of the in-plane stress vs. the out-of-
plane strain. ...................................................................................................................................... 95
Figure 3.17. Stress-strain loops recorded in the as-received tungsten for the
three considered material laws. .............................................................................................. 96
Figure 3.18. Evolution of the in-plane tensile stress amplitude obtained in the as-
received tungsten for the three considered material laws. ......................................... 97
Figure 4.1. Representation of polycrystals in CPFEM framework. a) Simplified 3D
grain assembly [186], b) advanced grain assembly obtained with the help of the
Voronoï tessellation [187]. ..................................................................................................... 107
Figure 4.2. a) A diagram illustrating the use of cohesive elements in a crack
propagation problem. b) Example of a traction-separation law, normalised by the
maximal cohesive stress 0T and maximal cohesive separation 0 [197]. ........ 108
Figure 4.3. Maximal principal stress distribution in “bricks” with different level
of refinement: coarse (a, b), medium (c, d) fine (e, f), and element type: C3D8 in
“simple bricks” (a, c, e) and C3D10 in “Gmsh-generated bricks” (b, d, f) ........... 109
Figure 4.4. A boxplot shows schematically five main reference points of a smooth
distribution of stress in cohesive elements. .................................................................... 110
Figure 4.5. Distribution of normal stress in CZ (open boxes) and maximal
principal stress in grain interior (filled boxes) in a) “simple bricks” and b) “Gmsh-
generated bricks” with different mesh refinement at 30% of tensile strain. Each
colour of the filled boxes corresponds to one of the 13 grains. .............................. 112
Figure 4.6. Effect of cohesive element stiffness on the stress distribution in
cohesive elements and grain interior of a Gmsh-generated brick with medium-
size elements. Each colour of the filled boxes corresponds to one of the 27 grains.
............................................................................................................................................................. 113
Figure 4.7. The finite element meshes used in the simulations of thermal fatigue
with CPFEM, a) transversal with respect to the heat flux, b) longitudinal, c)
equiaxed. ......................................................................................................................................... 114
Figure 4.8. Stress-strain loops as a result of simulation of thermal shock on the
surface of the recrystallized tungsten (equiaxed grains).......................................... 116
xviii
Figure 4.9. Stress-strain loops as a result of simulation of thermal shock on the
surface of the recrystallized tungsten (elongated grains). ....................................... 117
Figure 4.10. The evolution of normal stress distribution in the GBs of polycrystal
with equiaxed grains in the first two thermal shocks. ............................................... 118
Figure 4.11. The evolution of normal stress distribution in the GBs of polycrystal
with elongated grains in the first three thermal shocks. ........................................... 119
Figure 4.12. The evolution of shear stress distribution in the GBs of polycrystal
with elongated grains in the first two thermal shocks. .............................................. 120
Figure 4.13. The evolution of normal stresses in the first two thermal pulses in
recrystallized tungsten exposed to 380 MW m-2 thermal power density at base
temperature 27 °C. a) Elongated grains, b) equiaxed grains. .................................. 121
Figure 4.14. Distribution of the angle between cohesive elements and the heated
surface in the three considered meshes. .......................................................................... 122
Figure 4.15. Correlation between normal stress in cohesive elements and their
orientation. .................................................................................................................................... 122
Figure 4.16. The average in-plane stress and out-of-plane strain in the
polycrystal subjected to thermal shocks at different base temperature and
absorbed power density. ......................................................................................................... 125
Figure 4.17. The average FIP in the whole polycrystal with the L orientation
tested at different base temperature and applied power density. ........................ 126
Figure 4.18. Distribution of microscopic FIP in two selected grains at the end of
ten thermal shocks of 380 MW m-2. .................................................................................... 127
Figure 4.19. FIP distribution in individual grains after ten thermal shocks with
power density 380 MW m-2 at base temperature 1000 °C in polycrystal with
mixed hardening.......................................................................................................................... 128
Figure 4.20. Distribution of normal stress in the cohesive elements within the
first two thermal shocks of 380 MW m-2 at base temperature 1000 °C applied to
the material with the mixed hardening............................................................................. 128
Figure 4.21. Distribution of normal stress in cohesive zones (open boxes) and
maximal principal stress in grain interior (filled boxes) in three meshes of the
polycrystal with mixed hardening after exposure to ten thermal shocks at base
temperature 1000 °C and power density 380 MW m-2. ............................................. 129
Figure 4.22. a) EBSD maps of pure 0.1 mm tungsten foil projected on a cuboid to
better visualize the pancake-like microstructure. Black lines denote the initial
notch [40]. b) An example of the foil delamination occurred at 400 °C [40]. c) A
polycrystal composed of prismatic grains to represent the microstructure of the
foil in CPFEM simulations. Colour highlights separate grains. d) Embedded
cohesive elements which have different strength, according to their role: GBs
(green) are weaker than the transgranular crack plane (highlighted with red).
............................................................................................................................................................. 130
xix
Figure 4.23. Maps of normal strain inside cohesive elements (LE33) in
simulations with the J2 (a, c, e) and CP (b, d, f) models. The strength of GBs
increases from top to bottom: 50 MPa (a, b), 250 MPa (c, d) and 550 MPa (e, f).
............................................................................................................................................................. 132
Figure 4.24. Distribution of the out-of-plane stress S33 in the grain interior in
simulations with different GB strength. ............................................................................ 133
Figure 4.25. The density of energy dissipated in tensile tests of the as-received
IGP tungsten. ................................................................................................................................. 136
xxi
List of tables
Table 1.1. Impurity content of the IGP tungsten. ............................................................. 13
Table 2.1. Set of parameters reproducing the yield stress of as-received IGP
tungsten. ............................................................................................................................................. 52
Table 2.2. The fitted parameters of the plasticity model for as-received IGP W.
................................................................................................................................................................ 54
Table 2.3. The best fitted parameter set of equation (2.1) to describe yield stress
of recrystallized tungsten. .......................................................................................................... 55
Table 2.4. The best fitted parameter set of equation (2.16) to describe yield stress
of recrystallized tungsten. .......................................................................................................... 55
Table 2.5. The fitted parameters of the plasticity model for recrystallized
tungsten. ............................................................................................................................................. 57
Table 3.1. The CP model parameters independent of hardening type for as-
received tungsten. .......................................................................................................................... 85
Table 3.2. The CP model parameters for the isotropic, kinematic and mixed
hardening cases of as-received tungsten............................................................................. 85
1
Chapter 1.
Introduction Equation Cha pter 1 Section 1
1.1 Context
1.1.1 Energy demand in the world
Thanks to the improvement of the average standard of living, the average power
consumption per person steadily increases, especially in the developing
countries. However, it represents a global challenge as well, amplified by the
population growth. During the last century the total amount of energy used per
year has increased by a factor of ten and the primary source was fossil fuel [1]. A
study by the European climate foundation (ECF) published in 2010 showed that
the yearly power demand of the European countries will increase from 3250
terawatt-hour (TWh) in 2010 to 4800 TWh in 2050 [2].
The increased energy demand requires new sources of clean and sustainable
energy. In 2016 the estimated global final energy demand was provided by three
main energy sources: fossil fuels (79.5%), renewables (18.2%) and nuclear
energy (2.2%) [3]. Fossil fuels, such as petroleum, coal and gas, are non-
renewable, and, even though they are still sufficiently available to satisfy the
constantly increasing energy consumption, they might run out in our lifetime or
their extraction would become economically unfavourable. In 2000 a study
estimated that at the current consumption rates, oil reserves will run out within
25–40 years, coal within 70 years and natural gas reserves in 200 years [1].
Importantly, fossil fuels are found locally on our planet, having major economic
and political consequences, such as significant influence of supplying countries
on the energy cost, political instability, international disagreements and
conflicts. Also, they represent a highly useful mixture of complex chemical
substances, which should efficiently be used in chemical industry for production
of plastic, textiles, composite and advanced materials, instead of being burned.
Energy production from fossil fuels is accompanied by emission of huge amounts
of greenhouse gases, and, in case of poor filtration and processing of exhaust,
toxic substances including dust, leading to climate change, environmental
pollution, deterioration of areas around power plants. In other words, the need
for alternatives is a consequence of the drawbacks of the use of fossil fuels in
energy production.
1. Introduction
2
The two main alternatives used nowadays are renewable energy and nuclear
power. The most important renewable energy source is hydroelectricity that
supplies 3.7% of the energy (or 16.6% of electricity) in the world, but the dams
drastically change the environment and their use should be limited. Other
renewable sources, which include geothermal, solar, tide, wind, wood, biomass
and waste, account for merely several percent of the total energy production [3].
Most of them are indigenous, widespread, and enhance a country’s
independence from external supplies of fossil fuels. However, they suffer from
intermittency (the source is not continuously available) and lack of “on demand”
availability.
Another alternative to fossil fuels, nuclear power generated by fission of heavy
nuclei, does not have this disadvantage. It is a quite efficient, climate friendly and
relatively safe energy source, which produces around 10% of the world’s
electricity nowadays [4]. The energy released by a fission reaction is a million
times larger than that released by a chemical reaction (such as burning) due to
different fundamental forces involved.
The electromagnetic force that holds the atoms together in molecules is much
weaker than the strong nuclear force that binds the protons and neutrons in an
atomic nucleus. Thus, the mass of fuel needed to generate a given amount of
energy in a nuclear power plants is a small fraction of fuel required by a coal or
gas power plant.
Unfortunately, nuclear energy is not free of problems, the most undesirable of
which is long-lived nuclear waste, spent fuel, that has to be securely stored in
special mines for hundreds of thousands of years. All of the used fuel ever
produced by the commercial nuclear industry since the late 1950s would cover
a football field to a depth of less than nine meters. That might seem like a lot, but
coal plants generate that same amount of waste every hour [5].
Another possibility is to reprocess the spent fuel in order to filter out the fission
products and extract the remaining uranium that can further be used as fuel. The
generation IV fission power plants will produce less radioactive waste and new
methods for waste treatment are under development.
A possible solution of this problem is offered by an alternative source of energy
proposed in the 1950s, which is the nuclear fusion, a reaction that powers stars,
including the Sun, in which light nuclei coalesce (“fuse”) into heavier ones,
releasing a colossal amount of energy.
It is more efficient than fission (in terms of the amount of energy released per
gram of fuel), is seen as virtually unlimited alternative energy for the future and
produces neither greenhouse gases nor long-term radioactive waste. The fusion
reaction selected from a range of several theoretically possible reactions, and
anticipated in commercial fusion reactors, does indeed produce high-energy
neutrons as a by-product, which induce radioactivity in the surrounding matter.
However, its negative effect can be significantly minimized by a clever choice of
1. Introduction
3
structural and other materials, thereby only short-lived radioactivity is
produced.
Historically this reaction was first implemented in a hydrogen bomb and since
then the efforts of researchers have been focussed on finding the means to
harness the energy release. Controlled fusion has already been achieved in
numerous devices, the most powerful of which being JET (Joint European Torus),
located in the UK.
The ultimate goal of fusion research is to construct a device where the extraction
of fusion energy would be durable, stable and commercially justified. One of the
key issues to be addressed in the development of a commercial fusion power
plant is the selection of materials, durable enough to enable profitable
exploitation of the device, able to withstand the severe environment imposed by
hot fusion plasma, cyclic high heat load and irradiation with high energy
neutrons.
1.1.2 Nuclear fusion
1.1.2.1 Fusion in a nutshell
Nuclear energy can be gained in two ways, fission and fusion.
Fission is in essence splitting a heavy nucleus into two medium-size
nuclei initiated by an incident neutron. This reaction is exploited in
current nuclear power plants to produce electricity using uranium as
fuel.
Fusion, on the contrary, is merging two light nuclei together into heavier
ones, such as fusing hydrogen into helium.
Fine-scale measurements revealed that the mass of a nucleus is always smaller
than the sum of masses of protons and neutrons constituting the nucleus.
The energy E released in a nuclear reaction corresponds to the difference in
the nuclear binding energy, which in turn corresponds to the mass difference
m according to Einstein’s relation 2E mc . Figure 1.1 shows the nuclear
binding energy per nucleon (proton or neutron), demonstrating that light nuclei
(lighter than iron) release energy in fusion reactions, while the heavier nuclei do
so in fission reactions.
1. Introduction
4
Figure 1.1. Nuclear binding energy per nucleon as a function of the atomic mass [1].
Different mechanisms of the two reaction types lead to different requirements
imposed on the media conditions.
A fission reaction is initiated by a neutron which freely reaches a heavy nucleus
of fuel, destabilizes it, such that the nucleus splits into parts, repelling from each
other with high kinetic energy due to their positive electric charge and releasing
more neutrons which hit other nuclei of fuel thus maintaining the chain reaction.
In order to fuse, two nuclei have to approach each other close enough for the
forces of strong nuclear interaction, which are responsible for the intra-nuclear
processes, to start acting, and this happens only when the nuclei are 10-14–
10-
15 m apart, comparable to the size of a nucleus itself. However, their approach
is significantly hindered by the Coulomb repulsion due to the positive electric
charge of both nuclei.
Figure 1.2 schematically shows the interaction energy between two charged
nuclei vs. the distance between them, demonstrating the Coulomb potential
barrier which has to be overcome in order for these nuclei to undergo a nuclear
reaction, i.e. fusion. A classical estimation of the barrier height results in
tremendous several hundreds of keV which corresponds to the average kinetic
energy of gas molecules heated up to several billion Kelvin! Such temperature is
impossible to reach on Earth in a volume of matter reasonable for commercial
applications. Luckily, quantum mechanics provides the possibility of tunnelling
through the barrier, for which a kinetic energy of colliding nuclei of ~10 keV is
sufficient.
1. Introduction
5
Figure 1.2. Potential energy as a function of the distance between two charged nuclei [6].
1.1.2.2 Commercially attractive fusion reaction and fuel
In stars like the Sun the dominant reaction is the fusion of protons ( 1
1H nuclei)
into 4
2 .He It has a too low rate for commercial application on Earth, given a very
limited volume of plasma available in laboratories or in fusion reactors
compared to the enormous volume of the Sun.
There are several fusion reactions involving hydrogen isotopes such as
deuterium (D) or tritium (T) considered for the use in a fusion reactor, for
instance,
2 2 3 1
1 1 1 11.01MeV 3.02MeVD D T H (1.1)
2 2 3 0
1 1 2 0.82MeV 2.45MeVD D He n (1.2)
2 3 4 1
1 2 2 13.6MeV 14.7MeVD He He H (1.3)
2 3 4 0
1 1 2 3.05MeV 14.1MeVD T He n (1.4)
A measure of the reaction probability is the reaction cross section, which is
shown in Figure 1.3 as a function of the particles kinetic energy. The DT reaction
(1.4) is clearly identified as the most favourable choice with the highest reaction
cross-section and rate at the given conditions.
1. Introduction
6
Figure 1.3. Fusion cross-section of various fusion reactions as a function of kinetic energy of an incident D or p+ on a stationary target [7].
This reaction liberates a neutron of ~14 MeV which escapes from the plasma,
and a 3.5 MeV alpha particle which transfers its kinetic energy to the fuel nuclei
in the plasma, maintaining its temperature.
The fuel components are the hydrogen isotopes, deuterium (D) which is
naturally present in water, and tritium (T), an unstable isotope that has to be
produced artificially. A commercial fusion power plant will be self-sufficient
from the point of view of production of T. High-energy neutrons resulting in the
DT reaction will be used to bombard lithium, placed around the reactor vessel,
to generate more tritium according to the following reactions:
7 0 4 3 0
3 2 12.5MeVnLi n E He T n (1.5)
6 0 4 3
3 2 1 4.8MeVLi n He T (1.6)
Thus the basic fuels for nuclear fusion are lithium and water, both being readily
and widely available on Earth.
1.1.2.3 How to achieve fusion on Earth?
The fusion reaction in the core of the Sun takes place at ~15 MK, where the
hydrogen plasma is compressed by the immense solar gravity up to a density
above 150 g cm-3 [8], whereas the average density of Earth is 5.5 g cm-3, i.e. 27
times lower, [9]. The same approach, gravitational compression, is impossible on
Earth, and other means of the plasma confinement have to be applied, keeping in
mind that no material can withstand the colossal temperature involved.
1. Introduction
7
Two main options are used to solve the problem. One of them is the inertial
confinement, where the fusion plasma is created for fractions of a second from
fuel pellets with the help of powerful laser shots and is confined by its own
inertia only. Another option is provided thanks to the temperature required for
the fusion reaction: at ~100 MK the atoms of hydrogen isotopes are already
completely ionised, i.e., split into separate components - electrons and nuclei.
Due to their electric charge, the particles can be controlled by magnetic fields,
whose strength is comparable to that in medical magnetic resonance imaging
(MRI) scanners. The high-energetic charged particles would follow the magnetic
field lines in spiral trajectories due to the Lorentz force exerted on them.
Consequently, the plasma can be held at a distance from the physical walls of the
reactor vessel, preventing them from evaporating.
Significant technological experience has been obtained using the magnetic
confinement, and a number of ideas has been tried in devices of various design.
The most advanced magnetic confinement concept is implemented in a device
called a tokamak. The name is derived form a Russian acronym that stands for
"toroidal chamber with magnetic coils". The magnetic coils are used to create a
toroidal magnetic field around the torus. A poloidal magnetic field (orthogonal
to the toroidal direction) is created by the toroidal plasma current, which in turn
is induced by changing current in the central solenoid. The resulting magnetic
field lines are spiralled around the torus, that is required for achieving plasma
equilibrium. Toroidal, poloidal and resulting magnetic fields in a tokamak are
schematically shown in Figure 1.4.
Due to the need of changing the current in the central solenoid, tokamaks can
operate in cyclic mode only. In a different design option, called a stellarator, a
poloidal magnetic field is created by external coils, and the device does not
require the plasma current. The calculation of parameters of magnetic coils of
stellarators is onerous and could efficiently be done with the help of
supercomputers only. That is why the development of stellarators has not been
as rapid as that of tokamaks. The advantage of stellarators is the possibility to
work in continuous mode, which significantly reduces the issue of thermal
fatigue of plasma-facing components (PFC). Scientific feasibility of both types of
magnetic confinement has been demonstrated by devices JET (UK) and
Wendelstein 7-X (Germany).
Figure 1.4. Magnetic fields in a tokamak. From left to right: toroidal component, poloidal component and resulting helical magnetic lines [10].
1. Introduction
8
1.1.2.4 Achievements and records in fusion
The experiments with a toroidal configuration of fusion chambers started in
1956 in the USSR with a device called "TMP". The first tokamaks were very small
with the major radius of around 40 cm. Already at that time theoretical design
estimations predicted that a thermonuclear reactor should be as large as
~1000 m3 of plasma volume, corresponding to the major radius of 12 m.
The increase of the device size turned out to be necessary for the improvement
of the three components characterizing the quality of the magnetic confinement
in a fusion reactor: plasma temperature, plasma density and confinement time
E , being the ratio of the energy stored in the plasma plasmaW and the rate of
energy loss lossP .
plasma
E
loss
W
P (1.7)
Many tokamaks have been built since then throughout the world to continually
advance the plasma performance. Their operation is marked with a number of
records, one by one paving the way to a first commercial fusion power plant.
Joint European Torus (JET) located in the Culham Centre for Fusion Energy in
Oxfordshire, UK, is the biggest tokamak in operation nowadays, with the major
radius of 2.96 m. It is renowned for having performed the first controlled energy-
releasing DT reaction in the world, [11] and holds a record of fusion power of
16 MW achieved in 1997 [12].
The longest plasma discharge in a tokamak (6.5 minutes) was recorded in Tore
Supra in December 2003 in France [13]. The tokamak has undergone an update
and is currently known as WEST.
EAST (Hefei, China) achieved 100 s world record of steady-state high
performance plasma (H-mode) in July 2017 [14], followed by a record 100 s
plasma discharge in the Wendelstein 7-X stellarator, in November 2018 [15]. The
H-mode is the operational scenario envisaged in ITER, which would provide
advanced energy output.
The construction of the ITER tokamak in Cadarache (France) is “one step to
DEMO”, a planned demonstration fusion power plant which would generate
electric energy. The main goal of ITER is to produce more fusion energy, than is
used to “ignite” the plasma; a milestone which has not been achieved so far in
existing devices.
Other important goals include development and testing of key technologies
necessary for an efficient and safe future power plant, such as different concepts
of tritium blanket modules (TBMs), which are needed to enable tritium self-
sufficiency of DEMO and future commercial power plants.
Finally, ITER experience is absolutely necessary for the improvement of the
plasma confinement and diagnostics, to ensure that a long pulse, required by the
1. Introduction
9
DEMO balance of plant, would become feasible. The closure of the ITER cryostat
in late 2024 will be an important milestone marking the end of the first ITER
assembly phase (machine core assembly) and the start of integrated
commissioning. The next step will be to evacuate the vacuum vessel and cryostat
enclosures for a first round of leak testing at room temperature [16], finally
followed by ITER’s first plasma as planned for December 2025 [17].
1.1.3 ITER operational conditions
The aim of the present project is to develop a physically-based model of
thermally-induced plastic deformation of tungsten exposed to operational
conditions of ITER and to understand the process of accumulation of damage,
eventually leading to fatigue cracking.
1.1.3.1 The role of divertor
Plasma in tokamaks is heated in toroidal vacuum vessels surrounded by
magnetic coils. The air is evacuated from the vessel and is then replaced with
low-pressure gaseous fuel, deuterium, which is further ionized to create plasma.
Magnetic confinement cannot be perfect, and a small fraction of plasma does
interact with the vessel walls. In this way the plasma can become contaminated
with other elements, impurities, which have a negative effect on the efficiency of
the fusion reaction: they cool down the plasma due to electromagnetic radiation
and can, in the worst case, shut down the reaction.
A solution was put forward already at the dawn of the fusion research. Lyman
Spitzer at Princeton proposed a method for mitigating the consequences of the
plasma-wall interaction by diverting a part of magnetic lines at the edge of the
plasma into a separate chamber, where the interaction can take place. The
system was called a divertor. The produced impurities would be trapped in the
small chamber; from which they could be evacuated with a pump system [18].
The magnetic lines would be arranged in such a way, so as to separate the core
high-temperature plasma, where the fusion reaction takes place, from the outer,
much colder, layer (called the scrape-off layer, SOL) which can interact with the
vessel walls. As can be seen from Figure 1.5a, the closed magnetic field lines form
a D-shape in the middle of the chamber where the core plasma is located,
separated from the SOL. The first non-closed magnetic field line is called
separatrix and marks the border between the core plasma and the SOL
highlighted with pink colour. Thus, impurities introduced in the SOL remain
there, and are swept to the divertor region.
The divertor of ITER will be constructed of 54 cassette assemblies (one of them
is shown in Figure 1.5b). Tungsten monoblocks will be used as plasma-facing
components (Figure 1.5c) in the most thermally-loaded part of the divertor —
the vertical targets. The monoblocks will be assembled on a cooling pipe made
of a CuCrZr alloy using a copper interlayer to reduce thermal stresses at the joint
caused by the difference in the thermal expansion coefficient of W and CuCrZr.
1. Introduction
10
Figure 1.5. a) A schematic picture of ITER’s vacuum chamber [10,19]. Tungsten is shown with red colour. Black lines represent an example of magnetic field lines in the core plasma and a separatrix. The light pink region between the separatrix and the walls of the chamber represents the divertor plasma layer. b) A divertor cassette and its parts [20]. c) A plasma-facing unit: tungsten monoblocks assembled on a cooling pipe [21].
Figure 1.6. The monoblock geometry, the cross-section of the CuCrZr cooling pipe and the Cu interlayer. Note the bevelling of 0.5 mm introduced to reduce thermal load on the right edge of the monoblock by shadowing it with a neighbouring monoblock to the right. Dimensions are in mm [22].
1. Introduction
11
An individual monoblock and its dimensions are shown in Figure 1.6 together
with the cooling pipe and the interlayer. The divertor monoblocks have to
withstand high heat loads, especially at the strike point, where the plasma flow
gets in contact with the divertor surface, and the power density reaches
10 MW m-2 in the steady state of plasma and 20 MW m-
2 during slow transients
(which last less than ten seconds), resulting in a surface temperature of
~1000 °C or ~2000 °C correspondingly [20]. Several scenarios to reduce the
heat load power density have been developed, including:
• Aligning the divertor surface at a small angle to the magnetic field
(around 3°), to increase the effective area of the wall subjected to the
heat load
• Flux expansion of the field lines as they approach the divertor
• Periodical sweeping of the strike point over a considerable distance in
the poloidal direction
Because copper cannot withstand such high temperatures, the coolant
temperature at the inlet is chosen as 70 °C [23], corresponding to the lower
boundary of the monoblock temperature between plasma discharges.
1.1.3.2 Selected plasma scenario and the plasma-wall interaction
The plasma-wall interaction will allow for extraction of the generated heat from
the plasma, and for its transfer to the coolant, which will generate steam and spin
electric alternators, like in any ordinary power plant. A typical fusion power
plant would generate about 1000–1500 MW of electricity [1].
Commercially profitable long-term operation of fusion reactors requires the use
of a special plasma scenario, called the high-confinement (H-mode). In this case
the plasma density, temperature and pressure in the core are increased
compared to previously used low-confinement scenario, making the H-mode
favoured for the fusion reaction. This mode of operation is proposed as the
standard operating scenario for ITER [24].
Figure 1.7. Schematic representation of the normal operation with temperature excursions during transient heat loading. Lower temperature range is defined by the DBTT, while the upper range is limited by the recrystallization temperature [1].
1. Introduction
12
However, the H-mode is associated with the occurrence of plasma instabilities
called “edge-localized modes” (ELMs) [21,25] responsible for transient heat
loads depositing significant power density, ~1–10 GW m-2, at millisecond time
scale [26]. Their high repetition rate, around 1 Hz, results in approximately 1
million events during the lifetime of ITER. The heat flux due to ELMs is 2–3
orders of magnitude higher than that during steady plasma. These instabilities
are thus one of the main limiting factors for the lifetime of plasma-facing
components of the divertor. Typical temperature excursions at the surface of the
ITER divertor during normal operation are illustrated in Figure 1.7.
The main effect of repetitive ELM heat loads is thermal fatigue, which will cause
irreversible damage and shorten the divertor lifetime. Due to the high heat fluxes
impinging onto the first wall and the divertor, and simultaneous cooling by the
heat sink, large thermal gradients will occur synchronously with the ELMs. The
resultant thermal gradients will give rise to pulsed stresses, which will lead to
the thermal fatigue damage of the components: surface roughening and
formation of a surface crack network. While the formation of cracks is nearly
unavoidable, their propagation can be detrimental for the safe and stable
operation of ITER, and has to be limited by various measures.
Another concern is due to the residual stresses in the joints between the PFCs
and the heat sink due to different thermal expansion coefficients, which could
lead to detachment and worsening the thermal contact. This implies that testing
of tungsten components subjected to cyclic heat loads and thermal shocks are
essential for the qualification of the ITER device.
1.2 Tungsten as a material for fusion reactors
Tungsten (chemical element designation — W) is a transition element from
group VI in the periodic table, with atom number 74 and the atomic mass 183.85
[27] which defines its high density of 19.254 g cm-3 [28]. Phase α, body-centred
cubic (BCC) structure, is the only stable crystalline phase of W with lattice
constant 0.3165 nm at room temperature.
The selection of tungsten as the plasma-facing material in ITER is determined by
its highest melting temperature among metals (3422 °C), advantageous thermal
conductivity, its resistance to sputtering, high strength at elevated temperature
and moderate activation in neutron fields [29].
In the course of material selection for ITER these qualities overweighed the
perspectives of plasma contaminations by heavy atoms of tungsten. As
mentioned above, a divertor will remove impurities from the outer layer of
plasma in ITER, where they could initially be generated. In 2007 the ASDEX-
Upgrade tokamak became the world’s first full-tungsten fusion device, where
tungsten was used in both divertor and the first wall. Experiments in this
tokamak demonstrated the compatibility of a full-tungsten reaction chamber
1. Introduction
13
with the H-mode scenario, while preserving the plasma sufficiently clean of
impurities [30].
1.2.1 ITER-specification tungsten
The ITER Organisation has imposed requirements for the fabrication of tungsten
for plasma-facing divertor components in terms of purity, grain size, hardness
and density [20]. An important requirement is the elongation of grains, such that
the monoblocks are fabricated with the grains elongated towards the plasma-
facing surface as shown in Figure 1.8. In this case the intergranular cracks
appearing due to cyclic thermal load would propagate perpendicular to the
heated surface which is considered less detrimental for the operation of ITER
than delamination of grains at the surface leading to the plasma contamination
and consequent cooling.
Figure 1.8. Schematic view of a typical W monoblock indicating its microstructure and typical dimensions [31].
Table 1.1. Impurity content of the IGP tungsten.
A commercial tungsten grade compliant with the ITER requirements, produced
by the Austrian company Plansee AG (denoted as “IGP” standing for “ITER-grade
Plansee”) was investigated in the present work. It is polycrystalline tungsten of
>99.97% purity with the residual impurities specification listed in Table 1.1.
The material was supplied as a bar with a square cross-section of 36×36 mm2 as
shown in Figure 1.9a. The bar was fabricated by hammering on both sides,
1. Introduction
14
resulting in needle-like grains elongated along the bar axis. Prior to cutting the
samples, the bar was annealed at 1000 °C for one hour in inert environment for
degassing. According to an Electron Backscatter Diffraction (EBSD) analysis it is
a single-phase material with a grain size of 5–20 µm and 10–100 µm, normal to
and along the bar axis, respectively (Figure 1.9c). The initial dislocation density
is about (4–8)·1012 m-2, depending on particular sub-grain, with an average of
4.5·1012 m-2 measured by analysis of Transmission Electron Microscopy (TEM)
images [32], one of which is presented in Figure 1.9d.
The investigated tungsten grade is in line with the ITER specification: it adheres
to the regulation for chemical composition, density, hardness, grain size and
microstructure. More information on the ITER specification can be found in [33].
a) b)
c) d)
Figure 1.9. a) A fabricated bar of tungsten with indicated macroscopic directions; b) a TEM image of microstructure of as-received tungsten; c) an EBSD map of as-received tungsten; d) an EBSD map of recrystallized tungsten.
1. Introduction
15
1.2.1.1 Tungsten in the recrystallized state
Recrystallization of most metals and alloys starts from 0.4Tm upwards, where Tm
is the melting temperature, thus, it begins in tungsten at 1200–1400 °C. As
shown above, the surface temperature of the tungsten divertor will reach
1000 °C in the steady-state plasma discharges with infrequent rises up to
2000 °C during slow transients and even higher, up to the melting point, for
milliseconds-long pulses, due to ELMs.
It is expected that the top layer of divertor monoblocks will be recrystallized up
to a few mm depth, as registered after high heat flux tests (Figure 1.10). Surface
melting of divertor plasma-facing components can be prevented by ELM
mitigation techniques, though. Conservative finite element analysis (FEA) of the
stress state in tungsten monoblocks may require the knowledge of mechanical
properties of recrystallized tungsten.
Recrystallized tungsten has large grains depleted of dislocations, which reduces
its strength. The process of recrystallization is extended in time, hence,
intermediate — partially-recrystallized — microstructure will be observed in
the tungsten monoblocks in operational conditions most of the time. An exact
analysis of the material strength (and microstructure) evolution during
operation would require knowledge of the distribution of fraction of
recrystallized grains as a function of time (or the number of plasma discharges),
necessitating the use of recrystallization models as well.
To avoid such complicated analysis, we investigate two limiting cases of tungsten
from the point of view of microstructure, relevant for the application in ITER:
“as-received” (or “as-fabricated”) and “recrystallized”. To that end the same
mechanical tests have been carried out for the as-received material and for a
number of samples recrystallized at 1600 °C for 1 h. Recrystallization resulted in
equiaxed grains with the size around 50–100 µm, as measured by EBSD (Figure
1.9d) and reduced dislocation density down to 1011 m-2.
Figure 1.10. Metallographic cross-section in the centre of tungsten mock-up subjected to 20 MW m-2 in a high heat flux test, showing the layer recrystallized due to high thermal load [34].
1. Introduction
16
1.2.2 Mechanical properties under monotonic loading
Even though tungsten is not a structural material in ITER, divertor monoblocks
will experience significant thermal stresses during operation, thus the
knowledge of mechanical properties of tungsten is essential. For the purpose of
ITER they are mainly characterized with the help of two types of mechanical
tests: tensile and fracture toughness tests. Due to anisotropy of mechanical
properties caused by texture and microstructure with elongated grains, set as a
requirement by ITER, experiments have to be performed on samples machined
with different orientation.
It is only possible to give a general overview of mechanical properties of
tungsten, like of any material, speaking of single crystals of high purity.
Mechanical properties of commercial, polycrystalline material, which are of
technological importance, strongly depend on its purity, microstructure and
processing route.
Elastic properties of tungsten are close to isotropic and vary with temperature:
an experimental work by Lowrie and Gonas reports that in the range from room
temperature to 1800 °C Young’s modulus E decreases from 410 GPa to 315 GPa,
and Poisson’s ratio — from 0.31 to 0.28 [35,36].
Tungsten has a high ductile-to-brittle transition temperature (DBTT), in the
range 250–650 °C, depending on the alloying elements, purity and processing
route [37]. Neutron irradiation will further increase the DBTT, as it is a general
characteristic of BCC metals. Anyways, pure bulk polycrystalline tungsten is
brittle at room temperature, while single crystals, thin foils or wires of tungsten
demonstrate considerable plasticity [38–40].
Fracture toughness tests of commercially pure tungsten carried out in the
temperature range between -196 °C and 1000 °C [41] revealed that the
conditional fracture toughness QK is quite low at low temperature and does not
exceed 10 MPa m0.5 below 500 °C. However, it increases significantly up to
~80 MPa m0.5 at 800 °C indicating that the crack propagation was accompanied
by considerable plastic deformation. Investigation of fracture surfaces showed
intergranular as well as transgranular fracture of all tested materials, although
intergranular fracture behaviour was dominant in most cases [41,42].
Intergranular fracture has been observed in tungsten with impurities as well as
in highly pure tungsten, with no traces of impurities on grain boundaries (GB).
Thus, the strain incompatibility between grains is believed to be the deciding
factor of limited ductility of tungsten [42,43].
A series of experiments on another tungsten grade, a rolled rod fabricated by
Plansee Metall GmbH (Austria), was consistent with the observations by
Gludovatz at lower temperature, however, showing much lower values of QK at
527–927 °C which did not exceed 20 MPa m0.5 [44]. Besides, a loading rate effect
on the value of fracture toughness has been observed.
1. Introduction
17
Forged tungsten with flat grains has been investigated up to 1000 °C [45]. The
crack propagation was predominantly intergranular for longitudinal orientation
up to 600 °C, whereas transgranular cleavage was observed at low test
temperatures for radial and circumferentially oriented specimens. At
intermediate test temperatures the change of the fracture mode took place for
radial and circumferential orientations. Above 800 °C all three specimen types
showed large ductile deformation without noticeable crack advancement. Again,
the conditional fracture toughness QK barely exceeded 20 MPa m0.5 at 400 °C,
but the results at higher temperature were considered invalid from the point of
view of validity criteria according to the ASTM 399 standard [46].
Fracture toughness JcK of ITER-specification tungsten, recently measured
according to ASTM 1921 and referring to ASTM 1820, was around 10 MPa m0.5
at low temperature, but reached 50 MPa m0.5 at 600 °C, indicating the
importance of plastic deformation at high temperature, expected at the surface
of the ITER divertor [47].
Two main ways to increase ductility and fracture toughness of tungsten have
been identified: alloying with rhenium (Re) and grain refinement down to
nanocrystalline microstructure [43], which still have to be investigated.
Tungsten-rhenium alloys outclass other tungsten-based materials in terms of
ductility improvement. The positive effect on fracture toughness has been
confirmed in a series of tests up to 900 °C, where a W-26%Re alloy demonstrated
fracture toughness of ~50 MPa m0.5 even at room temperature [48]. W-Re alloys
with 3–10% Re are used in modern rotating X-ray anodes thanks to
improvement of mechanical properties and suppression of crack formation
[49,50]. Re is an expensive and rare element, hence alloying with Re is not
considered for the ITER divertor, but can be needed for future power plants.
However, the feasibility of using W-Re alloys in fusion devices is still
undetermined, because of an extreme brittleness of Re-rich second phase
precipitates which are formed under neutron irradiation [51]. Besides, the
presence of Re decreases thermal conductivity of the alloy [52], which can lead
to overheating and melting.
The positive effect of grain refinement on fracture toughness has been
demonstrated in experiments of pure, ultrafine grained 100 μm tungsten foil in
samples with different crack orientation relative to the rolling direction in the
temperature range from -196 °C to 800 °C [38,40]. The grain shape anisotropy
and a strong rotated cube texture have been demonstrated to be the decisive
factors for anisotropic fracture properties. The pronounced transition in failure
mode was observed going from brittle, transgranular fracture at -196 °C towards
pronounced delamination at intermediate temperatures and to ductile fracture
at highest temperatures.
Ultra-fine grained tungsten fabricated with the help of High Pressure Torsion
(HPT) showed fracture toughness increased up to 30 MPa m0.5 even at room
1. Introduction
18
temperature. The grain size decreases down to ~300 nm as a result of severe
plastic deformation [53].
Beneficial changes of microstructure during thermomechanical processing of
tungsten include elimination of pores, which may serve as stress concentrators,
decrease of grain size and build-up of dislocation density. Grain refinement as a
result of deformation is favourable for ductility of tungsten thanks to increased
density of GBs, which serve as dislocation sources. They significantly contribute
to the density of edge and mixed dislocations, which are more mobile than screw
dislocations in BCC metals, resulting in lower energy needed for deformation.
Moreover, it leads to the increase of the fraction of low-angle GBs, which are
easily penetrable by dislocations. Consequently, recrystallization eliminates the
favourable factors and reduces the material plasticity [43,54,55].
The dominance of intergranular fracture mode in tungsten enables performing
finite element analysis of deformation of tungsten polycrystal, in which special
cohesive elements are placed along GBs, as potential crack propagation path
(will be discussed in Chapter 4). The importance of plastic deformation for
fracture at elevated temperature necessitates understanding and
parameterization of plasticity of tungsten, which is in the focus of Chapter 2.
Before the specification of tungsten suitable for ITER has been established,
mechanical properties of several grades fabricated by a few companies have
been studied, among which are a sintered block, a heavily-deformed rod, a rolled
plate, single-forged and double-forged blanks, as well as tungsten doped with
potassium (K) and La2O3, summarised in the work of Uytdenhouwen [1], where
the test temperature reached 2000 °C. Tensile tests of double-forged tungsten
and parameterization of a dislocation density-based plasticity model have been
reported up to 2000 °C as well [56]. Finally, a recent overview of plastic
properties of baseline and advanced tungsten grades covered the temperature
range up to 600 °C [57].
As mentioned above, many properties of tungsten (and all materials in general)
are mainly determined by its microstructure, which in turn depends on the
fabrication route. Numerous tensile tests of different grades of tungsten show
significant differences in yield stress, ultimate tensile strength, uniform and total
elongation and fracture mode in materials with different microstructures. That
is why for the purpose of the present project a series of tensile tests of a single
selected material, IGP, have been carried out and used as a base for the
parameterization of a plasticity model.
1.2.3 Mechanical response of tungsten under cyclic loading
1.2.3.1 Overview of heat load tests
In order to ensure the structural integrity of the divertor during operation of
ITER, its monoblocks have to be tested in thermal cycles of high amplitude.
Various methods, such as beams of electrons, ions, or neutral particles, laser and
1. Introduction
19
plasma shots, can be used to simulate the thermal conditions in a fusion reactor.
Two types of tests are mainly used:
High heat flux test, in which a mock-up of a divertor (several
monoblocks assembled on a cooling pipe, Figure 1.11) is subjected to
cycles of heat load lasting usually for seconds. Coolant flows through the
pipe at speed and temperature envisaged in the real operation of ITER.
Thermal loads of 10 MW m-2 or 20 MW m-
2 are applied to simulate the
effect of long stationary plasma discharges and slow transients,
correspondingly. In order to pass the tests, the monoblocks have to
survive 5000 or 300 cycles (of low and high deposited energy density
correspondingly), preserving the thermal contact with the cooling pipe
and without formation of macroscopic surface cracks (called “self-
castellation”) [31,58].
Thermal shock test, in which a tungsten sample is subjected to
microsecond-long pulses of significant thermal power, amounting to
several hundreds of MW m-2, to mimic the effect of ELMs. The opposite
face of the sample is maintained at constant temperature. The
temperature profile caused by such short transient heating does not
spread deep into the material. That is why the surface temperature
excursions due to short transients are almost unaffected by the choice
of coolant temperature.
Figure 1.11. Divertor mock-up after exposure to a high heat flux [34].
The applied thermal flux should be uniform over the exposed area in order to be
able to compare the experimental results with the heat load expected in ITER
and theoretical predictions. Besides, the initiation and growth of cracks under
cyclic heat loads can also be affected by the power density profile. However,
generation of an electron beam, uniformly distributed over a large area is a
challenging task. Instead, beam rastering is used in order to deposit high heat
flux over a wide area uniformly. The rastering frequency should be high enough
(more than tens of kHz) to smooth the pulsations of deposited energy at a given
point of the surface.
Other high-temperature applications of tungsten, where it is subjected to cyclic
thermal load, include the European Spallation Source (ESS) and X-ray sources.
ESS is a facility under construction in Lund, Sweden, where tungsten will be used
1. Introduction
20
as a rotating spallation target. The surface will experience cyclic thermal loads,
like the ITER divertor, but the expected operation temperature is much lower,
500 °C maximum [59]. That is why the mechanical characterization of tungsten
for ESS has been carried out within this temperature window in tension and low
cycle fatigue [59,60]. The material was brittle up to 200–250 °C, and
demonstrated early necking but high total elongation at higher temperature.
Rotating X-ray anodes are also made of tungsten and tungsten-based alloys
[49,61–64]. A continuous high-energy electron beam is directed onto the rotated
anode, hence, every given unit of anode area experiences cyclic thermal shocks,
as it passes through the focal spot during rotation at frequency up to 250 Hz [65].
The temperature can rise by several hundred or a thousand of °C [50]. It has to
be noted that numerical analyses of thermomechanical conditions in X-ray
anodes have rarely been published [65], thus the results of the present thesis
might be useful for this application of tungsten as well.
1.2.3.2 High heat flux test
Numerous tests of both types have already been performed. Monoblocks
fabricated of different grades of tungsten, using various techniques of joining the
monoblock with the cooling pipe were qualified in machines like ion beam
facility GLADIS [66], linear plasma device Pilot-PSI [67] and electron beam
facilities IDTF [68] and FE200 [34]. Later, the monoblock dimensions and shape
were fine-tuned, by thermo-mechanical FEA of a monoblock subjected to a
steady-state plasma discharge and simultaneous optimization of the
temperature field.
The main outcome of the full-tungsten qualification program (in the unirradiated
state) is that the tested mock-ups and full scale prototypes (280 monoblocks in
total) successfully demonstrated their performance, with just 30% of them on
average, showing self-castellation, i.e. formation of a crack network, in the
tungsten armour [58].
Some monoblocks withstood critical heat flux tests during 1000 heat cycles at
20 MW m−2, by far exceeding the threshold of 300 cycles imposed by the ITER
Organisation [69]. Accompanying simulations confirmed that appearance of
large thermal stresses at the centre of loaded surface was consistent with the
location of macro-cracks in monoblocks [69].
1.2.3.3 Thermal shock test
First thermal shock tests in electron beam devices designed to characterize the
response of tungsten to ELMs involved merely a single shot of thermal power
[70]. Recently, tests with one million thermal shocks were performed to
investigate the fatigue and long term behaviour of the material [71], that
coincides with the expected number of ELMs in ITER’s operational lifetime.
1. Introduction
21
Figure 1.12. Damage mapping of tungsten samples exposed to ELM-like thermal shocks. Plain-coloured symbols stand for samples with 100 thermal shock pulses. Symbols with a black centre stand for samples exposed to 1000 pulses [26].
The goal of these tests was to identify the threshold conditions of thermal shocks,
which do not lead to surface crack formation after a given number of heat pulses.
The base temperature, the pulse length and the power density of one shot were
varied. The tests have been performed in quasistationary plasma accelerator
QSPA Kh-50 [72] or electron-beam device JUDITH [26,71] for the material in
unirradiated state. As a result, maps of base temperature vs. absorbed power
density were obtained, with Figure 1.12 serving as example.
The evolution of surface morphology with the increase of either cycle number or
heat power density:
1. Initial surface
2. Surface still not changed after a certain number of cycles
3. Roughened surface
4. Micro cracks on the surface
5. Propagated cracks
Rapid increase of surface temperature leads to expansion of the subsurface
layers with strain rate up to 8 s-1 [1], i.e., several orders of magnitude higher than
the strain rate in conventional tensile tests. Tungsten is known to demonstrate
rate-dependent plasticity [1,52], meaning that in order to extrapolate the
experimentally-obtained mechanical properties to higher strain rate and higher
temperature, aiming at simulation of thermal shocks due to ELMs, a physically-
based model of plasticity has to be employed.
1. Introduction
22
1.3 Overview of techniques
The present project relies on computational analysis almost entirely, but the
input for the simulations was obtained in experiments. Tensile tests were used
to find out the constitutive law of the investigated tungsten grade, i.e. the stress-
strain curves in a range of temperature and strain rate, while its microstructure
was characterized with the help of scanning and transmission electron
microscopes. The obtained constitutive laws were used in the J2 finite element
analysis of tungsten exposed to ITER-relevant thermal shocks, and had to be
translated to the microscopic level in order to be used in the crystal plasticity
framework. A short overview of numerical and experimental techniques
involved in the project is presented below, whereas more detailed discussion
will be provided in the corresponding chapters.
1.3.1 Numerical analyses of heat load tests
The finite element method (FEM) is the most widely used universal simulation
tool in structural mechanics nowadays. It originates from the work of Courant
[73], and was significantly enriched by Zienkewicz and Taylor [74,75]. It is a
numerical method to solve nonlinear partial differential equations, and has to be
provided physical laws in order to construct a model.
The idea behind it is to discretize a simulated body into smaller simpler parts,
called finite elements. The entire mechanical problem is then addressed by
solving a large system of equations, corresponding to the tessellated elements.
The elements are connected at the exterior nodes only, which can be displaced
by the applied load and, in turn, drag the connected elements along.
Displacements of any point in the elements is an interpolation of the nodal
displacements. Strain tensor in elements is calculated from the nodal
displacement, while stress tensor in elements is derived from the forces exerted
on nodes. Interpolation of the values calculated at nodes is carried out with the
help of polynomial shape functions, which can be of first-, second- and higher
order. Standard first-order elements (linear) are essentially constant strain
elements, while the second-order elements (quadratic) are capable of
representing all possible linear strain fields [76].
Variational methods are applied to find a solution by minimizing an associated
error function. The relation between stress and strain in an element is governed
by a constitutive law. FE analysis requires the three following general procedural
steps which are illustrated by the most typical tasks involved in them [77]:
1. Pre-processing
Generation of the mesh, including node coordinates and the choice
of element type
Specification of loading conditions
Input of material (constitutive) law
1. Introduction
23
2. FE analysis
The solution is obtained incrementally in time; it has to converge at
every time increment, meaning that the obtained fields of stress and
strain tensors must satisfy the conditions on compatibility,
equilibrium, boundary conditions and the constitutive law
simultaneously
3. Post-processing
Calculation of element data at integration points
Analysis of temporal evolution of a given quantity
Graphical representation of obtained solution such as isoline
images, animation
Among the variety of software for finite element analysis, Abaqus 6.17-1 by
Simulia was chosen for the present research, as a popular and powerful tool,
flexible enough so as to incorporate user-defined material behaviour, necessary
for the analysis at the grain level with the help of crystal plasticity.
The problem of crack formation in tungsten monoblocks due to plastic
deformation under cyclic heat loads is important and is investigated not only
with the help of qualification tests discussed above, but also with the help of FEA.
It requires mechanical properties of investigated material as input (tungsten in
our case). The lack of a database of mechanical properties of tungsten in the
temperature range corresponding to the operational conditions of ITER, as well
as a big number of investigated tungsten grades and dependency of plastic
properties on microstructure and fabrication route forces the use of simplified,
linear-elastic and ideal-plastic constitutive laws in many cases.
Such approach has widely been used for simulation of both stationary plasma
discharges [78–82] and the effect of ELMs [83] to assess the evolution of stress
and strain in tungsten under cyclic heat loads. These simulations have been
performed at the macroscopic scale, using J2 plasticity model and materials were
defined as perfect elasto-plastic solids with the yield stress and Young’s modulus
decreasing with temperature.
Engineering investigations of design options to mitigate deep cracking in
monoblocks relied on macroscopic J2 FEA [80]. Also, the concept of thermal
break has been evaluated in this way [84]. It is an “obstacle” in the monoblock
design that impedes the thermal flux towards the cooling pipe and increases the
temperature in tungsten above its DBTT.
Thermo-mechanical analysis of heat-exposed monoblocks in two limiting cases
of microstructure — as-received W and recrystallized W — was reported in [85]
and used an elastic-linear plastic constitutive law with kinematic hardening,
however, little information was provided regarding its parameterization.
1. Introduction
24
1.3.2 Consideration of cyclic deformation under J2 plasticity
theory
1.3.2.1 The Bauschinger effect
An interesting phenomenon was discovered by Johann Bauschinger, who
installed the largest testing machine of the period and made very accurate strain
measurements with a mirror extensometer. It turned out that materials pre-
strained in tension, generally exhibit a lower yield stress in subsequent
compression, and vice versa. The effect named after its discoverer has been
observed in many, especially structural, materials such as steels [86,87] or TiAl
alloys [88], not only in tension-compression cycles, but under conditions of any
significant change in loading path. [89].
An example of the Bauschinger effect is schematically demonstrated in Figure
1.13, conventionally denoting tensile stress and strain as positive, and
compressive stress and strain as negative. The solid black lines show the flow
curves in tension and consequent compression. The material loaded in tension
reaches the flow stress 1t , is elastically unloaded and then compressed. But the
plastic yield begins at compression stress 2c which is lower than 1t . The
stress drop is evident when comparing the dashed blue line, which is the point
reflection of the compression curve, and the forward flow curve.
Figure 1.13. Illustration of the Bauschinger effect in reversed loading. The yield stress in compression is lower than the stress achieved prior the load reversal. [90].
1.3.2.2 J2 plasticity model
The von Mises constitutive model of plasticity is available in Abaqus by default
and is widely used for macroscopic FEA of metallic materials where the
anisotropic properties of individual grains are averaged thanks to their large
number. In order to investigate the mechanical response of material at the
1. Introduction
25
microscopic level, where plasticity is governed by the interaction between grains
and the mutual orientation of slip planes, in which dislocation glide takes place,
we will use crystal plasticity constitutive model discussed in Chapter 3.
The von Mises model assumes that yielding of metal is independent of the
hydrostatic stress H , which is the sum of the diagonal components of the stress
tensor ijσ .
3
1
H ii
i
(1.8)
The model states that yielding begins when the equivalent stress (referred to as
“von Mises stress”) eq reaches the value of yield stress recorded in a uniaxial
tensile test of the given material
3
:2
eq σ σ (1.9)
where σ is the deviatoric stress tensor
H σ σ (1.10)
As the von Mises stress is proportional to the second invariant of the deviatoric
stress tensor 2J ,
eq 23 J (1.11)
the von Mises constitutive model is called “J2 plasticity”.
1.3.2.3 Isotropic and kinematic hardening
In order to better understand the Bauschinger effect, we should refer to the
concept of a yield criterion. It is a mathematical expression of the stress states
that will cause yielding or plastic flow, which is especially useful for studying
material yielding under complex stress states. The most general form of a yield
criterion is [89]
, , , , ,x y z xy xz yzf const (1.12)
This expression defines a closed surface in the stress space, called “yield locus”.
A point in this space corresponds to a particular local stress state at a material
point. Stress states inside the yield locus generate merely elastic deformation,
while those on the surface cause plastic flow.
There are two main models of the evolution of yield loci during deformation [89].
According to the isotropic hardening model, the effect of strain hardening is to
expand the yield locus in an isotropic manner without changing its shape (Figure
1.14a). It means that the stress for yielding in reverse loading would remain
equal to the stress reached by the end of direct loading.
1. Introduction
26
An alternative model is kinematic hardening, according to which plastic
deformation shifts the yield locus in the direction of the loading path without
changing its shape or size (Figure 1.14b). The models represent the limiting
cases of material hardening, whereas their combination at different proportion
is observed in reality.
Isotropic hardening is due to accumulation of forest dislocations, which pose as
obstacles for gliding dislocations by pinning them. One of the models of
dislocation density evolution is the one developed by Kocks and Mecking [91],
where the density is controlled by two terms, the multiplication rate (thanks to
the dislocation sources activated during deformation) and the dynamic recovery
rate.
Kinematic hardening is observed in material where stress heterogeneity occurs
at the microscopic level during plastic deformation [92,93]. Examples include
composites and multiphase materials where constituents have different strength
or stiffness [88,94] and precipitate hardened alloys in which the reverse flow is
facilitated thanks to the Orowan loops formed during direct loading [95–97].
Formation of directional dislocation substructures (such as cell walls) also
contributes to kinematic hardening.
Figure 1.14. Effect of strain hardening on the yield locus. The cross-section of the
locus in the x – y plane is shown. The isotropic model (a) corresponds to an
expansion of the locus. The kinematic hardening model (b) corresponds to a translation of the locus in the direction of the loading path [89].
In single-phase materials it emerges mostly due to the formation of dislocation
pile-ups at GB [98,99], and we will focus on this mechanism in the present work.
When dislocations gliding in a given slip system one after another hit a GB, the
leading dislocation stops, as the stress necessary to overcome the GB is too high.
Dislocations of the same sign repel each other, thus, the whole sequence of
dislocations stops. Thus, a pile-up creates a back stress on the dislocation source
so that the stress to continue to operate the source must rise.
1. Introduction
27
The distance between the dislocations is defined by the balance of the applied
stress, pushing the dislocations towards the GB and the backstress (Figure 1.15).
Upon unloading the pile-up dissolves into individual dislocations whose reverse
motion is facilitated by the backstress, effectively reducing the external stress
required for the yield.
Figure 1.15. Linear arrays of edge dislocations piled-up against barriers under an applied shear stress [100].
The stress experienced by the leading dislocation in a pile-up composed of n
dislocations is [89]
lead appliedn (1.13)
The same stress is exerted locally on the GB, in the vicinity of the pile-up. It means
that the presence of dislocation pile-ups (and, thus, the ability of material to
exhibit kinematic hardening) leads to a more severe stress state at GBs,
compared to a material with purely isotropic hardening, and can provoke
fracture if GBs are the weakest link in the material.
Having identified two major differences between materials exhibiting purely
kinematic and isotropic hardening, namely
the Bauschinger effect
more severe stress state at GBs
we raise a question relevant for specific ITER conditions: what is the impact of
the potential presence of kinematic hardening in ITER-specification tungsten on
the stress state and damage accumulation in a monoblock exposed to ELMs and
being under conditions of cyclic thermal stress?
Information on the Bauschinger effect, and consequently, on kinematic
hardening, cannot be inferred from uniaxial tensile tests, the main source of
constitutive laws for FEA. In order to quantitatively estimate the proportion of
kinematic hardening relative to isotropic hardening, cyclic mechanical loading
tests have to be performed, in which a sample is periodically loaded in tension
and compression.
Low cycle instrumented fatigue tests to study the Bauschinger effect have
scarcely been carried out for tungsten due to its brittleness and associated
technical difficulties in the manufacturing of samples of complex geometry,
needed for the tests. In Ref. [59] the authors performed strain-controlled low-
1. Introduction
28
cycle fatigue tests of different tungsten grades with three levels of strain
amplitude at 480 °C. The obtained stress-strain loops reproduced in Figure 1.16
clearly demonstrate a significant Bauschinger effect in forged tungsten under
given experimental conditions: tungsten, loaded up to 450 MPa in tension, yields
at ~100 MPa in compression. However, further analysis of available literature
has not yielded other works devoted to instrumented fatigue tests, based on
which the Bauschinger effect could have been assessed in various tungsten
grades. Furthermore, works on fatigue tests in tantalum have not been found
either, disabling the possibility to construct a plasticity model of tungsten based
on another refractory material with similar properties.
Figure 1.16. Comparison between a strain controlled fatigue test and a monotonic tensile test of polished forged tungsten at 480 °C [59].
1.3.3 Deformation of polycrystals at the microscale
1.3.3.1 What is crystal plasticity?
Finite element analysis of macroscopic samples or structural components can
generally be performed assuming constitutive laws of isotropic homogeneous
continuum media and the J2 plasticity model. Despite the fact that macroscopic
metallic bodies are represented by aggregates of grains, i.e. anisotropic single
crystals, their properties are averaged thanks to the abundance of grains and
thus the anisotropy of a macroscopic body is eliminated. The outcome of the J2
(Mises) plasticity simulations depends on the accumulated equivalent plastic
strain only, and is not affected by the anisotropy of grains.
On the other hand, consideration of deformation of an individual crystal has to
account for its anisotropy, which originates from the features of deformation
mechanisms in crystal lattice. The most important deformation mechanism is
dislocation glide, which can take place only in certain atomic planes, due to the
anisotropy of individual crystals.
1. Introduction
29
The model that predicts which slip systems will be activated and which level of
strain will be reached in them, given the applied macroscopic stress, is crystal
plasticity (CP). It operates with quantities, such as stress components, strain
components, dislocation density, averaged over individual grains. The CP model
also accounts for the interaction of every grain with its neighbours during plastic
deformation and can be applied to polycrystals. Coupled with FEM, and referred
to as “CPFEM” in this case, it is able to predict the stress and strain heterogeneity
within every grain, because in this case the quantities like stress are calculated
locally in a given finite element, rather than in a given grain, and can help identify
the most loaded locations where, for instance, crack initiation is possible.
On top of that, prediction of the build-up of internal stresses and associated
damage in real materials at the microscopic level requires the knowledge of an
accurate strain path, i.e. the evolution of all the components of the strain tensor
at a given material point. Indeed, different strain paths (possibly leading to the
same final deformation) will induce different crystal lattice rotations and
different heterogeneity of hardening throughout the polycrystal, affecting the
final material state.
Simplified approaches to describe plastic deformation of a polycrystal such as
the Sachs or the Taylor approach, assume that either stress or strain
(respectively) in every grain coincides with the macroscopic applied value. This
simplification has its drawbacks: according to the Sachs model the strain
compatibility condition is violated, i.e. the grains in the deformed polycrystal
have to overlap or detach from each other, whereas stress equilibrium condition
is violated at GBs in Taylor’s polycrystal [101]. Both drawbacks being unphysical,
the latter is nevertheless seen as a more appropriate assumption, and the Taylor
model matches better with experiments [102]. However, grains in real materials
show both stress and strain heterogeneity during deformation due to the grain
anisotropy. This effect can be captured by CPFEM.
The effect of kinematic hardening has rarely been considered in
thermomechanical simulations of tungsten exposed to thermal shocks, whereas
it can strongly affect the rate of build-up of internal stresses in cyclic loading,
compared to purely isotropic hardening model. As long as one of the origins of
kinematic hardening is the build-up of dislocation pile-ups at strong obstacles,
which create backstresses assisting the reverse deformation, its effect must be
incorporated in a microscale model.
Dislocation motion in plastically-deformed metallic polycrystalline materials is
hindered by obstacles; either weak, such as forest dislocations, irradiation-
induced voids and dislocation loops, or strong, such as GBs. Having stopped at
strong obstacles, which require high stress in order to be overcome, dislocation
cores merge into larger discontinuities, the predecessors of cracks. As long as
cracks primarily initiate at the GBs and triple junctions, where favourable
conditions are provided by stress concentration, the knowledge of stress and
strain heterogeneity in grains is essential for accurate prediction of cracking.
1. Introduction
30
Consecutive thermal loads and dilatation-contraction cycles caused by them lead
to the amplification of stress/strain heterogeneity.
Plus, the effect of neutron irradiation on material behaviour is reflected at the
micro level. First, irradiation-induced defects, serving as obstacles, modify the
dislocation glide law and alter the grain response to mechanical loading. Second,
plastic deformation of neutron irradiated material is reported to cause such
microstructure changes as dislocation channelling. Channels correspond to thin
strips of material depleted of irradiation-induced defects, where the dislocation
glide is eased as compared to the surrounding material, rich in defects. Due to
intensive dislocation glide, plastic deformation accumulates rapidly in these
regions, leading to significant stress concentration and crack formation.
Thus the problem to be solved in the frame of the present project requires
detailed knowledge of stress and strain heterogeneity at the grain level, which
will amplify due to cyclic strain and neutron irradiation. Application of the J2
plasticity constitutive model at the grain level cannot predict any heterogeneity,
and is thus not appropriate for the present problem. CPFEM is used here to
predict damage accumulation and potential cracking in tungsten plasma-facing
components in ITER.
1.3.3.2 Relevant application of CPFEM in literature
CPFEM is a widely used method which has been applied in investigation of grain
size effects, grain interaction, surface roughening, high-temperature
deformation, nanoindentation and many other phenomena [75]. It is flexible
enough to introduce the effect of neutron irradiation on mechanical properties.
Works on crystal plasticity were mostly devoted to face-centred cubic (FCC)
materials, while BCC materials were basically represented by pure iron or iron-
based alloys and steels [103], that is why we had to modify the typically used
model equations in order to take into account a non-zero athermal stress typical
for BCC metals. A short review below is focused on the applications of the CPFEM
where dislocations were the main carrier of plastic deformation.
The importance of heterogeneity of deformation at the grain level on damage
nucleation in polycrystals was discussed in [104]. Listing 19 hypotheses
regarding the damage nucleation, the work points out that some of them are
incompatible with others. Nevertheless, we have selected one of the criteria,
more suitable to our problem in our opinion, which is discussed below.
Crystal plasticity has been applied to model the cyclic mechanical behaviour of a
polycrystalline nickel-based alloy at a constant temperature [105], ignoring,
however, the work hardening.
A more advanced work of low cycle fatigue of a Ni-based superalloy [106]
resulting in a good agreement with the experimental results for stress–strain
loops, cyclic hardening behaviour and stress relaxation. Accumulated plastic
strain was used as a fatigue indicator parameter (FIP) and the evolution of
backstresses was tracked, so that the Bauschinger effect was captured on the
1. Introduction
31
stress-strain loops. It was a 2D model with plane strain conditions, well suitable
for simulation of a fracture toughness compact tension sample.
CPFEM has also been applied to study thermal fatigue caused by periodical
temperature excursions in P91 steel [107], however, not many papers are
devoted to this topic. The FE model with periodic boundary conditions in both
in- plane and out-of-plane directions used regular 1st order cubic elements. It
was first parameterised using isothermal low cycle fatigue experiments. Similar
to the previously mentioned work, the evolution of backstress was considered,
however, fatigue life was predicted with a more complicated FIP, determined by
the accumulated plastic strain, stress triaxiality and temperature.
1.3.3.3 Kocks-Mecking model of plasticity
The Taylor equation is one of possible links between material’s strength and
microstructure, in terms of dislocation density :
c disb h (1.14)
where c is the critical resolved shear stress (CRSS),
dish is the dislocation
strength, is the shear modulus and b is the magnitude of the Burgers vector.
A model derived by Kocks and Mecking [91] on the basis of various experimental
observations prescribes the storage of in deformed material as concurrent
multiplication and annihilation (dynamic recovery) of dislocation:
1 r
r r
dL N
d b
(1.15)
The first term is responsible for hardening due to dislocation multiplication and
is purely of geometric or statistical nature, thus, athermal. The rate of dislocation
multiplication is defined by the mean free path swept by dislocations which
can be assumed to be proportional to the mean dislocation spacing 1 . The
second term describes the annihilation of dislocations, proportional to rN , the
number of dislocation segments per unit volume involved, their mean length rL
and the effective rearrangement rate r , rendering the process thermally-
activated. Since r rL N is proportional to , equation (1.15) can be rewritten,
relying on two parameters 1k and
2k , the latter being rate- and temperature-
sensitive [108]:
1 2k kt t
(1.16)
Later, numerous modifications and improvements of the model were suggested
[108–111]. Nowadays the model is commonly used to describe plasticity of BCC
and FCC materials, with many types of microstructure [112,113]. Using the laws
on the temperature- and rate-dependency of 2k proposed in [114], it was
1. Introduction
32
possible to apply the Kocks-Mecking model to characterize plasticity of different
tungsten grades in a range of temperature and strain rate, exploited
experimentally [115]. These laws will be applied in the present work to
extrapolate the mechanical properties of tungsten obtained in tensile tests to
higher temperature and higher strain rate ranges.
First of the questions addressed in the present research is whether the Kocks-
Mecking model can successfully be applied to and is sufficient for
characterization of plasticity of the ITER-specification tungsten in both as-
received and as-recrystallized states in the range of temperature and strain rate,
in which the mechanical tests were carried out.
1.3.4 Tensile tests
Tensile tests are the most widely performed mechanical tests, which allow one
to find out the response of material to mechanical deformation (elongation) and
extract several technologically-important characteristics, such as
- yield stress, the load at which plastic deformation commences
- uniform elongation, the deformation at which plastic instability takes
place
- ultimate tensile stress, the load at which plastic instability takes place
- fracture strain, or total elongation which material can sustain
- fracture stress, the maximal value of load that material can sustain
- reduction of area, a characteristics of plasticity that compares the cross-
section area before and after the test
Part of the samples was scheduled for irradiation in the BR2 material test reactor
to derive the material mechanical properties in the irradiated state, forcing the
use of miniaturized samples in order to fit the irradiation channels. Samples for
tensile tests can have circular or rectangular cross-section. Even though
cylindrical samples produced by turning or grinding are usually preferred in
mechanical testing due to axial symmetry, their fabrication from tungsten is
expensive and challenging, since the material is brittle at room temperature.
Electrical discharge machining (EDM) is a more appropriate tool for fabrication
of tungsten samples, as it introduces less damage compared to conventional
machining techniques. Since samples with rectangular cross-section use the
space in irradiation channels more efficiently and are easier for fabrication with
the help of EDM than round ones, this geometry, also called "dog-bone" (shown
in Figure 1.17) was adopted for the present project.
1. Introduction
33
a) b)
Figure 1.17. (a) Sketch of a miniaturized dog-bone-shape tensile sample, and (b) photo of a sample before and after tensile test.
Figure 1.18. A sample in the furnace of the Instron machine. The thermocouple wires are attached to the gauge section of the sample.
An Instron pull bench was used to perform displacement-controlled tensile tests
in air, hence the temperature was maintained below 600 °C to reduce oxidation
of tungsten. A sample placed in the furnace for testing in the Instron machine is
shown in Figure 1.18.
1. Introduction
34
A sample is pulled by the grips with a given speed, while its elongation and the
applied force are recorded. Then they are normalized by the sample dimensions
in order to be comparable with other tests.
Engineering stress is the ratio of the applied force F and the initial area of the
reduced cross-section IA
I
F
A (1.17)
Engineering strain eng is the ratio of elongation
0L L and the initial gauge
length 0L
0
0
eng
L L
L
(1.18)
The whole curve obtained in tensile tests serves as input in finite element
simulations, but in order to do so, true stress and true strain have to be extracted
from the experimental data, because the engineering quantities do not take large
strain into account, when the cross-section area significantly decreases
compared to the initial one.
The standard approach to extract true stress and strain is based on the
assumption of uniform deformation and is, thus, applicable up to the onset of
deformation instability only.
a)
b)
Figure 1.19. Examples of two main types of stress-strain curves encountered in the present work: a) low uniform elongation, “early necking”, b) high uniform elongation. The thick lines highlight the range of applicability of the standard approach to extract true stress and strain.
Two types of load-displacement curves have been obtained for the considered
tungsten grades. Recrystallized tungsten demonstrated high plasticity at high
temperature, with high uniform elongation (Figure 1.19a). The as-received
1. Introduction
35
material, however, is characterized by low uniform elongation, which is almost
absent at high temperature (500 °C, 600 °C) and is referred to as “early necking”
(Figure 1.19b). Significant part of the curve demonstrates softening. Thus, even
though the total elongation is high, indicating high plasticity, the standard
method of extraction is unable to obtain this information, being limited within
the range of strain, marked with the thick red line. An alternative method to
extract true stress-strain curve from engineering data with early necking,
involving reverse finite element analysis, is discussed in Chapter 2.
1.3.5 Scanning electron microscope and electron backscatter
diffraction
Scanning electron microscopy (SEM) was applied in order to investigate polished
surface of the investigated material. SEM JEOL 6610 located at SCK•CEN with
secondary electron detector (accelerating voltage 15 kV and working distance of
10–11 mm), which is based on the interaction of a focused monochromatic
electron beam with material. The details about this technique can be found in
[116]
Electron backscatter diffraction (EBSD) allows one to study grain size and
crystallographic orientation. It is based on recording and indexing of so-called
Kikuchi lines that are produced by the backscattered electrons that are
subsequently diffracted by the crystal planes. The detailed description of EBSD
technique can be found in [117]. A Field Emission Gun Quanta-450 FEI SEM with
20 kV acceleration voltage located in the Department of Materials, Textiles and
Chemical Engineering of Ghent University was used to scan the samples. The step
size was 1.2–2.0 µm. The specimen was mounted with 70° tilt in order to reduce
the path length of the backscattered electrons and to increase the intensity of
electron backscatter patterns. During the image post-processing using OIM
Analysis software, points with Confidence Index lower than 0.1 were removed.
The SEM investigation and EBSD analysis of tungsten for the present project has
been reported in [118].
1.3.6 Transmission electron microscope
Transmission electron microscope (TEM) JEOL 3010 EX, with acceleration
voltage 300 kV was used to investigate the microstructure of tungsten, namely,
the size of grains and subgrains, their aspect ratio and dislocation density, which
are relevant for the numerical models used in the present research.
The set-up of a TEM is comparable with that of an optical microscope. A beam of
electrons is generated by a hot cathode and is accelerated by high voltage. Then,
a combination of magnetic lenses focuses the electron beam on the sample. To
avoid undesirable interaction with gas molecules, the electron microscope is
operated under ultra-high vacuum conditions. After the interaction with the
specimen, the transmitted electrons pass through a second combination of
1. Introduction
36
magnifying lenses. Finally, the electrons hit a fluorescent screen producing an
enlarged image of the sample microstructure. The transparency of a TEM
specimen is acceptable up to thickness about 200 nm.
The TEM investigation of tungsten for the present project has been reported in
[32].
1.4 Outline of the thesis and the addressed
questions
ELMs, periodic plasma instabilities accompanying the plasma discharges in the
selected operational scenario of ITER, will deposit pulses of heat energy on the
divertor surface, causing cyclic thermal strain, the rate of which can reach 8 s-1,
while the temperature of divertor surface will exceed 1000 °C or even approach
the melting point. On the contrary, conditions in tensile tests of samples in a
mechanical lab are limited in terms of both temperature and strain rate.
Consequently, the applicability domain of constitutive laws directly derived from
tensile test results is merely a small fraction of the whole domain of ITER
operation conditions.
Willing to overcome this limitation and aiming at the analysis of mechanical
response of W to ELMs with the help of a finite element solver, we need to
extrapolate the experimental results using a physically-based model of plasticity.
The model developed by Kocks and Mecking has been chosen to this end, as it
predicts the evolution of microstructure of material (dislocation density) during
mechanical loading and links it with the material strength. The question whether
the temperature- and rate-sensitive plasticity of ITER-specification tungsten in
uniaxial loading can be successfully described by the Kocks-Mecking model in
the whole range of temperature and strain rate anticipated in ITER (or, how the
model should be modified in order to do so) is addressed in Chapter 2.
The Bauschinger effect and the associated kinematic hardening can substantially
change the mechanical response of material under cyclic loads, but they have
scarcely been studied in tungsten experimentally. Consequently, there was not
enough input for simulations of mechanical response of tungsten to cyclic heat
loads, necessary to estimate the conditions of crack formation. In the absence of
experimental results on mechanical cyclic loading of tungsten, we consider
limiting cases in the present project. In Chapter 3 we hypothesise how the
kinematic hardening should be incorporated in the model of plasticity, having
the results of uniaxial tensile tests as reference, and apply the modified model to
estimate the effect of the presence (or absence) of the kinematic hardening on
thermal fatigue of tungsten exposed to ELM-like thermal conditions. On top of
that we discuss how the macroscopic model of plasticity should be translated to
the microscopic level to be applied in the crystal plasticity framework. It is
necessary because microstructure of tungsten, including dislocation density,
crystallographic texture as well as grain size and shape, is an important factor
1. Introduction
37
that defines its mechanical properties and must be incorporated in the model, as
we cannot rely on the macroscopic, averaged stress.
Finally, in Chapter 4, we discuss the application of the obtained CPFEM model to
address the effect of microstructure and the kinematic hardening on mechanical
response of tungsten polycrystal subjected to ITER-relevant thermal shocks.
The work is devoted to the analysis of damage accumulation at the microscopic
level, which eventually leads to crack formation, in tungsten subjected to thermal
shocks due to ELMs. It is a challenging goal, even without consideration of
neutron irradiation defects in the material, that is why we limit the scope of the
thesis to non-irradiated tungsten. Thus, the present work is relevant for the first
years of operation of ITER, where numerous non-nuclear plasma experiments
will precede a short nuclear phase, during which the divertor is expected to
receive a limited neutron damage, ~0.1 dpa (displacements per atom) [20,119].
The advantage of the CP model is that it can further be extended to take account
of the modification of mechanical properties induced by neutrons.
39
Chapter 2.
Applicability of the Kocks-Mecking model
to temperature- and strain rate-sensitive
uniaxial deformation
of ITER-specification tungsten Equation Cha pter 2 Section 2
2.1 Introduction
In this chapter we address the question whether the Kocks-Mecking model can
be applied to characterise plasticity of ITER-specification tungsten by
reproducing the experimental stress-strain curves, as well as to extrapolate them
to high temperature and strain rate, expected in ITER. Part of this chapter
devoted to recrystallized tungsten has been published [120].
Plasma-facing components in ITER will host a very heterogeneous temperature
field, inducing large thermal strains. As a result of the combined action of
stationary heat loads and ELMs, the surface temperature can reach 2000–
3000 °C [121] and the strain rate can be as high as several s-1 [1]. The much lower
temperatures experienced at some distance below the surface make the material
stronger and less ductile. While aiming to assess the stress state inside plasma-
facing components during ITER operation, we need to rely on a constitutive law
valid in such wide ranges of temperature and strain rate. As temperature- and
strain-rate field continuously evolve in time, the constitutive law should be a
continuous function of the two quantities. The mechanical response is of course
also influenced by irradiation. This, however, is not accounted for in the present
work.
Tensile tests involving significant ductility of ITER relevant tungsten grades have
so far been reported for the grade labelled as M184 — in the recrystallized state
after heavy deformation — [1] and for IGP tungsten [26]. They reported
significant temperature and strain-rate sensitivity of plastic deformation. This
applies also to the ITER-specification tungsten fabricated by Plansee AG [57].
Zhu et al. [122] applied the Johnson-Cook model to characterize the work
hardening of commercially pure tungsten fabricated by AT&M in the
temperature range 20–700 °C and revealed a big difference between dynamic
compression and quasi-static compression of tungsten due to strain rate
sensitivity.
2. Kocks-Mecking model for ITER-specification tungsten
40
Deformation of W above 0.15Tm is primarily controlled by the motion of
dislocations, their multiplication and interaction with GBs [123]. Several
previous studies relied on this fact, using models based on the Kocks-Mecking
equation which links plasticity with thermally-activated dislocation-dislocation
interaction. Work hardening of double-forged commercially pure tungsten [115]
and potassium-doped tungsten [56], both fabricated by Plansee AG, was
described in this way at high temperature, reaching 1000 °C and 2000 °C
correspondingly.
The Kocks-Mecking plasticity model was successfully applied to other refractory
BCC materials, such as tantalum-tungsten (Ta-W) alloys [124], to simulate
material response to high strain rate loading. An Arrhenius model of plasticity
based on thermally-activated dislocation motion was used to numerically
characterize deformation of Ta polycrystal in a wide range of temperature and
strain rate, up to 104 s-1 [125]. It indicates potential applicability of this class of
models to tungsten at high temperature and strain rate as well.
Wang et al. [126] reviewed the applicability of six constitutive equations based
on Arrhenius, Johnson-Cook, modified Johnson-Cook, Zerilli-Armstrong,
modified Zerilli-Armstrong, and Khan-Huang-Liang models to the description of
hot deformation of powder metallurgy tungsten. The Arrhenius model was
shown to have the highest accuracy, since it considers the coupled effects of
strain, strain rate and deformation temperature on plasticity.
In this chapter we adapt and assess the applicability of a Kocks-Mecking
modelling of thermally-activated dislocation slip, to characterise mechanical
response of tungsten compliant with the ITER specification as well as
recrystallized tungsten. Tensile tests performed at SCK•CEN in the temperature
range 250–600 °C provide information for the parameterisation of the model. At
higher temperatures, experimental tensile tests are more difficult to carry out as
they require heat-resistant equipment and measures against rapid oxidation of
samples, such as reduction environment. Inspired by some successful previous
applications of the Kocks-Mecking model at high temperatures [56,115], we
expect that the present model will be valid beyond the temperature range of the
experimental curves used for the parametrisation. From a practical viewpoint,
the model should in any case be most accurate in the conditions favouring
damage development of IGP tungsten, which is not the highest operational
temperature range.
The constitutive law proposed here is suitable for FEA. In the next chapters, it is
used to study the mechanical response of tungsten subjected to complex thermo-
mechanical loads, e.g. cyclic heat loads resulting from the plasma instability
during operation of fusion devices.
The chapter is organized as follows. Section 2.2 describes the hardening law, the
first finite element model, and the mathematical algorithm used to fit material
parameters. Results of tensile tests and inverse finite element analysis (IFEA) are
presented in Section 2.3, followed by a discussion in Section 2.4.
2. Kocks-Mecking model for ITER-specification tungsten
41
2.2 Plasticity model and numerical techniques
2.2.1 Temperature- and strain-rate dependent hardening law
Whereas the experimental tensile tests presented in this chapter were
performed at a fixed temperature and strain rate, ITER operating conditions
involve varying conditions of deformation. Hence, the goal of the present section
is to select a strain hardening law enabling us to perform numerical analysis of
tungsten in wide range of temperature and strain rate with a single set of
material parameters. This was achieved by combining and adapting various
material laws. In particular, the widely used macroscopic Voce law, which
predicts that the true stress saturates at large strains, was enriched by
considering that the sensitivity of its parameters to temperature and strain rate
results from thermally activated dislocation slip.
The initial yield stress 0 depends on temperature T and strain rate according
to a phenomenological formula proposed by Voyiadjis et al. [127]. A constant
term 0
VS is introduced to account for non-zero lattice friction stress at high
temperature in BCC metals, material constants V and 1
V define the shape of
the curve, and superscript “V” stands for “Voyiadjis”.
11
1
0 01 ln
pV q
V V V
V
TS S
(2.1)
The increase of strength during plastic deformation (work hardening) follows
Taylor [108] according to whom the strength is proportional to the square root
of dislocation density . Since the initial yield stress is defined by an
independent formula, it is added in Equation (2.2) as a separate term.
Subtracting the square root of the initial dislocation density 0 in the equation
ensures that the equation produces the correct initial stress:
0 0A (2.2)
The parameter A defines the strength of dislocation interaction whose
evolution with temperature might be properly described by an exponential
decay function. But to simplify the optimization problem, it was assumed to
decrease linearly with temperature, in line with a publication devoted to another
grade of tungsten [115].
0 sA A AT (2.3)
The dislocation density is updated based on the Kocks-Mecking equation [108],
discussed in Section 1.3.3.3:
2. Kocks-Mecking model for ITER-specification tungsten
42
1 2M M k k
(2.4)
The Taylor factor M is the ratio between macroscopically measured equivalent
tensile stress eq and an average shear stress in slip systems, as well as the ratio
between an average shear in slip systems and the macroscopically measured
equivalent tensile strain eq . It usually takes values around 2.5–3, depending on
the crystal symmetry, on the loading mode and on texture [125]. It was assumed
to be 2.5 for as-received tungsten.
eq
eq
M
(2.5)
According to equation (2.4), saturation of the dislocation density (and,
consequently, the stress, according to equation (2.2)) occurs when the rate of
dislocation multiplication due to their mutual pinning is balanced by their
annihilation with other dislocations and GBs. These two processes are effectively
parameterized by coefficients 1k and
2k . Integrating equation (2.4) we obtain an
expression for the dislocation density as a function of the accumulated plastic
strain:
2
10
2 1
2 2exp 0.5
k
k k
Mk k
(2.6)
Combining this with equation (2.2) leads to the standard Voce law [128]
(representative of Stage III):
0
0
expVoce sat sat
(2.7)
where 0 is the yield stress calculated using equation (2.1), is the
accumulated plastic strain, sat is the saturation stress:
1
0 0
2
sat
kA
k
(2.8)
and the characteristic strain 0 is related to the initial hardening rate:
0
2
2
Mk (2.9)
It will be shown later in this chapter that experimental curves are much better
reproduced when considering that the strain hardening, rather than flow stress,
saturates to a constant value, which has been referred to as Stage IV hardening.
Inspired from the work of Prinz et al. [129] who considered a cellular dislocation
2. Kocks-Mecking model for ITER-specification tungsten
43
structure in which the cell walls had non-saturating dislocation density, and
anticipating non-saturating stress-strain curves of the studied grade of tungsten,
we added a linear term KMH to equation (2.6) in order to let the total
dislocation density increase beyond the saturation value
2
1
2
k
k
at large strain:
2
10
2 1
2 2exp 0.5KM
k
k kH
Mk k
(2.10)
Then, the stress-strain relationship becomes:
10
2 1
0 0
2 2exp 0.5KM
k
k kA H
Mk k
(2.11)
For mathematical convenience, linear hardening is effective already at the onset
of plasticity but its contribution becomes predominant only after attaining large
strain, when the saturation is achieved. The evolution of hardening rate with
strain can be derived from equation (2.11):
12 0
2
2
0.5
exp 0.5KM
kMk
kA H
Mk
(2.12)
By matching equations (2.7) and (2.11) we find the link between parameters of
the Voce equation and the Kocks-Mecking model:
0 0
1
0
2 sat Ak
AM
(2.13)
As proposed in [115], 1k is constant, whereas
2k accounts for the fact that
dislocation recovery is a thermally activated process [114], introducing the
temperature- and rate-sensitivity of the model:
2 1 2
0
1 lnk C C T
(2.14)
Here 1C ,
2C and 0 are constants. The dislocation annihilation parameterized
by 2k , becomes more significant at higher temperatures.
2. Kocks-Mecking model for ITER-specification tungsten
44
2.2.2 Finite element simulation of tensile test beyond the onset of
deformation instability
There exists a standard approach to extract true stress-strain (S-S) curves,
representative of the actual capacity of material to resist mechanical loads, from
the engineering S-S curves measured experimentally, as discussed in Chapter 1.
However, its application is limited up to the onset of deformation instability —
necking. Hence, when the material exhibits low uniform elongation, a significant
part of the experimental results is unsuitable for characterisation with the
standard approach. An alternative method is necessary in order to extract the
true material response at strains beyond uniform elongation.
One group of alternative methods relies on the measurement of the sample
cross-section during tension, which can be done using video recording and
consequent image processing [130,131].
Another approach is to use inverse finite element analysis (IFEA). In the
conventional direct FEA, a known true S-S curve (constitutive law) is used to
predict the mechanical response of a component with an intricate shape or a
non-uniform loading. On the contrary, IFEA identifies iteratively the constitutive
law which leads to the best reproduction of a known mechanical response,
usually in a specimen with simple shape and loading. Such numerical approach
has been applied not only for extraction of a constitutive law [132–135], but also
for geometry optimisation [136,137]. In this chapter we develop an algorithm
which allows extracting true material properties beyond the uniform elongation
range.
The physically-based model of plasticity described in the previous section was
implemented in the form of a UHARD, a user-defined subroutine for the standard
FE solver Abaqus. Both elasticity and plasticity are assumed isotropic (J2 theory)
and the UHARD defines only the strain hardening. The routine is called at every
increment and every iteration of the simulation in every integration point of the
finite element mesh. Thus, a non-uniform strain rate field across a sample can be
properly processed, being especially important after the onset of deformation
instability. Indeed, the necking region, where strain rates are largest,
experiences more hardening, hindering a fast strain localisation.
In order to take account of the decrease of the axial force after the onset of diffuse
necking, necessary to construct a constitutive law at large strain, we have
performed displacement-controlled FE simulations of the tensile tests with the
help of the commercial finite element solver Abaqus 6.17-1. The sample
geometry shown in Figure 2.1 represented the experimental specimen with a
gauge length 5.2 mm and cross-section dimensions 1.6×1.8 mm2. The sample
was meshed into about 3100 second-order tetrahedral elements varying in size
from 0.2 mm in the gauge middle area to 2.0 mm in the grips with the help of
Gmsh software [138].
2. Kocks-Mecking model for ITER-specification tungsten
45
A small tapering (geometry imperfection) of 1 m was introduced in the central
cross-section of the mesh to ensure a stable development of plastic instability
(necking) in the gauge. Such imperfections are permitted in tensile experiments
according to the ASTM standard E8M-16a [139] and are widely used in FEA of
tensile tests, usually measuring 10-4–10-3 of the sample thickness [135,140,141].
An example of von Mises stress distribution in the sample is presented in Figure
2.1b. The snapshot was taken at the initiation of plastic instability, when the
stress field in the specimen gauge became non-uniform.
The force applied to the sample in the axial direction and the sample elongation
were recorded and recalculated into engineering S-S curves with the help of a
Python script.
Figure 2.1. A tensile sample used in FE analysis a) in the non-deformed state; b) at the onset of deformation instability. Colours represent the von Mises stress, ranging from 0 (in the grips) to 400 MPa (in the centre).
2.2.3 Optimisation algorithm
2.2.3.1 Basics of downhill simplex method
The best set of material parameters is determined while considering all tensile
tests performed on a given W grade and by applying an advanced optimisation
method.
The Nelder-Mead method (also known as “downhill simplex method”, “amoeba
method”, or “polytope method”) is a numerical method used to solve
optimization problems, i.e. problems where the minimum or maximum of an
objective function has to be found [142]. A usual meaning of an objective function
is the measure of the deviation of the results predicted by the model from the
corresponding experimental results, typically expressed as the sum of squares of
their difference.
The algorithm operates in a multidimensional parameter space, and, being a
direct search method, does not require the calculation of the objective function
derivatives (contrary to the steepest descent method and other gradient
2. Kocks-Mecking model for ITER-specification tungsten
46
methods). As will be shown further, the objective function designed for the
purpose of finding the constitutive law, involved calling an external software —
a finite element solver. It made impossible the calculation of the objective
function derivative, justifying the choice of the optimization algorithm.
The method uses the concept of a simplex, which is a generalisation of a
polyhedron in an n-dimensional space, with n+1 vertices. The n-dimensional
parameter space is formed by the n independent parameters in the optimization
problem. The search begins from a predefined initial point, and the search
domain should be limited to mitigate possible numerical issues. The algorithm
evaluates the objective function at every vertex, and extrapolates its behaviour
in order to replace the “worst” vertex (where the objective function is the
largest) with a new one.
The downhill simplex method foresees a few possible scenarios of defining the
new vertex in as few attempts as possible, expecting the objective function to
eventually be lower; but discussion of the exact scenarios is out of scope of the
present work. In this manner, iteration after iteration, the algorithm probes
numerous parameter sets and eventually reaches the objective function
minimum. It means reaching the best possible match between the experimental
and simulated data if the objective function is a measure of deviation between
the two.
2.2.3.2 IFEA based on the downhill simplex method
An iterative algorithm based on the downhill simplex method and IFEA has been
coded in the R programming language and implemented as a shell that combines
the input-output interface, the objective function and the call to the downhill
simplex method. The simplex method implemented in the “neldermead” package
has been selected [143].
The flowchart of the algorithm is shown in Figure 2.2. It receives a set of N
engineering “target” S-S curves (obtained experimentally in a range of
temperatures and strain rates) and an initial set of the plasticity model
parameters, that form a point in the 7- dimensional parameter space (0 ,A ,SA
1,C 2 ,C
0 , 1,k
KMH ). Then a simplex with eight vertices is constructed around
this point. The objective function is evaluated at all these points, followed by
identification of the worst vertex and its replacement with a better one. The
objective function is then evaluated at the new point in the following iteration,
and the process repeats in a loop until the objective function minimum is found.
The finally obtained parameter set (0 ,fA ,f
SA 1 ,fC
2 ,fC 0 ,f
1 ,fk f
KMH ) yields a
constitutive law, which, being provided as input to a simulation of tensile test,
would return the closest match between the simulated and experimental
engineering S-S curves in the whole range of temperature and strain rate
simultaneously.
2. Kocks-Mecking model for ITER-specification tungsten
47
Figure 2.2. Flowchart of the iterative algorithm for the plasticity model fitting to multiple stress-strain curves simultaneously.
Every evaluation of the objective function involved launching N simulations of
tensile test in Abaqus with the mesh shown in Figure 2.1 and the plasticity model
discussed above as the constitutive law. It has to be noted that the simulated
engineering S-S curves were observed to deviate from the target ones beyond
certain strain even in the last iterations of the algorithm, hence the range of
strain for the objective function evaluation was capped at 24%–40% identified
for each curve individually depending on temperature. In spite of that, the range
of strain available for fitting was much larger than the uniform elongation,
2. Kocks-Mecking model for ITER-specification tungsten
48
summarized in Figure 2.7b. Besides, if an engineering S-S curve featured a yield
drop, then only the part beyond the yield drop was taken as a target curve, given
that the plasticity model is applicable to monotonically increasing curves only
(in terms of true stress).
The objective function was calculated as the sum of squares of differences
between the engineering stress , obtained in a simulation iteration, and the
target engineering stress (obtained experimentally) plus the sum of squares of
differences between their derivatives with respect to engineering strain (i.e.,
stress-strain slope ), according to Equation (2.15). The derivatives were
calculated with the finite difference method. A weight coefficient = 5·10-3 had
to be introduced to tune the contribution of both quantities to the total value of
the objective function. The differences were evaluated at a set of P discrete points
separated by strain spacing , whose optimal value was found to be 2%.
2 2
exp exp
1 1 1
N P Psim sim
i i i i
j i i
(2.15)
a) b)
Figure 2.3. Illustration for the evaluation of the objective function. The sum of squares of differences is calculated at a discrete set of strain values, marked with circles. Both the engineering stress (a) and the stress-strain slope (b) contribute to the total value of the objective function. The arrows indicate that as the simulation result approaches the target, the objective function decreases.
Figure 2.3 illustrates the calculation of the objective function for a single S-S
curve from the two contributions: a) the S-S curve itself and b) the stress-strain
slope. As mentioned above, only the part of the experimental S-S curve indicated
with the solid line is used for the search. The dashed line shows the complete
experimental S-S curve for clarity. The sum of squares of differences between the
experimental (target) and the simulated curves was evaluated at a discrete set
of strain values (shown by circles).
Figure 2.4 illustrates the evolution of the input constitutive law (a) and the
produced output engineering S-S curves compared with the target one (b) in a
few iterations of the search process for a single combination of temperature and
2. Kocks-Mecking model for ITER-specification tungsten
49
strain rate. The change of shape of the input S-S curve was due to the change of
the plasticity model parameter set from iteration to iteration, guided, in turn, by
the downhill simplex algorithm. The corresponding engineering S-S curve might
occasionally deviate from the target when the simplex algorithm substitutes the
“worst” vertex with a “not-so-good” one; such directions of search in the
parameter space are discarded. At certain iteration the tensile test simulation
returns an engineering S-S curve perfectly matching the target within defined
range of strain, and the search stops.
a)
b)
Figure 2.4. The evolution of a) input true S-S curves, b) output engineering S-S curves in several iterations of the search algorithm.
2.3 Results
2.3.1 Experimental tensile tests
Tensile tests were performed at SCK•CEN (Belgium) in the temperature range
250–600 °C and strain rates 6·10-5–6·10-3 s-1 on commercially pure W produced
by Plansee AG according to the ITER specification [20], referred to as “IGP” and
described in Chapter 1. The material was not subjected to neutron irradiation
and was tested in two states: as-received and recrystallized. However,
investigation of tungsten after neutron irradiation is planned for the future, thus
2. Kocks-Mecking model for ITER-specification tungsten
50
the miniaturized design of tensile samples has been selected to comply with the
dimension limitations in the irradiation channels in the material testing reactor
BR2 (Belgium). For instance, fusion-relevant irradiation of tungsten (up to ~1
dpa) can be performed inside fuel elements, where the channel is merely 15 mm
in diameter.
Experimentally obtained engineering stress-strain curves for as-received IGP
tungsten are shown in Figure 2.5 with dashed lines. This tungsten grade has a
high ductility even at 250 °C and high yield stress, 500–700 MPa.
Figure 2.5. Engineering stress-strain curves for as-received IGP tungsten. Solid lines highlight the range of uniform deformation.
It is known that the maximum of engineering stress (ultimate tensile strength
UTS) corresponds to the onset of deformation instability. Necking causes a rapid
decrease of the central cross-sectional area of a sample. The deformation ceases
to be uniform and the standard approach to extract true stress and strain
becomes invalid from that moment. The solid lines in Figure 2.5 correspond to
the uniform deformation range and show that significant part of the
experimental results cannot be processed with the standard approach. That is
why an advanced method based on IFEA is applied to parameterize the plasticity
model for as-received IGP tungsten.
2. Kocks-Mecking model for ITER-specification tungsten
51
Figure 2.6. Engineering stress-strain curves for the recrystallized tungsten.
a) b)
Figure 2.7. a) Yield stress and ultimate tensile strength as well as b) uniform elongation and total elongation of both grades of tungsten tested at 6·10-4 s-1.
The experimental engineering stress-strain curves for the recrystallized
tungsten are plotted in Figure 2.6. It has low ductility at low temperature, which
nevertheless increases with the temperature increase. The yield stress is much
lower than in the as-received W, but the work hardening capacity is much higher
in recrystallized tungsten. The values of yield stress and UTS as well as uniform
and total elongation of the two grades of tungsten are summarized in Figure 2.7.
2. Kocks-Mecking model for ITER-specification tungsten
52
2.3.2 Results of inverse finite element analysis
2.3.2.1 As-received tungsten
The parameters describing the evolution of the yield stress values as a function
of temperature and strain rate (equation (2.1)) were fitted before considering
the strain hardening. Following [144], the values of p and q were fixed at 0.5 and
1.5, respectively. The other parameters, identified with the help of a non-linear
least-squares optimisation method, are summarised in Table 2.1. A comparison
of the experimentally measured yield stress values and the predicted ones is
shown in Figure 2.8 for three different strain rates.
Table 2.1. Set of parameters reproducing the yield stress of as-received IGP tungsten.
VS , MPa V , K 1
V , s-1 0
VS , MPa p q
2886 1.91·104 2.8·107 495 0.5 1.5
Figure 2.8. The best fit of equation (2.1) to the yield stress of as-received IGP tungsten at different temperatures and strain rates.
In order to find the strain hardening parameters, the IFEA of the tensile test
combined with the iterative algorithm discussed above was applied to N = 15
experimental engineering S-S curves. The initial parameter set, i.e. the starting
point for the search, was roughly estimated, based on the typical order of
magnitude of the quantities involved in equations (2.2)–(2.12). The initial
dislocation density was set equal to 4.5·1012 m-
2, as measured by TEM[32].
2. Kocks-Mecking model for ITER-specification tungsten
53
Figure 2.9. True stress-strain curves of as-received IGP tungsten obtained with the help of IFEA of tensile test.
Figure 2.10. Engineering stress-strain curves obtained in the last iteration of the IFEA of tensile test for as-received IGP W, compared to the experimental data.
2. Kocks-Mecking model for ITER-specification tungsten
54
The finally obtained true S-S curves for all the tested samples of as-received IGP
tungsten are summarised in Figure 2.9. Note that the algorithm considered
responses far beyond uniform elongation, and the final plastic strain reached
values of 0.8–1.0, corresponding to localized plastic strain in the thinnest cross-
section of a sample, i.e. in the necking region.
The accuracy of the theoretical constitutive law for as-received IGP tungsten can
be checked by comparing the engineering S-S curves at the last iteration of the
IFEA. This is done in Figure 2.10. As mentioned above, the range of strain for the
curve fitting has been capped. Nevertheless, a perfect match has been achieved
for all the curves in the whole tested range of temperature and strain rate well
beyond uniform elongation, thus covering the mechanical response of material
after the onset of deformation instability.
The model parameters fitted to characterise plasticity of IGP tungsten in the IFEA
are summarised in Table 2.2. The coefficient at the linear term HKM is nearly zero,
indicating the validity of the standard Voce equation for as-received tungsten.
Table 2.2. The fitted parameters of the plasticity model for as-received IGP W.
0
fA ,
MPa·m-1
f
sA ,
MPa·m-1 K-1 1
fC 2
fC ,
K-1 0
f ,
s-1 1
fk ,
m-1
f
KMH ,
m-1
4.38·10-4 ≈0 1.17·10-4 0.348 5.1·107 2.64·106 ≈0
2.3.2.2 Recrystallized tungsten
This subsection contains material published by our team in [120], corrected and
improved afterwards.
Similarly to the analysis of as-received tungsten, yield stress of recrystallized
tungsten was fitted first with the help of equation (2.1) using a non-linear least
squares optimisation method. The values of p and q were fixed at 0.5 and 1.5 as
well. Unfortunately, even after trying various starting points (to avoid ending the
search at a local minimum instead of the global one) and after setting different
limits in the parameter space, this equation did not adequately reproduce the
experimental yield stress. Figure 2.11 summarises the experimental yield stress
and the curves corresponding to the closest obtained match (dashed lines).
An alternative to equation (2.1) was proposed by Beyerlein and Tomé [114], who
observed an exponential decay of the initial yield stress with temperature in low-
symmetry metals, including zirconium, magnesium, beryllium and -uranium
[145]. An enhanced equation version was used to describe the evolution of yield
stress in tantalum-tungsten alloys [124] and another grade of tungsten in [115].
Superscript “B” stands for “Beyerlein” and distinguishes the parameters
corresponding to equations (2.1) and (2.16), respectively.
0 0
1
exp ln 1B B B B
B B
TS K S
(2.16)
2. Kocks-Mecking model for ITER-specification tungsten
55
BS , B , BK , 1
B and 0
BS are constants defining the shape of the curve. This
equation showed a better match with the experimental data, after being fitted
with the help of the nonlinear least-squares optimization method, even though
the chemical composition of the two tungsten grades is identical. The difference
seems to originate from different grain size and GB types: a larger fraction of low-
angle boundaries is present in the as-received tungsten. Corresponding curves
are shown in Figure 2.11 with solid lines. The fit of yield stress with equation
(2.16) is used further in the text.
Figure 2.11. Yield stress of recrystallized W. Symbols represent experimental data, and lines highlight its evolution with temperature at given strain rates, obtained using two different fitting functions.
Table 2.3. The best fitted parameter set of equation (2.1) to describe yield stress of recrystallized tungsten.
VS , MPa V , K 1
V , s-1 0
VS , MPa p q
2464 7.61·103 9.48 149 0.5 1.5
Table 2.4. The best fitted parameter set of equation (2.16) to describe yield stress of recrystallized tungsten.
BS , MPa B , K K 1
B , s-1 0
BS , MPa
657 278 0.44 1.22·10-6 90.6
2. Kocks-Mecking model for ITER-specification tungsten
56
Figure 2.12. Experimental true stress-strain curves of recrystallized tungsten.
Figure 2.13. Hardening rate derived from experimental true stress-strain curves of recrystallized IGP tungsten
2. Kocks-Mecking model for ITER-specification tungsten
57
The set of material parameters of equations (2.1) and (2.16) allowing the best fit
of recrystallized tungsten are summarised in Table 2.3 and Table 2.4
respectively.
Given the large uniform elongation of recrystallized tungsten at high testing
temperatures, it would have been possible to derive true S-S curves with the help
of the standard approach (Figure 2.12). Nevertheless, parameterization of the
strain hardening parameters accounted for the material response beyond the
necking point.
The hardening rate, derived from the true S-S curves, is shown in Figure 2.13. It
highlights the deviation from the standard Voce equation, and the necessity of an
extra linear term in equation (2.11).
The iterative algorithm was used to perform the IFEA of the tensile test and
parameterize the hardening law. As mentioned in Chapter 1, the initial
dislocation density 0 measured in recrystallized W with the help of TEM was
1011 m-2 [32]. The parameter set, that provides the best match between the
model prediction and the experimental engineering S-S curves, is summarised in
Table 2.5, where 1C ,
0 and 1k were adopted from a paper on a similar grade of
tungsten [115]. The parameters 1k and
0 could be incorporated directly,
whereas comparing equation (2.14) in the present work and Eq. (9) in [115]
leads to
1
1
k bC
g
(2.17)
where is an interaction parameter, b is the Burgers vector and g is the
normalized activation energy; all three values being reported in the cited paper.
Table 2.5. The fitted parameters of the plasticity model for recrystallized tungsten.
0
fA ,
MPa·m-1
f
sA ,
MPa·m-1 K-1 1
fC 2
fC ,
K-1 0
f ,
s-1 1
fk ,
m-1
f
KMH ,
m-1
6.37·10-6 2.7·10-9 4.2·10-5 20.75 107 4.8·108 6.4·107
Figure 2.14 shows both experimental (solid) and modelled (dashed) true stress-
strain curves for recrystallized tungsten deformed at different strain rates and
temperatures. The stress-strain curves for 300 °C and 400 °C show that the
quality of fit is reduced at low temperature due to the narrow range of strain, i.e.
the low total elongation of recrystallized tungsten below 400 °C. However, the
match between the model prediction and experimental curves at 500 °C and
600 °C is excellent.
2. Kocks-Mecking model for ITER-specification tungsten
58
Figure 2.14. Experimental and fitted true stress-strain curves for recrystallized IGP tungsten at strain rate 6·10-4 s-1.
Figure 2.15. Experimental and simulated engineering stress-strain curves at 500 °C and 600 °C for recrystallized tungsten.
Figure 2.15 compares engineering S-S curves obtained in experiments (solid)
and in the last iteration of simulations (dashed). They are grouped according to
the test temperature and the strain rate. A good match is observed between them
up to the onset of plastic instability, shortly after which the model tends to
overestimate strength and fracture strain. The latter is most probably due to
ductile damage accumulation taking place in the material, but not accounted for
in the model. For the same reason as for the as-received tungsten, the strain
range within which the search of true S-S curve is performed, should be capped.
2. Kocks-Mecking model for ITER-specification tungsten
59
2.4 Discussion
2.4.1 Strain-rate sensitivity
Speaking of the applicability of the parameterized plasticity model to the
simulations of thermal loads relevant to ITER, the major concern is the strain
rate, which differs by orders of magnitude between quasi-static tensile tests and
the dilatation-contraction cycles caused by ELMs. So far tensile tests of IGP
tungsten have been performed at low strain rate, 10-3–10-5 s-1, thus no data are
available to calculate reliable parameters of the model at high strain rate.
However, an insight into strain-rate sensitivity of tungsten at high rates can be
gained from literature analysis.
Figure 2.16. Illustration of rate sensitivity of tungsten (other than IGP) in a wide range of strain rate, showing the true stress at 4% of strain as a function of strain rate [146].
Mechanical tests on another tungsten grade, an extruded tungsten rod from
Teledyne Firth-Sterling by the Army Research Laboratory, USA, have been
reported [146]. The experiments have been performed in a wide strain rate
range and included quasi-static compression (10-3–100 s-1), compression Kolsky
bar tests (103–104 s-1) and pressure-shear plate impact tests (104–105 s-1).
To detect strain rate sensitivity of that tungsten grade, the value of true stress
recorded at 4% of true strain was plotted as a function of strain rate, as
illustrated in Figure 2.16. There is a clear linear trend for both recrystallized and
as-received tungsten states in the range of strain rate up to 102 s-1 (shown with
2. Kocks-Mecking model for ITER-specification tungsten
60
dashed lines). This result indicates that the rate sensitivity of other tungsten
grades measured in tensile tests at low strain rate might as well be extrapolated
to higher rates, including 8 s-1 expected in the divertor monoblocks exposed to
ELMs. This way to show rate sensitivity was also applied in [101], where stress
measured at 0.15 strain was plotted against strain rate for copper single crystals
and revealed a linear trend up to strain rate around 103–104 s-1 as shown in
Figure 2.17.
Figure 2.17. Strain rate sensitivity for Cu deformed in compression at 25°C, shown as the stress at 15% of strain as a function of strain rate. [101].
2.4.2 Deformation stage IV
2.4.2.1 Deviation from the Voce equation
The true S-S curves obtained for the recrystallized IGP tungsten deviate from the
standard Voce equation, and require an extra non-zero linear term in it. Also, the
standard Voce equation prescribes the hardening rate to be a decreasing linear
function of true stress, which reaches zero at the saturation stress sat (Figure
2.18). The hardening rate calculated for recrystallized tungsten does not follow
this trend and approaches zero asymptotically with the increase of stress (Figure
2.19b).
2. Kocks-Mecking model for ITER-specification tungsten
61
Figure 2.18. Hardening rate as a function of true stress indicates the presence of deformation stages III and IV (solid line). Hardening rate derived from the standard Voce equation is shown by the dashed line for clarity.
A similar behaviour was detected in S-S curves reported in other works on
recrystallized tungsten. Figure 2.19 collects the engineering S-S curves obtained
at 500 °C (a) and the calculated hardening rate (b) from two other works apart
from the present project. Labels “U1” and “U2” correspond to tungsten
recrystallized at 1750 °C during 2 h in vacuum tested at different deformation
speed, 0.2 mm min-1 and 42 mm min-1 correspondingly and reported by
Uytdenhouwen [1], and label “W1” shows the results of IGP tungsten
recrystallized at 1600 °C during 1 h in vacuum tested by Wirtz et al. [26]. The
hardening rate calculated from tensile curves for these samples approaches zero
asymptotically as well, being a feature of deformation stage IV.
2.4.2.2 What is deformation stage IV?
Deformation stage IV in FCC and BCC metals and alloys was observed in tests
where large deformation can be attained, such as torsion, where the
development of deformation instability in a sample is postponed [147,148].
Instead of reaching saturation at the end of stage III, the true stress maintained
basically linear increase within a wide strain range (up to ~10 in Fe, and ~5 in
Ni at room temperature) [148].
The occurrence of stage IV hardening is often attributed to the formation of a
cellular dislocation structure inside individual grains. Several approaches have
been proposed to understand the cellular structure formation and its impact on
the subsequent stress-strain evolution [129,149,150]. Although the dislocation
density in the cell interiors does indeed saturate with strain, in accordance with
the Kocks-Mecking model, the dislocation density in the cell walls keeps growing
and thus contributes to further hardening.
Notably, most of those works dealt with FCC metals due to their superior
capacity for plastic deformation as compared to BCC metals. However, the
cellular structure was also observed in BCC tungsten deformed in compression
in the range from room temperature up to 600 °C [151,152]. The microstructure
2. Kocks-Mecking model for ITER-specification tungsten
62
of single crystal tungsten and dilute W-based alloys was investigated in a wide
temperature range from -123 °C (0.04Tm) up to 317 °C (0.16Tm) under
compressive deformation [153].
a)
b)
Figure 2.19. (a) Engineering stress-strain curves and (b) hardening rate for different grades of recrystallized tungsten obtained by uniaxial tensile tests at 500 °C [1,26].
The Kocks-Mecking–like models, modified in order to account for cellular
structures, were successfully used to describe deformation stage IV in FCC
metals with the help of a second state variable associated with lattice
incompatibility [109] as well as in BCC metals and alloys including pure tungsten
[112] and Ta-10W alloy by introduction of a separate dislocation substructure
density [124].
2. Kocks-Mecking model for ITER-specification tungsten
63
2.4.2.3 Evidence of deformation stage IV in tungsten
The microstructure evolution during plastic deformation in ITER-specification
tungsten was investigated by our team based on TEM examination after
interrupted tensile tests at 600 °C [152]. Due to the lack of recrystallized IGP
tungsten at our disposal, these observations were performed on double-forged
tungsten grade samples (provided by Plansee AG as well) after recrystallization
(and denoted as DFR, standing for “double-forged recrystallized”). Although the
annealing of both DFR and IGP grades was performed under the same conditions
(1600 °C during 1 h), the values of dislocation density in the samples did not
coincide and amounted to 5·1012 m-2 and 1011 m-2 correspondingly. Figure 2.20
demonstrates that samples deformed up to 20% contained dislocation tangles
(precursors of dislocation walls) and those deformed up to 28% showed the
formation of cells, resulting in grain refinement [152].
Figure 2.21 provides a comparison between the experimentally measured
dislocation density and the prediction of the present model, revealing that the
model overestimates the dislocation density. The initial dislocation density used
in this particular calculation was assumed to be equal to 5·1012 m-2,
corresponding to the experimental value measured in the DFR tungsten, for
which the interruptive tests were performed [115]. It should, however, be noted
that the experimental measurements excluded the dislocation density in the cell
walls, which were considered as precursors of low angle GB. Whereas the
dislocation density in the present model should be thought of as a weighted
average of dislocation density in the bulk and that in the cell walls. This
contributes to the discrepancy between the model results and the experimental
data.
Exploring the existing TEM images we can already assume the value 3·1015 m-
2
as a preliminary estimation of dislocation density in the dislocation tangles.
Zones I and II shown in Figure 2.20 correspond to the grain interior and
dislocation tangles, where the dislocation density was identified. This value is
much higher than the bulk dislocation density, such that the weighted average
dislocation density in tungsten after 20% deformation appears to be in the range
between 3·1014 m-2 and 1015 m-2, which is closer to the model prediction.
The discussed approach was selected as a quick and simple way to parameterize
the tensile S-S curves of recrystallized tungsten, which are important for FEA of
stress state in PFCs. It would be possible to fit the plasticity model starting from
experimentally measured dislocation density, provided it is known as a function
of strain, test temperature and strain rate. Note that the “weighted” dislocation
density would be necessary, which accounts for dislocation storage in both cell
interior and walls.
Then, the plasticity model would have to be fitted in two stages: first to
reproduce the dislocation density, adjusting 1k ,
1C , 2C and
0 , and second, to
reproduce tensile S-S curves, adjusting the remaining model parameters only.
2. Kocks-Mecking model for ITER-specification tungsten
64
a)
b) c)
Figure 2.20. TEM micrographs showing dislocation tangles (a, b) and dislocation cells (c), probed by TEM at 20% (a, b) and 28%(c) of plastic strain in the DFR tungsten. The grain refinement was observed in the tests performed at 500 °C and 600 °C after 20% plastic strain. Zones I in the images show examples of the grain interior, while zones II correspond to dislocation tangles where the dislocation density was measured [120].
This approach would result in a more accurate extrapolation of mechanical
properties to high temperature, but would require a number of interrupted
tensile test series, followed by laborious TEM analysis.
Observation of dislocation cells in the recrystallized tungsten is in line with the
detection of deformation stage IV on the S-S curves. Dislocation cells have also
2. Kocks-Mecking model for ITER-specification tungsten
65
been observed in TEM images of as-received IGP tungsten [152], but stage IV has
not been detected during the analysis of deformation curves, and the use of the
standard Voce equation leads to a good match with the experimental curves.
The apparent discrepancy can be explained by the difference in grain size.
Formation of numerous dislocation cells in large grains of recrystallized
tungsten significantly hinders the dislocation motion, leading to an increased
hardening and pronounced stage IV. On the contrary, dense GB network in as-
received tungsten is already a strong obstacle for dislocation motion, and the
fraction of newly formed cell walls is nearly negligible from the point of view of
dislocation motion.
Figure 2.21. Dislocation density predicted by the model superimposed on the experimental data from [115].
2.4.3 Individual curve fitting with the iterative algorithm
The proposed optimization algorithm can also be used to extract constitutive law
from individual engineering stress-strain curves. In this case the plasticity model
reduces to the Voce equation (2.7), and the algorithm searches for the best set of
the Voce parameters (0 , sat ,
0 ). The question is, whether the fitting of
individual curves would reveal the temperature- and rate-dependency of these
parameters.
2. Kocks-Mecking model for ITER-specification tungsten
66
Figure 2.22. Flowchart of the iterative algorithm for the Voce equation fitting to a single stress-strain curve.
The flowchart of this reduced algorithm is shown in Figure 2.22. It is different
from the algorithm for multiple curve fitting, outlined in Figure 2.2, in the sense
that the search is performed in a 3-dimensional parameter space (accelerating
the search), the simplex has 4 vertices, and the objective function is calculated
for a single engineering S-S curve, as long as N = 1 in equation (2.15).
2. Kocks-Mecking model for ITER-specification tungsten
67
Figure 2.23. Engineering stress-strain curves, as a result of FE simulation of a tensile test, using the best constitutive laws obtained with the help of individual curve fitting. Dashed lines show corresponding experimental results.
Engineering S-S curves obtained in the experiments and those found with the
help of IFEA of individual curves are summarized in Figure 2.23. The match
between the experimental and simulated results has improved, compared to
Figure 2.10. Strain range well beyond the onset of deformation instability has
been covered as well.
Given such high quality of fit, one would expect that the obtained parameters of
the Voce equation for individual curves could reveal trends, being plotted against
temperature and strain rate. To check that, the values of the characteristic strain
0 and the saturation stress sat are plotted in Figure 2.24 (a) and (b)
correspondingly. However, no clear trend is observed for neither quantity; the
values are quite scattered and even increase around 600 °C, whereas a
monotonic decrease is expected according to the plasticity model outlined above.
Thus, this approach does not have predictive power: the results cannot be
extrapolated to higher temperature and strain rate.
Another noticeable feature is the correlation between 0 and
sat . It means that
the Voce equation is less sensitive to simultaneous proportional change of the
two parameters, compared to their separate variation (especially considering
the fact that the simulation deals with a part of the Voce curve, limited up to true
strain ~1). In this case many pairs of 0 and sat located in the vicinity of the
2. Kocks-Mecking model for ITER-specification tungsten
68
found pair (0
f , f
sat ) could result in almost identical true S-S curves, thus,
forming a set of solutions which the IFEA of individual engineering S-S curves
cannot distinguish within the tolerance defined by the downhill simplex method.
Effectively it means quite large vertical error bars in Figure 2.24.
a)
b)
Figure 2.24. The Voce parameters 0 (a) and sat (b) as a function of temperature,
obtained in the IFEA of individual experimental S-S curves.
To complete the comparison of the two approaches, a similar analysis should be
made for the model fitting to multiple curves. The material constitutive
behaviour at every combination of temperature and strain rate can be described
with the Voce equation, whose parameters can be calculated using the plasticity
model and the found set of parameters (0
fA , f
sA , 1
fC , 2
fC , f
o , 1
fk , f
KMH ).
The characteristic strain 0 and the saturation stress
sat , being a result of
plasticity model fitting to multiple experimental curves, are shown in Figure 2.25
(a) and (b) correspondingly, as a function of temperature. Both quantities clearly
follow the theoretically prescribed trends, and can be extrapolated to higher
temperature and strain rate, relevant for ITER. They are quite large compared to
2. Kocks-Mecking model for ITER-specification tungsten
69
usual values, for instance 0 being typically in the range 0.1–0.5. The difference
is that the Voce equation is applied here to a material with low uniform
elongation and large total elongation, which means a sooner fulfilment of the
Considère criterion and later attaining the saturation stress. Consequently, both
sat and 0 must be larger than in materials with high uniform elongation, what
results in true constitutive laws with low curvature, as seen in Figure 2.9. Even
though it resembles the non-saturating constitutive law, observed in the
recrystallized tungsten, the IFEA returned a negligibly small value of the linear
coefficient KMH for as-received tungsten. Since fewer degrees of freedom result
in an enhanced fit accuracy, it is beneficial for the parameterization.
a)
b)
Figure 2.25. The Voce parameters 0 (a) and sat (b) as a function of temperature,
obtained in the IFEA of multiple experimental S-S curves.
2. Kocks-Mecking model for ITER-specification tungsten
70
2.5 Conclusion
In this chapter we have assessed a hardening law assuming dislocation-mediated
plasticity and accounting for the effect of temperature and strain rate on the
dislocation density evolution. The model has been parameterised for two grades
of tungsten: as-received IGP tungsten and recrystallized grade, relying on
experimental data obtained in tensile tests in a range of temperature and strain
rate. Numerical optimisation with the help of IFEA has been employed to fit the
model to multiple experimental curves at once and to obtain, thus, a bird-eye
view of the trends of temperature- and rate-sensitivity of the material.
Even though the parameterisation has been performed in the temperature range
of 250–600 °C, which represents the low temperature application window for
tungsten as divertor material in fusion reactor ITER, we assume that the
prediction of the model is valid at higher temperature, expected at the surface of
divertor, at least in the range where deformation by dislocation slip dominates.
The classical Kocks-Mecking approach is suitable for the characterisation of
plasticity of as-received tungsten. An extra term, linear with respect to applied
strain, has to be added in the evolution of the dislocation density of recrystallized
tungsten, to take account of what appears to be deformation stage IV, i.e. the
absence of saturation of dislocation density and true stress with increase of
strain.
Deformation-induced grain refinement by means of the build-up of dislocation
walls and cells as well as low-angle GBs has been confirmed by TEM
investigations and is assumed to induce stage IV hardening.
Finally, in order to proceed to investigation of mechanical state of tungsten
under ITER-relevant thermal conditions at the level of grains, the developed J2-
plasticity model needs to be implemented in the crystal plasticity framework,
which will be covered in the next chapter.
71
Chapter 3.
Development of a crystal plasticity model
accounting for backstresses Equation Cha pter 3 Section 3
3.1 Introduction
Thermal shock tests were identified as one of main qualification techniques for
the ITER project, where the plasma-facing components have to sustain a
predefined number of cycles, experiencing cyclic thermal strain and stress.
In order to investigate the conditions leading to intergranular crack formation in
tungsten exposed to thermal shocks, which mimic the plasma instabilities in a
fusion environment, we need to construct a plasticity model at the microscopic
level, where the anisotropy of individual grains causes microscopic
heterogeneity of stress and strain, in particular along GBs and near triple
junctions.
It is the constrained thermal expansion of the polycrystal which gives rise to
thermal stresses. Hence, the model has to face two main challenges: first, the
material strength continuously evolves following the oscillations of
temperature; second, the cyclic character of deformation can involve kinematic
hardening, i.e. the repeated elastic-plastic transients are expected to be
influenced by internal stresses due to the piling up of dislocations against
obstacles (such as GBs).
Predicting microscopic stresses based on crystal plasticity theory appears to be
a suitable choice. Such models are designed to take account of plastic anisotropy,
i.e. orientation of slip planes with respect to applied load. A temperature-
dependent resistance of crystal lattice to shear, which defines the material
strength, can be enforced to allow the simulation of mechanical response under
evolving temperature. Kinematic hardening can be organically incorporated in
the model, since it is attributed to a microscopic process occurring at the scale of
dislocation slip systems.
Crystal plasticity simulations presented in this work were all carried out using a
numerical tool previously developed at UCLouvain. In the context of the present
work, the crystal plasticity law has been improved in two regards. First, the
representation of thermally activated dislocation slip has been adapted from
room-temperature deformation of FCC metals [154] to high-temperature
deformation of BCC metals. Second, an original idea has been proposed and
3. Crystal plasticity model accounting for backstresses
72
tested in order to account, in a simplified way, for kinematic hardening resulting
from the accumulation of dislocation pile ups at GBs and their dissolution upon
load reversal.
In the present chapter, crystal plasticity relies on simplified “mean-field”
assumptions in order to relate the micro and macro scales. This means that strain
and stress are assumed uniform inside each grain. More advanced modelling of
the microscopic heterogeneity of mechanical fields is postponed to the next
chapter where crystal plasticity based finite element modelling (CPFEM) will
allow accounting also for intra-granular heterogeneity.
We have to acknowledge the scarcity of experimental data on kinematic
hardening in tungsten, due to high cost and technical difficulty associated with
fatigue tests, especially at high temperature. As shown in Figure 3.1 reproduced
from [59], there is a significant Bauschinger effect during low-cycle fatigue test
of forged tungsten at 480 °C.
Figure 3.1. Stress-strain loops obtained in low cycle fatigue tests of forged tungsten at 500 °C (other than IGP) [59] and the results of fitting of a J2 Armstrong-Frederick model of kinematic hardening.
The evolution of backstresses b , causing kinematic hardening, is usually
described by the Armstrong-Frederick family of models [155,156], which can be
written in the simplest one-dimensional case (tension in the direction 1) as
11 11
b bA B (3.1)
where A and B are the model constants and strain rate is denoted by .
3. Crystal plasticity model accounting for backstresses
73
To illustrate the applicability of the Armstrong-Frederick model to tungsten, we
coupled it with a J2 implementation of the hardening model presented in Chapter
2. As shown in Figure 3.1, the Bauschinger effect was reproduced in all three
experimental stress-strain loops when the saturating value of the backstress
(A/B) amounted to about 30% of the saturating value of the flow stress.
Implementation of the Armstrong-Frederick model in the crystal plasticity
framework is discussed further in the text.
The amplitude of kinematic hardening cannot be probed experimentally under
monotonic loads such as the uniaxial tensile tests reported in the previous
chapter. Hence, we do not know, at this stage, whether the phenomenon remains
important at higher temperatures and the present chapter explores several
hypothetical scenarios. Two limiting cases were parameterised for the
simulations, encompassing the absence of kinematic hardening and the absence
of isotropic hardening, respectively. An intermediate case was considered too, in
which the initial yield stress was partly due to kinematic hardening (i.e.
accumulation of dislocation pile-ups at GBs prior to macroscopic yield), and
isotropic hardening was responsible for the deformation strengthening.
3.2 Context
The thermal shock test is one of the qualification tests of plasma-facing
components accepted for the ITER project. Numerous tests have been carried out
on several baseline and advanced grades of tungsten, as discussed in Chapter 1.
In this chapter we aim to simulate experiments reported in [26], since they were
performed on IGP tungsten in a range of base temperature and thermal power
density, looking for the effect of the experimental conditions on the damage
formation in the material.
a) Transversal
b) Longitudinal
c) Recrystallized
Figure 3.2. Schematic representation of the three types of samples used in the thermal shock experiment [26].
Samples cut out of as-received IGP tungsten in two orientations (denoted as “T”
and “L” for “transversal” and “longitudinal” correspondingly) as well as out of
recrystallized tungsten (“R”) were tested. The top surface of blocks
12×12×5 mm3, shown schematically in Figure 3.2, was exposed to an electron
beam depositing thermal power of 190 MW m-
2 or 380 MW m-2 in pulses 1 ms
long. The temperature of the bottom surface was kept constant at 27 °C, 400 °C
or 1000 °C. 100 or 1000 thermal shocks were delivered, after which the state of
the surface indicated the material resistance to ELM-like thermal conditions.
3. Crystal plasticity model accounting for backstresses
74
Based on the experiments, it is possible to find out the damage threshold, which
is the value of thermal power density at a given pulse length, below which no
cracks appear on the surface after a given number of pulses. The damage
threshold decreases with the increase of base temperature, and the effect of
pulse frequency and the number of cycles alone might also play a role. Damage
threshold for the T orientation and recrystallized tungsten is much lower than
for the L orientation [71]. Not only IGP, but also double-forged tungsten in the T
orientation and recrystallized tungsten were found more susceptible to cracking
than the L orientation [157].
According to [157],
The general mechanisms of material degradation under electron
beam thermal shock loading are subdivided in two phases:
1) single pulse: formation of temperature gradients and related
thermal stresses, i.e. compressive stresses during heating due
to expansion of the volume below the loaded area constrained
by the ‘‘cold and rigid’’ bulk material and formation of tensile
stresses during cooling [158],
2) multiple pulses: thermal fatigue damage due to repetitive
loading.
Simulations dedicated to thermal shock tests are not reported frequently. Most
of them relied on simplified constitutive laws, such as ideally plastic [79,159], in
which, however, distributions of temperature, plastic strain and stress were
obtained. In an advanced technique “eXtended FEM” (XFEM) the authors could
calculate the J-integral for inserted pre-cracks in different positions and could
identify the damage threshold in terms of thermal power density, which agreed
roughly with experimental observations. Kinematic hardening was taken into
account in the work of Du [121], in a J2 analysis of thermal shock with the help of
a linear-plastic material law. The effect of coupled high-heat flux and thermal
shocks was investigated in a numerical analysis [83] using a J2 plasticity model
as well.
In this project we develop a crystal plasticity model, applicable to high-
temperature cyclic deformation of tungsten and incorporating the effect of
kinematic hardening to investigate the mechanical state and damage
accumulation in tungsten exposed to ELM-like thermal shocks.
3.3 Workflow of the suggested two-scale
simulation scheme
On the one hand, thermal shocks generate complex geometry-dependent stress
and strain states in the subsurface region of a sample, rapidly evolving in time.
In order to capture such a strain field, finite element modelling is required at the
3. Crystal plasticity model accounting for backstresses
75
macroscopic scale, i.e. at a scale much larger than characteristic microstructural
dimensions such as the grain size.
On the other hand, the CP approach is computationally demanding, and it is most
relevant at the scale of individual grains. Simulations involving large numbers of
grains have been reported too, but they require extra efforts and techniques to
reduce the computational time, such as homogenisation over a number of
neighbouring grains.
Balancing between feasible computational time and appropriate physical
description of the model, we have selected an original approach, combining the
macro- and micro-scale simulations.
The originality of the approach is to perform a thermomechanical simulation of
the ITER-relevant heat load at the macroscopic scale (a 12×12×5 mm3 tungsten
block, illustrated in Figure 3.11) under the assumption of isotropic J2 plasticity,
whereas crystal plasticity simulations are performed subsequently at the most
critical positions in the sample, using as input the strain and temperature history
which was predicted in the macroscopic simulation. The latter simulation uses
the macroscopic constitutive law, which was derived from tensile test results in
Chapter 2.
The macroscopic simulation was itself decoupled into a purely thermal
simulation followed by a mechanical simulation with a known temperature
history. The preliminary thermal simulation was performed to find the evolution
with time of the temperature field in the sample. It used the thermal properties
of tungsten available in literature [159]. Then, the obtained temperature field
served as input in a thermomechanical simulation on the same mesh, where the
bottom face was fixed and stresses emerged due to thermal expansion of the
heated area. The temperature- and rate-dependent constitutive law obtained for
the recrystallized tungsten in Chapter 2 was applied in the form of a user-defined
subroutine UHARD.
Finally, the strain path and the temperature profile were recorded at a point of
interest of the macroscopic specimen, and they were then applied at the
microscopic level to a polycrystal, whose mechanical response assumed that all
grains undergo uniform strain (Taylor mean-field crystal plasticity model).
3.4 Crystal plasticity framework
3.4.1 What is crystal plasticity theory?
The main mode of plastic deformation in polycrystalline materials is shear in
individual grains, which is carried out by dislocations gliding in slip systems.
Owing to the crystallographic anisotropy, the deformed grains change their
shape as well as the crystallographic orientation. Consequently, a
comprehensive theory of deformation of crystals must include the
crystallographic and anisotropic nature of dislocation glide, as well as take
3. Crystal plasticity model accounting for backstresses
76
account of the crystal orientation with respect to the external loading, or to the
neighbouring crystals [102].
Crystal plasticity is one of such models, stemming from the pioneering
contribution by Taylor [155]. The theory of CP is based on the assumption that
macroscopic plastic deformation is the superposition of crystalline slip in all
activated slip systems [160], whereas a slip system becomes active if the
resolved shear stress in it reaches a threshold value. The main conceptual
advantage of CP models is that they can combine a variety of mechanical effects,
which are direction-dependent owing to the underlying crystalline structure,
and can take account of dislocations as the main carriers of plastic deformation.
3.4.2 Traditional crystal plasticity for polycrystals
Prediction of deformation in single crystals is straightforward with the above-
mentioned assumption. Transitioning to polycrystals can be carried out by
considering that single crystal plasticity is valid within each grain, and by making
assumptions about how macroscopic constraints apply to individual grains in
the polycrystal [161]. For many years, this micro-to-macro transition has relied
on simplified assumptions after Sachs or Taylor, according to which all grains
undergo correspondingly either the same stress, or the same deformation as the
whole macroscopic polycrystal, hence the name “mean field” crystal plasticity.
These simplifications make it impossible to ensure strain compatibility and
stress equilibrium at GBs simultaneously. Grains in real deformed polycrystals
acquire non-uniform stress and strain due to the interaction with neighbours.
Such heterogeneities appear in the form of grain-scale orientation gradients as
well as a subdivision of the grain into volumes undergoing distinct deformation
[161].
On top of assuming uniform distribution of strain, stress and other quantities
within individual grains, the standard CP disregards potential effects of grain
shape, relative size and arrangement, thus the deformation of a given grain is
defined solely by its initial orientation. These simplifications can partly explain
the discrepancies between experimental results and the predictions of
simulations with Taylor-type models [161].
Nevertheless, the simulations of the present chapter assume a uniform
deformation of all grains, which has the effect of maximizing the heterogeneity
of stress resulting from the crystallites plastic anisotropy. Even though such
assumptions are less realistic than the CPFEM presented in the next chapter, they
rely on the same mathematical modelling of dislocation slip and allow us to
capture the main macroscopic trends.
3. Crystal plasticity model accounting for backstresses
77
3.4.3 Mathematical formulation of the grain-level plasticity law
This section was written with the help of my supervisor.
One originality of the model developed at UCLouvain is to rely on a simplified
treatment of elasticity in order to simplify the mathematical representation of
finite strains and to allow an efficient and fully implicit time integration of crystal
plasticity equations. The consistent tangent operator allows rapid convergence
of iterative solution schemes, for instance when the code serves as a user-defined
material law (UMAT) in the Abaqus finite element code.
As commonly assumed in crystal plasticity theories, the deformation gradient
tensor is multiplicatively decomposed: el p F R F F . In this expression, elF
and pF correspond to the elastic and plastic parts of the deformation, whereas
R is an orthogonal matrix representing the rotation of the crystal lattice from
its initial to its final orientation. The total deformation gradient F maps the
initial (undeformed) configuration onto the current (deformed) configuration.
The multiplicative decomposition of F defines two fictitious, intermediary
configurations [162]. The first one is obtained by mapping the initial
configuration using only pF , which amounts to consider that the material
deforms solely due to dislocation glide. The mapping el pF F defining the second
intermediary configuration includes also the elastic deformation of the lattice.
The latter fictitious configuration is sometimes called “unrotated configuration”
because it lacks only the crystal rotation. In metals, since elastic strains are small
as compared to plastic strains, the two intermediary configurations are very
close to one another.
Besides, when temperature fluctuates, the thermal strain is accounted for before
proceeding to the integration of crystal plasticity equations. The multiplicative
decomposition of the deformation gradient includes a supplementary isotropic
expansion, th T F I , where the value of thermal expansion coefficient
= 5.0·10-6 K-1 was taken as an approximate average of the temperature-
dependent value from [159] in the studied range of temperature.
Computing the velocity gradient tensor L requires time derivatives, which are
denoted with a dot:
1 11
1
T el el T el p p el T
L v F F
R R R F F R R F F F F R (3.2)
This expression is simplified by accounting for the fact that elastic strains are
infinitesimal so that el elF I ε with el 1ε , leading to:
1
1
T el p p T
T el p p T
p
( )
L R R R ε F F R
R R R ε F F R
LΩ
(3.3)
3. Crystal plasticity model accounting for backstresses
78
We have adjoined a tilde on top of three (second-order) tensors to highlight the
fact that they apply to the “unrotated configuration” (the second fictitious
intermediary configuration). In the latter configuration, the velocity gradient is
additively decomposed into a skew symmetric tensor Ω called the lattice spin
(i.e. rate of crystal rotation), a symmetric elastic strain rate elε and a plastic
velocity gradient p
L . These three tensors are most conveniently expressed in a
coordinate frame that rotates with the crystal frame. We will hence call them “co-
rotational” tensors.
The anisotropic elastic stiffness operator C then allows computing the co-
rotational Cauchy stress, el:σ C ε , whereas the plastic velocity gradient is equal
to:
p
sym skw
L b n M M M (3.4)
Here is the dislocation slip rate along the th slip system which is
characterized by the unit vectors b , parallel to the Burgers vector, and
n ,
normal to the slip plane. The Schmid tensor
M , dyadic product of the two
vectors, is subdivided into a symmetric sym
M and a skew-symmetric skw
M part.
The material response is computed incrementally by time integration under a
prescribed velocity gradient L D W where D is a symmetric strain rate
tensor and the skew-symmetric W tensor involves both the lattice spin and the
plastic spin. A set of nine equations is formed by separating symmetric and skew-
symmetric tensors:
Tsym
Tskw
:
R
σ
Ω
C R D R M
R W M
(3.5)
The dislocation slip rates are computed using a thermally activated viscoplastic
law which is discussed in the next section. Supplementary to σ , which is the
average microscopic stress, mobile dislocations are subjected to a backstress bσ
due to the pile up of other dislocation loops already immobilized at the GBs. The
backstress evolves according to a saturating Armstrong-Frederick law [155]:
symb b whereA B
Mσ σ (3.6)
A and B are material parameters. In case of monotonic loading, the tensor bσ
progressively aligns with the plastic strain rate (symmetric part of p
L ) and it
saturates at an amplitude scaling with /A B . The parameter A defines the initial
rate of increase of the backstress. Note that the model treats the backstresses
3. Crystal plasticity model accounting for backstresses
79
phenomenologically and does not consider dislocation pile-ups as objects. The
pile-ups are assumed not to contribute to the total dislocation density variable
. In this way the model is seen more versatile, since not only dislocation pile-
ups can generate backstresses in materials. Other sources include variation of
strength between material’s constituents, as discussed in Section 1.3.2.3.
Time integration of the material law is fully implicit and it is solved incrementally
following a Newton-Raphson scheme. As the increments of dislocation slip
t depend on the stress, there remain 14 independent unknowns in the
set of non-linear equations: the six components of the co-rotational stress
increment σ , the five independent components of the increment of backstress
bσ , which is deviatoric, and the three independent components of the skew-
symmetric tensor t ΩΩ representing the increment of lattice rotation:
sym
skw
symb b
:
/ (1 )
|
|
t t
t
t
t
t
t
A B B
σ C D M
Ω W M
σ M σ
(3.7)
The fully implicit time integration is simplified by accounting for the fact that
each time increment involves a sufficiently small increment of lattice rotation to
ensure that:
T
T
|
| | |
| | | |t t t t t t
t t t t
t
D R D R
R D R Ω D D Ω
D
(3.8)
|t tW is computed in the same way, thus depending only on the lattice rotation
at the beginning of the time step T |tR and on the increment of rotation Ω
which is determined in the Newton-Raphson solution.
The model now needs to be completed by expressions prescribing shear rate and
critical resolved shear stress as functions of state variables. The shear rate is
usually formulated as a function of the resolved shear stress, , and the critical
resolved shear stress,
, cf (3.9)
Due to work hardening and also to strain rate sensitivity, the critical resolved
shear stress evolves as a function of the total shear, , and the shear rate, .
,c g (3.10)
3. Crystal plasticity model accounting for backstresses
80
Thus, a system of equations with tightly interrelated variables is obtained, which
has to be solved for every iteration of the solution of the non-linear equation set
(3.7). This means that two Newton-Raphson schemes are imbedded.
In the present research, a thermally-activated law for dislocation slip [154] was
adapted in order to include the kinematic hardening mechanism as well as the
athermal stress characteristic of BCC metals at high temperature. To start, jumps
of dislocations over the obstacles are predicted using a usual equation of the
Arrhenius-type [163,164]:
0 exp 1 exp b c
B B
G ab
k T k T
(3.11)
Here kB, T, 0 and a are the Boltzmann constant, the temperature, the reference
strain rate and the area swept out for the reverse jump. Thus, the product ab
corresponds to the activation volume.
Here we had to account for the presence of athermal stress in BCC metals c , and
the CRSS at 0 K is denoted as ˆc , being the maximal value of thermal stress.
The athermal stress evolves as a function of dislocation density
0c y disb h (3.12)
where 0y may be chosen to depend on grain size.
G is the free enthalpy allowing a mobile dislocation to overcome short-range
obstacles [165], where 0F , p=0.5 and q=1.5 [144] are constants:
0 1ˆ
qp
b cG F
(3.13)
Thermally activated plasticity is properly modelled as long as
ˆc b c
. For lower stresses the response is purely elastic. For larger
effective stresses (which might appear at high temperatures), the plastic strain
rate is limited by viscous drag of dislocations, rather than by their mutual
pinning
0
ˆ
b c
(3.14)
The dislocation density is assumed to evolve according to the Kocks-Mecking
model. The product 2 plays the role of
2k used in Equation (2.4), where 2 is
constant and the temperature- and rate-effects are accounted by the factor
1 2k (3.15)
3. Crystal plasticity model accounting for backstresses
81
1/1/
0
0
1 ln
pq
Bk T
F
(3.16)
This factor also affects the value of B in equation (3.6) in order to enforce the
congruence between isotropic and kinematic hardening evolution:
0B B (3.17)
where 0B is a constant determined by fitting. In this way, similar patterns of
evolution of initial yield stress, initial work hardening and the saturating stress
on temperature and strain rate in all three materials (purely isotropic, purely
kinematic and mixed) are fulfilled, and the stress-strain curves in all three cases
of hardening can match each other in the whole investigated range of
temperature and strain rate.
In the first publication [120], a different formulation of viscoplasticity was used
to model recrystallized tungsten. The old formulation is not well adapted to very
high temperatures but provides similar predictions to those obtained with the
new formulation in the range of temperatures that was considered then. Slip
rates were defined following Rice, Hutchinson and Peirce [75] applicable not
only for FCC, but for BCC metals at high temperature [115]. Equation (3.9) took
the form of
1
0 sgnm
c
(3.18)
where the strain rate sensitivity exponent m was set equal to 0.02.
Expression for slip resistance was obtained from equations (2.7) and (2.10) with
the help of the Taylor factor, assumed to be equal to that in as-received tungsten,
namely 2.5. Essentially, the equation was rewritten in terms of critical resolved
shear stress c vs. accumulated shear strain in a slip system, preserving the
linear term with respect to shear 2
IVH
M
0
2
0
expsat sat IV
c
H
M M M M M
(3.19)
The equations were embedded in the user-defined subroutine UMAT containing
the algorithm of the crystal plasticity model.
3.5 Identification of material parameters
Before performing meaningful simulations e.g. of tungsten exposed to thermal
shocks, the constitutive law for the CP model had to be parameterized. As it is
impossible to derive exact parameters of kinematic hardening from tensile tests
3. Crystal plasticity model accounting for backstresses
82
alone, we had a certain freedom in the choice of parameters: different ratios
between kinematic and isotropic hardening lead to the same experimental
stress-strain curve. Hence, we have considered three cases of hardening: purely
isotropic, purely kinematic and mixed.
The parameters for the three hypothetical materials had to be fitted so as to
reproduce experimental tensile curves of as-received IGP tungsten (after
extraction of true stress as discussed in Chapter 2). The model parameterization
was performed with the help of an iterative optimization algorithm, similar to
the one discussed in Chapter 2. As long as this approach involves many iterations,
it is more efficient to rely on the less time-consuming crystal plasticity
implementation — the mean-field Taylor-type crystal plasticity, rather than
CPFEM.
The model polycrystal was composed of 100 randomly-oriented grains, enough
to form a representative volume element, whose plasticity was controlled by the
developed CP model. Every iteration of the optimisation algorithm involved a
group of N = 15 simulations (corresponding to the 15 tensile experiments
performed at different temperature and strain rate). They were launched for a
given set of model parameters (starting off from an initial guess). The objective
function was set as the total sum of squares of differences between the
simulated ,i n
s and the experimental ,i n
e true stress values at three
reference points, as illustrated in Figure 3.3, over all the 15 experimental stress-
strain curves,
3
2, ,
1 1
Ni n i n
e s
n i
(3.20)
where 𝑛 = 1–15 denotes the ID of the simulation in the group and 𝑖 = 1–3
corresponds to the selected reference points (0.02%, 0.2% and 0.5% of plastic
strain). Such a narrow range of strain for fitting was chosen in order to better
represent the very beginning of the deformation curve, as long as the thermal
strain achieved in a single cycle was not expected to exceed 1% [166]. The
hardening rate at 1% of plastic strain was also monitored to match the
experimental value. Different parameter sets were probed at every iteration,
until the objective function minimum was found, denoting the best match with
the experimental points. The known material parameters were fixed: the Young
modulus E = 388 GPa, Poisson ratio ν = 0.28, initial dislocation density
0 = 4.5·1012 m-2 [32] and Burgers vector b = 0.274 nm.
3. Crystal plasticity model accounting for backstresses
83
Figure 3.3. On the evaluation of the objective function. The squares of differences between experimental and simulated values of stress are summed over three points per curve and then are summed over all 15 stress-strain curves.
First, the parameterization of the purely isotropic hardening case was
performed. In order to parameterise the other two hypothetical materials, some
model parameters were manually adjusted, as summarized below:
Purely kinematic hardening
The dislocation strength hdis was reduced to suppress isotropic hardening, 0y
was increased to compensate the suppressed contribution to the CRSS from the
initial dislocation density, the rest of the parameters were left unchanged. The
objective function was minimized by searching for A and B.
Mixed case
was reduced to provide room for kinematic hardening in the very beginning
of plastic deformation, dislocation strength hdis was assigned the same value as
in the purely isotropic hardening case to provide the same work hardening rate
as in the isotropic case. The values of A and B were found using the iterative
algorithm.
Figure 3.4 shows how the three investigated hypothetical hardening cases were
constructed, illustrating the assumed decomposition of an experimental stress-
strain curve. The dotted lines in Figure 3.4 indicate the macroscopic stress, which
arises due to 0 only. When the resolved shear stress in a slip system exceeds
this level, the deformation is considered plastic and the hardening mechanisms
are activated. The dashed lines indicate the sum of 0 and the isotropic
hardening contribution, which increases with plastic strain due to the increase
of dislocation density. The solid lines correspond to the sum of all the
contributions, replicating the experimental stress-strain curve.
3. Crystal plasticity model accounting for backstresses
84
Figure 3.4. Illustration of construction of the three cases of hardening.
Thus, the difference between the dashed and the solid lines of the same colour
for the mixed case is due to kinematic hardening and is described by the
Armstrong-Frederick law. It means that a part of the initial yield stress is caused
by the accumulation of dislocation pile-ups at GBs prior to macroscopic yield,
while for the pure kinematic case the accumulation of pile-ups commences
merely after reaching the initial yield stress, is extended in time and develops
with much lower rate than in the mixed case.
The numerical stability of the developed constitutive law had to be ensured in
the ranges of temperature and strain rate that are relevant for the thermal shock
experiments. Following [26], the upper boundary for temperature can be
estimated as 1700 °C, and the largest strain rate is expected to reach order of
magnitude of several s-1 [1]. Besides, the selected equations require a limit on the
minimal allowed strain rate, chosen in this work quite arbitrarily to be 10-6 s-1.
0.00 0.02 0.04
200
300
400
500
600
Kinematic
hardening
Work hardening
due to dislocations
Kinematic
hardening
Tru
e s
tre
ss [M
Pa
]
Flow stress
Base stress
a) Isotropic
Initial dislocation
hardening
Work hardening
due to dislocations
0.00 0.02 0.04
True strain
Flow stress
Dislocation
contribution
Base stress
b) Mixed
0.00 0.02 0.04
Flow stress
Base stress
c) Kinematic
3. Crystal plasticity model accounting for backstresses
85
3.6 Results
3.6.1 Identification of model parameters based on uniaxial tensile
tests
3.6.1.1 As-received tungsten
Applying the fitting algorithm outlined above, we have parameterized the crystal
plasticity model for as-received IGP tungsten in the three considered cases of
hardening: purely isotropic, purely kinematic and mixed. Some of the
parameters were set to be independent of the hardening type, because they
describe the rate of dislocation accumulation and the activation energy. Such
parameters are listed in Table 3.1. The other parameters, which were varied
manually or fitted, are grouped in Table 3.2. Note that, since the parameters of
the Armstrong-Frederick model are responsible for hardening above the dotted
lines in Figure 3.4, the value of A is much higher for the mixed hardening case.
Table 3.1. The CP model parameters independent of hardening type for as-received tungsten.
k1, m-1 2 F0 a
0 , s-1
1.16·108 10.7 0.53𝜇𝑏3 100𝑏2 6.64·104
Table 3.2. The CP model parameters for the isotropic, kinematic and mixed hardening cases of as-received tungsten.
Hardening A , GPa B 0y , MPa , MPa hdis
Isotropic - - 17.86 260.7 0.129
Kinematic 1.1 5.36 28.57 260.7 0.013
Mixed 3400 750 17.86 167.9 0.129
Figure 3.5 shows the corresponding fitted true S-S curves for temperature and
strain rate used in tensile tests (300 °C and 600 °C and 6·10-4 s-1), strain rate
expected when tungsten is exposed to thermal shocks (6 s-1) as well as for the
model applicability limit, 1700 °C and 10-6 s-1. The curves obtained for the three
hardening modes coincide well with experiments at all combinations of test
conditions. This confirms that monotonic tensile tests alone do not suffice in
order to probe the amplitude of backstresses.
3. Crystal plasticity model accounting for backstresses
86
Figure 3.5. True deformation curves obtained in simulations of tensile test with the crystal plasticity model and the best parameter sets for three hardening cases.
The evolution of dislocation density is shown in Figure 3.6 for the same
combinations of test conditions. As expected, it is identical for the three
considered hardening modes, whereas it depends on temperature and strain
rate. Note that the model does not treat dislocation pile-ups as separate objects
and does not take into account their density. Besides, this figure illustrates the
existence of the model applicability domain: at a certain combination of
temperature and strain rate (1700 °C and 10-6 s-1 in this case), the derivative of
dislocation density w.r.t. strain diminishes, and becomes negative outside the
domain, provoking numerical instability of simulations. The applicability domain
was defined beforehand, anticipating the conditions in future simulations.
3. Crystal plasticity model accounting for backstresses
87
Figure 3.6. Evolution of dislocation density in the simulated polycrystal of as-received tungsten with the best parameter sets for three hardening cases.
3.6.1.2 Recrystallized tungsten
Simulations of uniaxial tension of recrystallized tungsten were also performed
to validate the direct use of parameters obtained in the macroscopic model
fitting. The obtained stress-strain curves are compared with their experimental
counterparts in Figure 3.7. The rate sensitivity of the simulated material
decreases with the increase of temperature, as the contribution of the thermal
stress component decreases.
Figure 3.8 highlights the applicability domain of the model, showing true stress-
strain curves obtained in uniaxial tension simulations at high temperature and
at the limiting values of strain rate as discussed above.
3. Crystal plasticity model accounting for backstresses
88
Figure 3.7. True stress-strain curves obtained in uniaxial tension with the CP model of recrystallized tungsten (dashed) superimposed on the experimental curves (solid).
Figure 3.8. True stress-strain curves at high temperature and the limiting values of strain rate, demonstrating the applicability domain of the model of deformation of recrystallized tungsten.
3. Crystal plasticity model accounting for backstresses
89
A good match between the simulated and experimental mechanical response to
uniaxial tension indicates the possibility to use the developed microscopic
constitutive law for simulations of a complex load, such as the thermal strain and
stress caused by the thermal shocks.
3.6.2 Isothermal mechanical cycles
3.6.2.1 As-received tungsten
Figure 3.9. Stress-strain loops obtained in simulations of mechanical isothermal cyclic loading of as-received tungsten.
Before using the developed model in simulations of thermal fatigue, it was first
tested in isothermal cyclic loading, i.e. tension-compression. A series of
simulations was performed in a range of temperature, covering the whole
applicability domain, and strain rate 6·10-4 s-1. The obtained stress-strain loops
are summarized in Figure 3.9 for the three studied hardening modes. Slow
gradual increase of stress amplitude is seen for the isotropic hardening case,
because in this model the multiplication of dislocations takes place in both direct
and reverse loading. The loops corresponding to kinematic hardening are stable
because the backstresses accumulated during direct loading diminish and
change sign during reverse loading. A small Bauschinger effect is visible even in
the purely isotropic hardening case, originating from grain-to-grain variations of
3. Crystal plasticity model accounting for backstresses
90
strength, caused by plastic anisotropy. Deformation of polycrystals is similar to
that of composites, as discussed in Subsection 1.3.2.2.
3.6.2.2 Recrystallized tungsten
Simulations of isothermal mechanical cyclic loading, i.e. tension-compression
cycles, of recrystallized tungsten revealed a more rapid increase of stress
amplitude than in as-received tungsten, as compared in Figure 3.10. It is caused
by two reasons: the large work hardening capacity of recrystallized tungsten and
the presence of the linear term in the equation for slip resistance. Note that the
rate of increase of stress diminishes, as the temperature approaches the model
applicability limit of 1700 °C.
Figure 3.10. Stress-strain loops obtained in simulations of mechanical isothermal cyclic loading of recrystallized and as-received tungsten.
3.6.3 Macroscopic thermal shock simulation
The simulations replicated the experiment carried out at Forschungszentrum
Jülich in the JUDITH1 facility, in which box-shaped W samples were subjected to
ELM-like heat load induced by an electron beam [26]. A thermal power density
of 190 MW m-
2 or 380 MW m-2 was applied at the centre of the top surface of the
W block 12×12×5 mm3 by an electron pulse, 1 ms long, while the bottom surface
was kept at a constant base temperature 27 °C, 400 °C or 1000 °C.
3. Crystal plasticity model accounting for backstresses
91
Figure 3.11 depicts the FE mesh used in the macroscopic simulation and the
temperature field at the end of exposure to the heat flux 190 MW m-2, showing
the heated central area (4×4 mm2). Deformation of the sample due to high heat
load has been magnified by a factor of 10 for illustrative purpose. The yellow dot
in the centre indicates the element for which the strain state was recorded. High
stress concentration and initiation of intergranular cracks are expected in this
region.
Figure 3.11. FE mesh of the sample studied in JUDITH1 facility for a macroscopic thermo-mechanical simulation. The colour indicates temperature field at the end of heat flux exposure, with the blue colour corresponding to the base temperature, 400 °C, and the red - to the maximal attained temperature ~750 °C.
Figure 3.12. Evolution of temperature and the von Mises strain in the centre of the heated area exposed to an ELM-like thermal shock of 190 MW m-2.
For the microscopic simulations we need to know the evolution of temperature
at a selected point, as well as stress or strain state. Figure 3.12 shows an example
of the evolution of the temperature and of the von Mises strain with time in the
selected element, where one can see a rapid increase of both values during the
3. Crystal plasticity model accounting for backstresses
92
heating period (the first millisecond). Upon cooling down, the temperature fades
out significantly. However, von Mises strain decreases only slightly. That is
caused by the irreversible nature of plastic strain and its ability to accumulate
after a number of heat load cycles, provoking further build-up of stress and
consequent crack initiation. The most significant drop of temperature is
observed in the first millisecond after switching off the heating (i.e. between time
marks 1–2 ms).
Components of stress tensor were measured in the centre of the heated area (the
yellow dot in Figure 3.11). The shear components turned out to be zero while the
normal components are shown in Figure 3.13 as functions of time (a) and
temperature (b). Only two non-zero components are present, identical thanks to
symmetry of the problem: S11 and S22, which are normal stresses along the
heated surface, revealing the plane stress state in that location. The most
significant excursion of the in-plane stress components is observed during
heating and the first millisecond of cooling. These findings allow us to apply
simplified boundary conditions of plane stress in the microscopic simulations,
instead of following the exact recorded strain path. This approach can help
identify main trends in the mechanical response of material under thermal
shocks and significantly reduce the required computational time.
The value of normal stress in the subsurface region is close to residual stresses
in tungsten exposed to ELM-like thermal shocks measured with the help of X-ray
diffraction (XRD) [72,167]. The neutron diffraction method has been used for
detection of internal stresses in fabricated monoblocks [168] and can be applied
to measure residual stress in tungsten after thermal shocks.
a) b)
Figure 3.13. Normal stress components in the centre of the sample exposed to 380 MW m-2 as a function of (a) time and (b) temperature. The only non-zero components are S11 and S22, indicating a plane-stress state.
3. Crystal plasticity model accounting for backstresses
93
3.6.4 Microscopic thermal shock simulation
The developed CP model was used in mean-field simulations of the mechanical
response of a tungsten polycrystal to ELM-like thermal shocks, defined by
triangular waveform excursions of temperature between the base and the peak
values under the conditions of plane stress. 1000 or 100 thermal pulses were
simulated for every combination of base temperature and power density for both
as-received and recrystallized tungsten, and the values of thermally-induced in-
plane stress and out-of-plane strain were recorded.
The simulation box represented a polycrystal composed of 100 randomly
oriented grains, which is schematically shown in Figure 3.14. The thermal
expansion (shown by the orange colour) was allowed only in the direction Z,
whereas the other two directions were constrained.
Figure 3.14. Schematic view of the simulation box in the initial and deformed state. The thermal strain is denoted as .
3.6.4.1 As-received tungsten
Thermally-induced stress and strain recorded in simulations of thermal shocks
in as-received tungsten with isotropic hardening are shown in Figure 3.15 (other
material laws will be reviewed in Section Discussion). Due to the cyclic nature of
deformation, the plots have the form of loops.
Application of the lower power density, 190 MW m-2, leads mostly to cyclic
elastic deformation in as-received tungsten, which begins with 1·10-3–2·10-3 of
plastic strain, thus the material is in the state of elastic shakedown. That explains
the absence of cracks on its surface in experiments [26].
Significant plastic deformation and non-degenerate stress-strain loops are
observed in the simulations of higher heat loads (380 MW m-2). The average
strain (the loop centre) and the strain amplitude have increased by the factor of
2–3 as compared to the lower power density. The shape of the loops does not
change significantly from cycle to cycle, due to quite low increment of work
hardening per cycle and due to kinematic hardening originated from the stress
3. Crystal plasticity model accounting for backstresses
94
heterogeneity in neighbouring grains. Macroscopically observed yield stress
corresponds to yielding in the softest grain, whereas all the grains reach the
plastic plateau soon after that. It indicates that the state of elastic shakedown in
as-received tungsten might not be reached even after a large number of cycles
and the material is under conditions of low cycle thermal fatigue.
Figure 3.15. The mechanical response of as-received tungsten (isotropic hardening only) to thermal shocks of different power density in terms of the in-plane stress vs. the out-of-plane strain.
3.6.4.2 Recrystallized tungsten
The evolution of stress-strain loops recorded in simulations of thermal shocks in
recrystallized tungsten is shown in Figure 3.16 for the material with isotropic
hardening only. The loops progressively change their dimensions from one cycle
to another along with material hardening.
The first cycle begins with accumulation of plastic deformation in compression
during heating: 0.2–0.3% and ~0.8% at low and high power density
correspondingly. Tungsten exposed to low power density 190 MW m-2 at base
temperature 27 °C experiences elastic shakedown, i.e. the absence of plastic
deformation in cyclic loading, from the second cycle, as its response has not
changed from cycle 1 to cycle 10. This observation is in line with the experiment
[26] where no damage and no surface modification was observed in
3. Crystal plasticity model accounting for backstresses
95
recrystallized tungsten at room base temperature at low power density. The
contribution of plastic strain decreases with the increase of stress amplitude.
And, since the total strain is fixed, the loops degenerate and elastic shakedown is
eventually reached by the 1000th cycle in tungsten exposed to 190 MW m-2 at
400 °C and 380 MW m-2 at 27 °C.
Figure 3.16. The mechanical response of recrystallized tungsten to thermal shocks of different power density in terms of the in-plane stress vs. the out-of-plane strain.
The loops are asymmetric due to the difference between yield stress at maximum
and minimum temperature during cyclic heating, which is especially pronounced
at lower base temperature. It means that as the sample is cooled down, its
strength continuously increases, resulting in a higher recorded stress. As the
base temperature increases, the stress amplitude decreases; since the material
loses its strength. In contrast with the as-received tungsten, low power density
causes plastic deformation in recrystallized tungsten at high base temperature
due to its reduced strength.
The maximal strain does not exceed 0.5% and 1% at low and high power density
correspondingly similar to the as-received tungsten, but the stress amplitudes
differs significantly in the two states of tungsten. Plastic strain accumulation is
accompanied by the increase of stress amplitude and ratcheting, i.e. the increase
3. Crystal plasticity model accounting for backstresses
96
of the mean plastic strain with the number of pulses. It might be caused by low
initial yield stress, high work-hardening capacity and the linear term in the
constitutive law for recrystallized tungsten. The latter might still be excessive, as
the amplitude of stress reaches unreasonable values, and the range of strain in
which its presence is physically-sound has still to be checked experimentally by
applying large plastic deformation to tungsten or by cyclic mechanical tests.
Another important point is to introduce a fracture criterion which would limit
the number of cycles sustained by tungsten, probably way before reaching the
elastic shakedown.
3.7 Discussion
3.7.1 Effect of kinematic hardening
Figure 3.17. Stress-strain loops recorded in the as-received tungsten for the three considered material laws.
Stress-strain loops for all hardening cases of as-received tungsten are grouped
in Figure 3.17, and the tensile stress amplitude (measured at the end of every
3. Crystal plasticity model accounting for backstresses
97
pulse) is plotted as a function of cycle number in Figure 3.18. The stress-strain
loops obtained in different hardening cases generally look similar, but a more
pronounced Bauschinger effect for the mixed hardening, and a slower increase
of stress amplitude for the pure kinematic hardening are observed.
Figure 3.18 reveals that the stress amplitude decreases with the increase of base
temperature for the three cases, showing the tendency of the material to sustain
a larger number of thermal pulses at high temperature, or to reduce the density
of surface cracks after a given number of pulses, which agrees with the
experiments.
Figure 3.18. Evolution of the in-plane tensile stress amplitude obtained in the as-received tungsten for the three considered material laws.
The presence of isotropic hardening, i.e. higher dislocation strength and their
continuous multiplication, leads to a fast expansion of the yield surface,
increasing the maximal tensile stress. The difference between the isotropic and
kinematic cases is negligible at low power density 190 MW m-2, as deformation
is mostly elastic and the rate of accumulation of dislocation density is low.
On the other hand, at high power density, the application of purely kinematic
hardening model returns the lowest macroscopic stress amplitude among the
3. Crystal plasticity model accounting for backstresses
98
explored cases. Indeed, kinematic hardening corresponds to the reversal of
microscopic internal stresses in every cycle, whereas isotropic hardening is
associated with continuous dislocation multiplication.
We should, however, not conclude from the observation of stress amplitude
evolution that the existence of kinematic hardening has a positive impact on the
fatigue resistance of tungsten.
When dealing with kinematic hardening, it is important to keep in mind that the
backstress amplitude actually measures the heterogeneity of stresses witnessed,
respectively, by the mobile dislocations accommodating plasticity and by
dislocations already piled up against GBs. It is a repulsive stress which tends to
separate the two types of dislocations. During monotonic loading, mobile
dislocations progress against the backstress (“they have wind in the face”) since
the backstress makes it more difficult to reach the GBs and extend the already
existing backstresses. When the macroscopic load is reversed, it adds up to the
pre-existing backstress. Mobile dislocations now move in the opposite direction
(“with the wind in the back”). This causes early plasticity (the Bauschinger effect)
while the dislocation pile-ups are progressively dissolved.
In GB regions, the effect of the backstress is to push immobilized dislocations
against the GB (making the pile-up denser). Hence, the stress amplitude in the
vicinity of GBs, i.e. where damage is expected to initiate, is larger than the stress
measured macroscopically in experiments. When assessing the strength of a
material, kinematic hardening is likely to favour the onset of damage at GBs.
Here we do not consider the possibility of dynamic recrystallization in hot
tungsten, which can reduce its strength and the rate of accumulation of
backstresses. It would affect both hypothetical materials, with isotropic and
kinematic hardening, by increasing the grain size and reducing dislocation
density. The proposed model assumes that the grain size remains constant, and
the dislocation density changes due to deformation only. The main application of
the model might be to analyse stress state at a small depth of a tungsten PFC,
where temperature is not sufficient for recrystallization, but periodic stresses,
transmitted from the surface, are significant to cause formation of fatigue cracks.
3.7.2 Note on the mixed hardening case
The results of simulations of the mixed hardening case (the presence of both
isotropic and kinematic hardening) are different from the pure cases: a rapid
accumulation of internal stresses is observed in the first few cycles, especially at
low power density. It contradicts the intuitive expectations of the mixed case
being somewhere between the pure cases. However, it might indeed represent
the reality. Experimental validation would be necessary to find out the actual
response of material to cyclic loading, by means of instrumented strain-
controlled fatigue tests and thermomechanical fatigue tests.
3. Crystal plasticity model accounting for backstresses
99
The first conclusion that could have been made is that the synergy between
isotropic and kinematic hardening in the material would increase the risk of
crack formation during thermal shocks compared to material exhibiting pure
isotropic hardening. Even though piling up of dislocations at GBs in material with
kinematic hardening is known to increase stress concentration, and provoke
damage, the simulation observations should be treated carefully due to the
following point.
Deformation in the present model is considered plastic (and, consequently,
hardening mechanisms are activated), when resolved shear stress exceeds the
value of 0 (the dotted lines in Figure 3.4). In the purely kinematic case
0
corresponded to the CRSS, but in the mixed case 0 was purposely lowered. As
long as a fraction of the CRSS is due to the Hall-Petch effect [115], related to the
build-up of dislocation pile-ups at GBs, the kinematic hardening mechanism (the
Armstrong-Frederick model) was set to define this portion of CRSS in the mixed
case (whereas in the purely isotropic case the contribution of the Hall-Petch
effect was taken into account in 0 ).
From the physical point of view, the mixed case interprets deformation of
material as if the multiplication of mobile dislocations commenced
simultaneously with the initial formation of dislocation pile-ups prior to their
saturation and consequent macroscopic flow. Hence, in the mixed case, a larger
portion of deformation loops is considered plastic, compared to the pure
hardening cases, and, consequently, a higher increment of dislocation density
and stress is achieved in every thermal cycle.
An alternative approach would be to assume that deformation switches from
elastic to plastic when stress exceeds the initial CRSS (at zero strain), which in
the mixed case is the sum of 0 and the saturated backstress. It would mean that
at the onset of plastic deformation dislocations start gliding and form pile-ups,
but do not multiply until the backstress saturates. Up to our best knowledge
there is no clear information in literature whether the multiplication of mobile
dislocations takes place simultaneously with the initial accumulation of
dislocation pile-ups prior to macroscopic yield, and thus we test only one of the
two possibilities in the present work.
Moreover, the present formulation of the mixed hardening will be beneficial in
the next chapter, since the presence of dislocation pile-ups in material is known
to aggravate stress concentration at GBs, and to promote damage. Thus, what we
called “mixed hardening” here should be more appropriate for the description of
kinematic hardening, than what we denoted as “pure kinematic hardening”. For
this reason, we will investigate the effect of kinematic hardening on the
mechanical response of tungsten to thermal shocks, considering two material
laws — isotropic hardening and mixed hardening in Chapter 4.
3. Crystal plasticity model accounting for backstresses
100
3.8 Conclusion
An existing CP model of deformation of polycrystals has been enhanced i) to
correctly capture the existence of athermal stress in BCC metals, and ii) to take
into account backstresses to properly work with kinematic hardening, which is
necessary for simulations of cyclic loading.
The model can be used in two modes — standalone and coupled with the Abaqus
finite element solver (CPFEM mode). The former has been used in the present
chapter, while the latter will be considered in Chapter 4, to perform a thorough
investigation of damage accumulation during loading at the microscopic level.
Three hypothetical material laws with different share of kinematic hardening
have been parameterized to represent mechanical properties of ITER-
specification tungsten. On top of that, recrystallized tungsten was also
parameterized, considering the presence of isotropic hardening only.
The main purpose of this chapter was to check the applicability of the model to
simulation of cyclic loading of tungsten with different modes of hardening, which
was proven in analysis of both isothermal mechanical loading and thermal shock
loads mimicking the fusion environment. Qualitative agreement with the
thermal shock experiments has been obtained, linking the stress state during
cyclic loading and the damage of the exposed surface.
In addition, our analysis shows that the presence of the initial ELM-induced
plastic deformation (attained in the first cycle) does not allow the material to
return to its initial deformation-free state at the end of the heat pulse. This means
that the post-heated area tends to remain elevated due to a non-zero out-of-
plane strain component. Such observation explains the origin of surface
roughening, which is regularly observed experimentally as early as after a few
pulses and is well known to be a precursor of crack nucleation at later stages of
ELM exposure.
101
Chapter 4.
Damage evolution and failure of tungsten
at the microscopic level
in thermomechanical fatigue conditions. Equation Cha pter 4 Section 4
4.1 Introduction
4.1.1 The need of CPFEM
Finally, we have come to the central question of the project: understanding the
origin of crack formation in tungsten exposed to thermal shocks. As the fatigue
cracks in tungsten appear at GBs and, especially, at triple junctions, fine-scale
processes at the grain level are significant, making the J2 plasticity model
inapplicable for analysis.
Understanding the initiation of fatigue damage requires accounting for
heterogeneity of stress and strain not only from one grain to another
(intergranular heterogeneity) but also inside every grain (intragranular
heterogeneity), which could not be captured by the Taylor-type CP model used
in Chapter 3. The intragranular heterogeneity originates due to complex
boundary conditions at every grain in real deformed polycrystals, where both
stress equilibrium and strain compatibility have to be fulfilled simultaneously.
Plus, given the fact that the microstructure heterogeneity will further increase
during neutron irradiation in fusion devices, as a result of plastic flow instability
observed in irradiated material experimentally, the heterogeneity of strain in
grains will amplify as well. Another important, experimentally discovered point,
is the effect of the grain shape and the orientation of the elongated direction with
respect to the exposed surface on the formation of cracks in tungsten. Defining
grain shapes and mapping their neighbours is not possible in the Taylor-type CP
simulations.
That is why a thorough investigation of mechanical response of tungsten to
thermal shocks requires an appropriate computational tool, able to describe
material plasticity at the grain level, to take account of the grain shape and
interaction with neighbours, and not to neglect the strain and stress gradients
inside grains.
A full potential of crystal plasticity is unlocked in an advanced technique called
“crystal plasticity based finite element modelling” (CPFEM), which is used in this
4. Thermomechanical fatigue of tungsten at the microscopic level
102
chapter for exact predictions of fatigue damage in polycrystalline tungsten
subjected to thermal shocks due to ELMs. In the CPFEM framework every grain
of a polycrystal is tessellated into finite elements, in which stress and strain are
defined by a complex interaction with the surrounding elements, controlled by
the CP model, relying on dislocation glide in slip systems.
4.1.2 Overview of CPFEM theory
A brief quotation from a comprehensive overview of the CPFEM approach
[75,102] is provided here for the convenience of the reader, highlighting its
features and differences from the mean-field CP approach.
The CPFE method has evolved as an attempt to employ some of the extensive
knowledge gained from experimental and theoretical studies of single crystal
deformation and dislocation motion to inform the further development of
continuum field theories of deformation. The general framework supplied by
variational crystal plasticity formulations provides an attractive vehicle for
developing a comprehensive theory of plasticity that incorporates existing
knowledge of the physics of deformation processes [169–171] into the
computational tools of continuum mechanics [74] with the aim of developing
advanced and physically based design methods for engineering applications
[172]. The first CPFE simulations were performed by Peirce et al. in 1982 [173].
One main advantage of CPFE models lies in their ability to solve crystal
mechanical problems under complicated internal and/or external boundary
conditions. This aspect is not a mere computational advantage but is an inherent
part of the physics of crystal mechanics since it enables one to tackle those
boundary conditions that are imposed by inter- and intra-grain micromechanical
interactions [174]. This is not only essential to study in-grain or grain cluster
mechanical problems but also to better understand the often quite abrupt
mechanical transitions at interfaces [175].
CPFE simulations can be used both at microscopic and macroscopic scales [176].
Examples for small-scale applications are inter- and intra-grain mechanics,
damage initiation, mechanics at interfaces, simulation of micromechanical
experiments (e.g. indentation, pillar compression, beam bending), or the
prediction of local lattice curvatures and mechanical size effects. Consequently,
CPFE methods gain momentum for the field of small-scale material testing where
the experimental boundary conditions are difficult to control and/or monitor. In
such cases the experimental results may sometimes be hard to interpret without
corresponding CPFE simulations that allow an experimentalist to simulate the
effects of details in the contact and boundary conditions.
4.1.3 Indicators of fatigue
This subsection is inspired by analysis of a review paper by Korsunsky [177] and
the references therein.
4. Thermomechanical fatigue of tungsten at the microscopic level
103
To increase reliability of fatigue durability prediction, the used finite element
model must possess a constitutive law, validated in a wide range of temperature
and loading conditions, rely on relevant experimental data and utilize an
adequate relationship linking deformation history and damage [177]. But,
generally speaking, very large accumulated strain, exceeding the experimental
limit, can be attained in finite element analysis, if solely a plasticity law is
provided, since the model is not informed about the fracture strain. It is not
physically-sound, and the model requires a criterion to limit the possible
deformation range, or to indicate the moment of fracture.
In order to predict crack initiation in mechanical fatigue, a number of fatigue
indicator parameters (FIP) has been proposed and found useful in different
applications. Generally, an FIP can be written as a function of cyclic strain or
stress. When it reaches a predefined critical threshold, the sample is considered
to break.
In specimens of simple shape this indicator can be calculated as a single number
for the whole sample (evolving with time), but in objects of complex shape
subjected to fatigue, the indicator must be evaluated locally, showing a non-
uniform spatial distribution which would indicate the most probable location
and moment of material failure.
Deformation history can be accounted for if is taken as a functional, calculated
including the combination of stress and strain values at all data points in a stress-
strain loop [177]. An example of a functional criterion is the energy dissipation
criterion [178,179], which may be written as
dt
t t t (4.1)
where the integral can be taken over a fatigue cycle or another time interval t of
interest.
According to [177],
“Skelton [180] suggested that the dissipated energy per saturated
cycle could be considered as a material constant expressing the
necessary energy to propagate a crack by the distance equivalent to
the size of the process zone, and proposed a way in which the
lifetime of the specimen was related to a crack propagation law
driven by dissipated energy.”
In the case of non-saturated stress-strain cycle, the evolution of the loop shape
and dimensions has to be taken into account in the durability prediction, or the
FIP has to be calculated incrementally in every cycle.
Whereas many criteria were obtained for uniaxial cyclic stress, the choice of the
exact mathematical expression in the case of multiaxial stress is challenging, and
can be solved, for instance, by choosing an appropriate “norm” of the involved
tensors, such as the von Mises stress and strain or a tensor operation resulting
in a scalar. Not only dissipated energy density was tested as an FIP, but such
4. Thermomechanical fatigue of tungsten at the microscopic level
104
individual quantities as accumulated slip [181,182] or slip rate [183]. Some
works have not identified any particular approach to give invariably better
predictions than others [177]. Others clearly prefer the energy density [103]
claiming that individual quantities have not been found to correlate with
experimentally observed number of cycles to nucleation of crack.
Considering the reasoning above, the dissipated energy density was selected as
an FIP in the present work. The increment of dissipated energy at a given
material point experiencing multiaxial stress state can be written at the
microscopic level based on shear stresses and shear rates in the -th
crystallographic slip system [177], which can be calculated either within the CP
model
1
d dN
t
(4.2)
or at the macroscopic level, being the product of the Cauchy stress σ and the
plastic component of velocity gradient pL [184].
pd : dM t σ L (4.3)
Subscripts and M stand for “microscopic” and “macroscopic”
correspondingly. The chosen kinds of stress and strain rate must be power-
conjugate in order to represent a meaningful product.
Simulations of fatigue crack formation with the help of CPFEM involving an FIP
have already been performed and reported [185].
It is still unclear, however, and has scarcely been reported in literature whether
the emerging backstresses have an effect on the fatigue life. Do the dislocation
pile-ups (the main cause of kinematic hardening), moving periodically back and
forth due to external cyclic load, contribute to the damage accumulation? If yes,
how should the backstresses be included in the calculation of FIPs?
Most of the conventional fatigue indicators assume that damage initiates inside
the bulk of grains whereas damage is expected at GB in this material. Hence, we
define a new fatigue indicator which is specifically designed for GB cracking
(although it could be justified also in particle strengthened metals). Using CPFEM
the fatigue indicator is computed everywhere inside the grain in order to
demonstrate that it's value is maximized at GB. Based on the anisotropy of
adjacent grains, CPFEM allows predicting which are the weak spots along the GB
according to the chosen fatigue indicator.
We hypothesized that since dislocation pile-ups produce stress field
concentrated at GBs, either boundary cracks or yielding in the adjacent grains
can nucleate [100]. It means that the ability of material to experience kinematic
hardening due to the presence of dislocation pileups may promote damage
initiation. In comparison, purely isotropic hardening assumes that dislocation
4. Thermomechanical fatigue of tungsten at the microscopic level
105
density increases proportionally to the accumulated strain irrespective of the
location in a grain; be it next to or far away from a GB (or another obstacle).
In this work, we assumed that, in the presence of kinematic hardening, the FIP
should scale with the stress predicted ahead of dislocation pile ups rather than
the stress experienced by mobile dislocations. The relevant stress value is thus
the sum of (rather than the difference between) the resolved shear stress and
the backstress b
in slip system . This takes account of the stress-magnifying
nature of dislocation pile-ups.
1
d dM
b t
(4.4)
An important point is to determine the threshold value, which corresponds to
the fracture of material as a result of exhausting the deformation capacity.
Usually in literature this is done on the basis of fatigue experiments, knowing the
energy dissipated in one cycle [177]. The threshold should depend on the
material microstructure, and even orientation of grains of a given material, since
a high density of GBs at the sample surface promotes percolation of initial cracks
and reduces the fatigue life. In the absence of fatigue tests on IGP tungsten we
attempted to calculate the threshold based on energy dissipated in tensile tests,
as shown in section Discussion.
The ability to capture stress- and strain heterogeneity in CPFEM models implies
that the FIP distribution is also heterogeneous, and its maximum indicates the
location of a potential crack formation. It can be thought of reaching such
dislocation configuration at high strain, where every new coming dislocation
contributes to the formation of a void, which in turn serves as a seed for a crack.
The fact that the studied tungsten is a single-phase uniform material eliminates
a potential difficulty of treating in a different way regions close to a second-phase
inclusion, where cracks can form even at low plastic strain due to the mismatch
of stiffness or strength.
4.1.4 Overview of the chapter
In this chapter we set the goal to find the difference between the mechanical
response of tungsten exposed to ELM-like thermal shocks, assuming prevalence
of either isotropic or kinematic hardening of the material.
We extend the workflow proposed in Chapter 3, and apply the strain path
recorded in the macroscopic simulations of thermal shock, to a finite element
mesh representing a polycrystal, in which crystal plasticity model developed in
Chapter 3 serves as the constitutive law. The details of the FE simulation setup
are discussed in Section 4.2.
To obtain a clear view and single out the effect of grain shape alone on the
damage accumulation and on the intra-granular heterogeneity of strain and
stress, each constitutive law is applied here to both of the observed grain shapes
4. Thermomechanical fatigue of tungsten at the microscopic level
106
— elongated and equiaxed ones — as if we had two hypothetical materials on
top of the two existing tungsten grades. Different quantities are used to assess
damage in the polycrystals — stress at GBs and FIP, linked to the dissipated
energy. They are applied to recrystallized and as-received tungsten grades
correspondingly in Sections 4.3 and 4.4.
Another application of the CPFEM model is considered in Section 4.5, where a
delamination of tungsten foil is simulated, inspired by an experimental work
dedicated to the measurement of fracture toughness of a ultrafine-grained foil
[40].
The obtained results are discussed in Section 4.7. Part of this chapter has been
included in our published paper [166].
4.2 FEA setup
4.2.1 Crystal plasticity — standalone and CPFEM
The CP model discussed in Chapter 3 can be used in two modes:
i) In the standalone mode — it is a Taylor-based crystal plasticity, in
which individual grains are assigned the same deformation as imposed
to the whole polycrystal. Grains cannot be visualized in this approach;
they actually do not have exact location, shape and neighbours. Such
simulations of an “abstract polycrystal” are presented in Chapter 3.
ii) In the CPFEM framework — it is coupled with finite element solver
Abaqus, in which a representative volume element (RVE) is tessellated
into several grains, and every grain is tessellated into finite elements
using a FE mesh generator (Figure 4.1). Then every finite element is
characterized by a given grain orientation and a set of state variables,
whose evolution is controlled by the CP model. This type of simulations
is discussed in the present chapter.
Grains in the CPFEM framework are usually tessellated into simple shapes, such
as cubes, as shown in Figure 4.1a. However, grains in real polycrystals have
complex shape, which is best represented in simulations with the help of the
Voronoï tessellation (Figure 4.1b). Meshing of complex polyhedral can be done
with the help of triangulation, forcing the use of tetrahedral elements, whereas
simple cubic grains are easily tessellated into hexahedral elements. Below we
compare the use of the two element types.
Apart from being initially integrated into commercial finite element codes,
CPFEM approach can be implemented as a user-defined subroutine, making it
more accessible to researchers and available on many platforms [102].
4. Thermomechanical fatigue of tungsten at the microscopic level
107
a) b)
Figure 4.1. Representation of polycrystals in CPFEM framework. a) Simplified 3D grain assembly [186], b) advanced grain assembly obtained with the help of the Voronoï tessellation [187].
UMAT is a user-defined material subroutine for the standard finite element
solver Abaqus, which provides sufficient flexibility to parameterize the
mechanical response of virtually any material, including anisotropic, and to
incorporate any physics behind. Hence, UMAT was considered as a tool of choice
to implement the crystal plasticity model and couple it with Abaqus.
The model presented in the thesis is of local type. This means that the response
of a material point is assumed independent of the state at neighbouring points
[188]. In reality, the local amplitude of backstresses should depend on the
shortest distance to the GB, and the strength of pile ups should depend on the
permeability of GBs to dislocations. In the present model, grain size is accounted
for in a very simplified way. In a nonlocal model, the plastic strain gradient
contributes to hardening while introducing a material length scale. There is thus
exchange of information between neighbouring material points [189–194].
Another simplified approach would be to add an extra state variable at every
material point, which is the distance to the nearest GB, and modify the model
equations as well, to hinder the dislocation motion in the direction of the nearest
GB, mimicking the repulsive effect of backstresses.
4.2.2 Cohesive elements
Cohesive elements (CE), also called cohesive zones (CZ), are 2D finite elements
that can be used as a layer connecting neighbouring 3D elements. As the name
suggests, they are placed along surfaces inside the FE mesh which are initially
joined but are likely to separate in the course of deformation. The cohesive force
must be representative of the physics of the bonding of the two surfaces. The
latter surfaces may belong to two distinct components (e.g. coating on substrate,
or a layer of glue) or be the crack faces in a single component (Figure 4.2a). CE
are typically used in simulations of delamination of fibre-reinforced composite
laminates, crack growth at the macroscopic level [195] and in polycrystals at the
4. Thermomechanical fatigue of tungsten at the microscopic level
108
microscopic level [193,194,196].Note that even at the lower scale cohesive
elements are applied under assumption of continuous media and cannot capture
effects originating at the level of atoms or dislocations, where such models as
molecular dynamics, kinetic Monte-Carlo or dislocation dynamics would be
more appropriate. If together with placing CE along GBs the strain gradient
plasticity model is applied in a FEA, grain-size-dependent strength and plasticity
of polycrystals could be investigated [193,194].
Akin to the volume finite element, CE are characterised by a specific constitutive
law, called “traction-separation law” (TSL), which defines the stress applied to a
cohesive element as a function of the associated separation of the two surfaces.
Various formulations of TSL exist for different applications, most of which
enforce zero strength beyond a critical separation 0 (Figure 4.2b), meaning that
the given element cannot bear any (tensile) load and is considered “broken” or
“opened”. The slope of the initial linear region is the element stiffness, and the
area under the TSL is the cohesive energy 0 , or the energy spent per unit area
of crack extension. For brittle materials this value represents the fracture
toughness, but for predominantly plastic material, such as tungsten at high
temperature, the TSL must be different and include the effect of the plastic zone
ahead of the crack tip in real materials.
In this chapter, the cohesive elements are first used in a rather unconventional
way: they are used as strain gauges in order to measure the predicted stress
values exactly along the GBs. For this, they are assigned a very large stiffness
(much larger than the elastic stiffness of tungsten) and an unattainable strength,
so that the opening remains infinitesimal and reversible. In the last section of the
chapter, CE are used while allowing progressive damage in order to predict the
interplay of intra-granular and inter-granular cracking in tungsten as reported
experimentally in [40].
a) b)
Figure 4.2. a) A diagram illustrating the use of cohesive elements in a crack propagation problem. b) Example of a traction-separation law, normalised by the
maximal cohesive stress 0T and maximal cohesive separation 0 [197].
4. Thermomechanical fatigue of tungsten at the microscopic level
109
4.2.3 Analysis of mesh sensitivity
Before we can simulate thermal shock tests in the CPFEM framework, we should
identify the mesh features: element type, order, mesh density. To do so, a
benchmark of uniaxial tension of a polycrystal composed of 3×3×3 cubic grains
has been performed, using the crystal plasticity UMAT as the material law.
a)
b)
c)
d)
e)
f)
Figure 4.3. Maximal principal stress distribution in “bricks” with different level of refinement: coarse (a, b), medium (c, d) fine (e, f), and element type: C3D8 in “simple bricks” (a, c, e) and C3D10 in “Gmsh-generated bricks” (b, d, f)
The grains have been meshed assuming either a linear or a quadratic
displacement filed inside each element. Hexahedral elements of the 1st order
(referred to as C3D8 in Abaqus and “simple bricks” here) were generated
manually. Then, using the Gmsh software [138], the same polycrystal was
meshed again using tetrahedral elements of the 2nd order (referred to as C3D10
4. Thermomechanical fatigue of tungsten at the microscopic level
110
in Abaqus and “Gmsh-generated bricks” here). It is known that the use of
tetrahedral elements of the 1st order should be avoided under large plastic
strains, as they possess unphysically high stiffness when incompressibility is
approached [75]
Three levels of mesh density were selected for both types of meshes:
coarse, around 2200…2500 nodes
medium, 11000…12000 nodes
fine, 22000…26000 nodes
The polycrystal composed of randomly-oriented grains was loaded under
uniaxial tension in the X direction at 400 °C and 6·10-4 s-1 up to 30% of strain.
Periodic boundary conditions were enforced so that grains on the edge behave
as if they were embedded in the bulk of a polycrystal.
Figure 4.3 collects the images of the deformed 3×3×3 polycrystals at the end of
deformation, where the colour maps the distribution of the maximal principal
stress. Notably, the global shape change is always the same and the pattern of
typical maxima and minima of stress is repeated in both mesh types, and
especially in the simple bricks.
It would be meaningful to compare the whole distribution of stress in the grain
interior and in cohesive elements, to characterize intergranular and
intragranular heterogeneity. As the crack formation is defined by the maximal
tensile stress value, analysis of stress distribution is important from the point of
view of damage accumulation assessment and is used in the further text. An
excessive scatter of the values, being unphysical, could indicate an inadequate
mesh.
Figure 4.4. A boxplot shows schematically five main reference points of a smooth distribution of stress in cohesive elements.
4. Thermomechanical fatigue of tungsten at the microscopic level
111
We use so-called “boxplots” in this chapter to easily visualize whole distributions
of a quantity in question (stress in GBs in this case). The distribution is
characterized by five most important reference points, facilitating comparison of
several distributions in one figure.
As Figure 4.4 illustrates, the filled boxes represent the middle 50% of all the
stress values, taken between the first and the third quartiles of the distribution
(denoted in the figure as Q25 and Q75 correspondingly). Contrary to usual
convention, we use the thin vertical “whiskers” to highlight the range between
the 5th and 25th percentiles (the lower whisker) and between the 75th and 95th
percentiles (the upper whisker). A horizontal black bar in the middle of the box
corresponds to the distribution median, which is the second quartile or the 50th
percentile (Q50).
To characterize the stress state in several meshes quantitatively, distributions of
normal stress in the cohesive zones are plotted in Figure 4.5 with open boxes
grouped by their orientation with respect to the coordinate axes. Due to the
geometry simplicity, the cohesive elements can be split into three groups, normal
to one of the three coordinate axes (X, Y, Z), denoted as CZX, CZY, CZZ
respectively. Filled boxes show the distribution of maximal principal stress in the
grain interior, measured in 13 out of 27 grains (to reduce the number of boxes in
one plot). The boxplots are grouped by the element size, from coarse to fine.
The plot provides the following evidence. Distribution of stress in cohesive
elements is very wide, spanning the range beyond 1 GPa in both compression
and tension. Even though the median of stress distribution in CZX is higher than
in other groups (implying predominantly tensile nature of stress in CZX), all the
distributions overlap significantly, and this effect does not diminish with the
mesh refinement.
Both intragranular (the range of individual filled boxes in Figure 4.5a) and
intergranular heterogeneity (the difference between neighbouring filled boxes)
of maximal principal stress in the grain interior of simple bricks is much lower
than the range of distribution of stress in CZ and looks reasonable. This indicates
that linear hexahedral elements might be suitable for simulations with the help
of CPFEM, but not together with cohesive elements, which demonstrated
excessively wide range of stress, compared to that in the 3D elements.
A similar analysis of stress state in the Gmsh-generated bricks (Figure 4.5b)
shows much narrower distribution of normal stress in the cohesive elements.
Here the central 50% of stress recorded in CZX and the other two groups do not
overlap. Besides, the stress distribution in CZY and CZZ is symmetric with
respect to zero, in line with the uniaxial stress state of the polycrystal.
4. Thermomechanical fatigue of tungsten at the microscopic level
112
a)
b)
Figure 4.5. Distribution of normal stress in CZ (open boxes) and maximal principal stress in grain interior (filled boxes) in a) “simple bricks” and b) “Gmsh-generated bricks” with different mesh refinement at 30% of tensile strain. Each colour of the filled boxes corresponds to one of the 13 grains.
4. Thermomechanical fatigue of tungsten at the microscopic level
113
The density of Gmsh-generated mesh affects the intragranular heterogeneity of
stress in the grain interior, which is high in the coarse mesh, compared to the
medium and the fine ones, and slightly higher compared to that in the simple
bricks. Also, just like in the case of simple bricks, the stress in the grain interior
is higher than in the CZ normal to the tensile axis.
As mentioned above, we first used cohesive elements with unrealistic stiffness
(million times higher than the Young modulus) to serve as “stress gauges” only.
Can the choice of element stiffness play a role in the appearance of the gap
between stress in cohesive elements and the grain interior, observed in Figure
4.5a-b? To check that, the same Gmsh-generated brick with the medium mesh
density was loaded in tension, while the stiffness of cohesive elements was
reduced to 400 GPa, close to the value of the Young modulus of tungsten.
Distribution of stress in cohesive elements and in grains turned out to be almost
identical, irrespective of the stiffness, as shown in Figure 4.6.
Figure 4.6. Effect of cohesive element stiffness on the stress distribution in cohesive elements and grain interior of a Gmsh-generated brick with medium-size elements. Each colour of the filled boxes corresponds to one of the 27 grains.
Thus, higher stress in the grain interior compared to the GBs is a feature of
models of this type, and is not an undesirable artefact. Note that the maximal
principal stress in the grain interior was compared to the stress normal to
cohesive elements, and these quantities are not necessary measured in the same
coordinate system. As Figure 4.3 shows, the cohesive elements rotate with
deformation, and the norm to their surface deviates from the tensile direction.
4. Thermomechanical fatigue of tungsten at the microscopic level
114
Consequently, the stress state in rotated cohesive element changes: the shear
component of stress appears, and the normal stress component reduces.
To conclude, the mesh with tetrahedral 2nd order elements shows better
performance, making this element type favourable for the consequent CPFEM
simulations. It avoids unphysically wide distribution of stress in cohesive
elements even despite the fact that cohesive elements of 1st order were used with
both 3D element types. Assigning high stiffness to cohesive elements does not
have adverse effect on the stress heterogeneity neither in the grain interior, nor
in the cohesive elements themselves, but suppresses their opening, undesirable
when the CZ are used as stress gauges at GBs. Besides, to avoid symmetric and
ordered structure of GBs, which can bias the distribution of normal stress in
cohesive elements, polycrystals with polyhedral grains obtained with the help of
the Voronoï tessellation, are preferred to those with cubic grains (bricks).
4.2.4 Mesh of polycrystals used in the work
Periodic finite element meshes which conform to GBs in a polycrystalline
aggregate made of periodic Voronoï cells were generated with an automatic
method [187]. The algorithm allows the user to set up the grain number, the
average aspect ratio in the polycrystal, and the crystallographic orientation of
every grain. Cohesive elements were placed along all the GBs to serve as stress
gauges.
a) b) c)
Figure 4.7. The finite element meshes used in the simulations of thermal fatigue with CPFEM, a) transversal with respect to the heat flux, b) longitudinal, c) equiaxed.
In accordance with the experimentally obtained EBSD grain orientation maps of
tungsten in both as-received and recrystallized conditions, two FE meshes were
created with, respectively, elongated and equiaxed grains. The aspect ratio of the
elongated grains in the longitudinal, normal and transverse directions (“L”, “N”
and “T”) was chosen equal to 4:2:1. To comply with the thermal shock
experiments, where the tungsten samples were oriented either in the
longitudinal or in the transverse direction with respect to the heated surface
(that is, the elongated grains were parallel, or perpendicular to the heated
4. Thermomechanical fatigue of tungsten at the microscopic level
115
surface), the mesh with elongated grains was oriented in the two possible
directions, too, as shown in Figure 4.7.
The meshes in the present simulation consisted of eight grains for both equiaxed
and elongated polycrystals, tessellated into approximately 10 000 2nd order
tetrahedral elements and the same number of cohesive elements, connecting the
neighbouring grains. It is to be noted that the mesh with elongated grains could
not be obtained by mere stretching the mesh with equiaxed grains, otherwise the
initially distorted elongated finite elements would cause numerical issues during
simulations. It means that in order to obtain a mesh with elongated grains, the
mesh with equiaxed grains was constructed first, then only the surfaces defining
the GBs were stretched, and both the GBs and the grain interior were re-meshed
with equiaxed finite elements.
Despite the fact that the elongated grains are a feature of the as-received
tungsten, and the equiaxed grains are a result of recrystallization, both mesh
types were probed in simulations with constitutive laws for the as-received and
as-recrystallized tungsten in order to single out the effect of grain shape alone.
4.3 Analysis of fatigue damage in recrystallized
tungsten using cohesive elements
The thermomechanical effect of the exposure to thermal shocks was simulated
at the microscopic level in three polycrystalline meshes shown in Figure 4.7. The
aggregate of equiaxed grains was also oriented in two different directions with
respect to the heated surface (labelled as “X” and “Z” orientation). Even though
the two orientations of the mesh with equiaxed grains are identical from the
physical point of view, such procedure allows one to estimate the sensitivity of
the output to the grain arrangement and the mesh variation. For the same reason
a random crystallographic texture was assigned to all polycrystals.
Similar to the analysis done in Chapter 3, the polycrystals were restrained in all
directions, except the normal to the heated surface, thus enforcing plane stress
conditions. The temperature evolved following a triangular waveform with 1 ms
of heating and 1 ms of cooling to mimic a thermal shock. The build-up of
intergranular stresses was predicted with the help of the CP model, while
accounting for the elastic anisotropy of tungsten.
4. Thermomechanical fatigue of tungsten at the microscopic level
116
4.3.1 Results
Since CPFEM analysis is time-consuming, four thermal pulses were simulated for
every test condition and polycrystal. First quantities recorded in the simulations
were the in-plane stress and the out-of-plane strain averaged over the whole
polycrystal. The stress-strain loops obtained in the thermal shock simulations
and demonstrated in Figure 4.8 and Figure 4.9 for equiaxed and elongated grains
correspondingly, generally repeat the patterns observed in the corresponding
standalone simulations in Chapter 3.
Comparing Figure 4.8 and Figure 4.9, no effect of the selected mesh and its
orientation with respect to the exposed surface on the average mechanical
response of recrystallized tungsten can be found.
Figure 4.8. Stress-strain loops as a result of simulation of thermal shock on the surface of the recrystallized tungsten (equiaxed grains).
4. Thermomechanical fatigue of tungsten at the microscopic level
117
Figure 4.9. Stress-strain loops as a result of simulation of thermal shock on the surface of the recrystallized tungsten (elongated grains).
The distributions of normal stresses in cohesive elements are shown in Figure
4.10 and Figure 4.11 for the equiaxed and elongated grains correspondingly. The
panels of the figures correspond to various base temperature and thermal flux.
Each panel shows two thermal pulses which consisted of 1 ms heating and 1 ms
cooling each, in which compressive stresses dominate in the heating phase, and
tensile stresses are observed in the cooling phase.
These figures give an overview of the trends in the mechanical response of
tungsten to thermal shocks. Similar to the stress-strain loops, the stress in GBs
decreases with the base temperature, as material becomes softer. The median
tensile stress at the end of cooling is higher than the median compressive stress
at the end of heating, due to the asymmetry of the stress-strain loops shown in
Figure 4.8 and Figure 4.9.
4. Thermomechanical fatigue of tungsten at the microscopic level
118
Figure 4.10. The evolution of normal stress distribution in the GBs of polycrystal with equiaxed grains in the first two thermal shocks.
The choice of orientation (“X” or “Z”) of the equiaxed grains does not influence
significantly the distribution of normal stresses in GBs, confirming the model
stability to variations of grain arrangement. However, the choice of orientation
of the elongated grains with respect to the exposed surface impacts the stress
state drastically (Figure 4.11). Stresses in the boundaries of grains in the “T”
orientation (perpendicular to the exposed surface) are much larger in tension as
well as in compression. Hence, the majority of cohesive elements experiences
tensile stress and are prone to the intergranular crack formation and
propagation. Thus, the microscopic simulation results conform with the
experimentally observed premature cracking of samples with transversal
orientation of grains [26,71].
4. Thermomechanical fatigue of tungsten at the microscopic level
119
Figure 4.11. The evolution of normal stress distribution in the GBs of polycrystal with elongated grains in the first three thermal shocks.
The distribution of shear stresses in the GBs was assessed as well. Figure 4.12
shows its evolution in time for the elongated grains. The shear stress is not
influenced by the choice of the polycrystal orientation and shows the same
trends with temperature and thermal power density as the normal stresses.
Finally, to compare the mechanical response of the material with equiaxed and
elongated grains, the distribution of normal stresses in GBs were analysed in the
first two thermal pulses to make the boxplots clearer. Figure 4.13 reveals that
tensile stresses developed in the boundaries of equiaxed grains are high and
compared to those in the elongated grains in the “T” orientation. This can be the
main reason why cracks are formed early in tungsten with equiaxed grains, as
observed in experiments.
4. Thermomechanical fatigue of tungsten at the microscopic level
120
Figure 4.12. The evolution of shear stress distribution in the GBs of polycrystal with elongated grains in the first two thermal shocks.
4. Thermomechanical fatigue of tungsten at the microscopic level
121
a)
b)
Figure 4.13. The evolution of normal stresses in the first two thermal pulses in recrystallized tungsten exposed to 380 MW m-2 thermal power density at base temperature 27 °C. a) Elongated grains, b) equiaxed grains.
4. Thermomechanical fatigue of tungsten at the microscopic level
122
4.3.2 A note on the stress in cohesive elements
The first impression is that the simulations confirm that cracks will appear in the
transversal orientation sooner than in the longitudinal orientation, as observed
by experiments [71]. However, the difference in normal stresses in these two
polycrystals can be purely geometrical, and, thus, should be treated with care.
Figure 4.14. Distribution of the angle between cohesive elements and the heated surface in the three considered meshes.
Figure 4.15. Correlation between normal stress in cohesive elements and their orientation.
4. Thermomechanical fatigue of tungsten at the microscopic level
123
To check that, the distribution of the angle between a cohesive element and the
heated surface is plotted in Figure 4.14. In the transversal orientation the
majority of cohesive elements are perpendicular to the heated surface
(maximum at 90°), while in the longitudinal orientation most of them are
misaligned to it by a small angle (maximum at 30°).
Moreover, normal stress in cohesive elements correlates with the angle between
cohesive elements and the heated surface, as illustrated in Figure 4.15, that shifts
the distribution of stresses plotted in Figure 4.11 and Figure 4.13 to higher
values for the transversally-oriented polycrystals.
However, the predominant orientation of GBs can indeed be the real origin of
sooner crack formation in the transversal samples. An alternative approach to
characterise the possibility of cracking under thermal shocks is considered in the
next section for the as-received tungsten.
4.3.3 Conclusions of the section
Experimentally, commercial grades of tungsten in the transversal orientation
show early fracture compared to the longitudinal orientation in thermal shock
tests [26,198], tensile tests [57] and fracture toughness tests [45,199].
The simulation of thermal shock tests performed in the present work, using an
approach that links the macro- and microscopic levels, demonstrates that this
difference can be explained by statistically higher tensile stresses in GBs in the
transversal orientation during the cooling phase (immediately after every
thermal pulse). As the maximal tensile stress increases with the increase of
thermal power density and with the decrease of the base temperature, it explains
the existence of the cracking threshold derived from the thermal shock
experiments, i.e. the minimal thermal power density at which cracks appear, as
a function of the base temperature.
This conclusion, however, could have been biased due to purely geometrical
reasons: the majority of cohesive elements in the simulations with longitudinal
samples are oriented in the stress-free direction, i.e. they do not experience
normal stresses, which drastically shifts the distribution to lower values. On the
other hand, the difference in the geometrical arrangement of grains can indeed
be the main reason of different strength of the material in transversal
orientation. An alternative approach to characterize development of damage in
thermo-mechanically loaded material in various orientations is discussed in the
next section devoted to the as-received tungsten.
4. Thermomechanical fatigue of tungsten at the microscopic level
124
4.4 Analysis of fatigue damage in as-received
tungsten using the fatigue indicator
Having finalised the analysis of thermomechanical response of recrystallized
tungsten to thermal shocks, here we estimate the accumulation of fatigue
damage under thermal shocks in the as-received IGP tungsten. Different grain
shape and their orientation with respect to the heated surface are considered in
the same manner as for the recrystallized tungsten. In contrast with the previous
section, an FIP was selected as an alternative way characterising the fracture
probability, instead of measuring the normal stress in cohesive elements.
Besides, as long as a commercial grade of tungsten demonstrated the
Bauschinger effect associated with kinematic hardening [59], we investigate its
effect on the damage accumulation.
Similar to the simulations of the recrystallized tungsten, the polycrystal was
restrained in two directions, and was free to deform in the third direction,
ensuring plane stress state. The temperature of the whole polycrystal evolved
following triangular waveform. Three values of the base temperature were used:
27 °C, 400 °C or 1000 °C, and the temperature pulse height was either 350 °C or
700 °C, corresponding to thermal power density 190 MW m-2 or 380 MW m-2 in
the experiments performed by the team of Wirtz [26]. Ten thermal cycles were
simulated to identify trends in FIP. In this series of simulations only two
hardening cases were considered: purely isotropic and mixed, as explained in
Section Discussion of Chapter 3.
4.4.1 Results
The average in-plane stress and out-of-plane strain in the polycrystal collected
in Figure 4.16, grouped by the thermal shock parameters, basically reproduce
the results obtained in the mean-field CP simulations in Chapter 3, showing that
deformation is mostly elastic at low power density 190 MW m-2. At high power
density 380 MW m-2, the plastic strain dominates, the presence of kinematic
hardening leads to a pronounced Bauschinger effect. The stress-strain loops for
the as-received tungsten have higher symmetry compared to the as-
recrystallized grade shown in Figure 4.8.
4. Thermomechanical fatigue of tungsten at the microscopic level
125
Figure 4.16. The average in-plane stress and out-of-plane strain in the polycrystal subjected to thermal shocks at different base temperature and absorbed power density.
The evolution of FIP averaged over the whole polycrystal during the ten thermal
shocks is shown in Figure 4.17. When kinematic hardening is active, the FIP
grows faster, as the stress at GBs is magnified due to the cumulative effect of
dislocation pile-ups. Hence, the eventual crack formation is delayed in the case
of pure isotropic hardening.
Damage is accumulated very slowly in samples exposed to the power density
190 MW m-
2, and we focus on simulations with the power density 380 MW m-2
in the further text, covering the case of significant plastic deformation and low
cycle fatigue. Little effect of the base temperature is seen, however.
4. Thermomechanical fatigue of tungsten at the microscopic level
126
Figure 4.17. The average FIP in the whole polycrystal with the L orientation tested at different base temperature and applied power density.
Attention must also be paid to the microscopic spatial heterogeneity of damage.
The distribution of FIP in two selected grains after ten thermal shocks at
380 MW m-2 is shown in Figure 4.18. Here the distribution is shown in the form
of boxplot, like in the section devoted to the recrystallized tungsten, but in the
traditional way, where the whiskers span the following range: 1.5 times the filled
box height, measured from the first quartile down and from the third quartile up.
The values outside of this range are considered “outliers” and are shown with
dots or small circles.
Figure 4.18 reveals that FIP has a lower median in the case of isotropic
hardening, in line with Figure 4.17, but it is difficult to make a conclusion
regarding the effect of kinematic hardening on the range of FIP. Equiaxed grain
1 shows the range of FIP comparable to that of elongated grain 1, but FIP in grain
4 is much larger with numerous outliers.
4. Thermomechanical fatigue of tungsten at the microscopic level
127
Figure 4.18. Distribution of microscopic FIP in two selected grains at the end of ten thermal shocks of 380 MW m-2.
It makes sense to check the distribution of FIP in all grains, hence we plotted it
in Figure 4.19 for the polycrystal with mixed hardening exposed to 380 MW m-2
at 1000 °C. Apparently, FIP is not affected by the orientation of the elongated
grains with respect to the heated surface. However, it is sensitive to the grain
shape, as wider boxes and significantly longer distribution tails are observed in
the equiaxed grains, showing that they are more prone to crack formation
(determined by the maximal attained value of FI), compared to elongated grains.
4. Thermomechanical fatigue of tungsten at the microscopic level
128
Figure 4.19. FIP distribution in individual grains after ten thermal shocks with power density 380 MW m-2 at base temperature 1000 °C in polycrystal with mixed hardening.
Even though we focus on the analysis of FIP in polycrystals exposed to thermal
shocks, distribution of normal stress in cohesive elements was also considered,
similarly to the recrystallized tungsten. The evolution of this distribution in
polycrystals in the first two thermal shocks of 380 MW m-2 at base temperature
1000 °С is illustrated in Figure 4.20 with boxplots for the material with mixed
hardening. Like for the recrystallized W, the highest stress is observed after
cooling of the transversal samples, followed by equiaxed and longitudinal ones.
Figure 4.20. Distribution of normal stress in the cohesive elements within the first two thermal shocks of 380 MW m-2 at base temperature 1000 °C applied to the material with the mixed hardening.
4. Thermomechanical fatigue of tungsten at the microscopic level
129
Figure 4.21. Distribution of normal stress in cohesive zones (open boxes) and maximal principal stress in grain interior (filled boxes) in three meshes of the polycrystal with mixed hardening after exposure to ten thermal shocks at base temperature 1000 °C and power density 380 MW m-2.
Besides, stress in CZ of the same mesh was also compared with the maximal
principal stress in the grain interior, revealing the same gap between their
average values, as in the preliminary simulations in Section “Analysis of mesh
sensitivity”.
The applicability of FIP to the understanding of damage accumulation has been
explored. It was found to be almost unaffected by the material microstructure
within the framework of CP (contrary to the normal stress in cohesive elements,
considered in the simulations of as-recrystallized tungsten). The presence of
kinematic hardening in the as-received tungsten was shown to increase the
accumulation of fatigue damage at GBs, indicating shorter fatigue life of divertor
components in this case.
4.5 The effect of crystalline anisotropy
on grain delamination
As a side problem, we use the CPFEM framework to analyse the propagation of
crack in a thin tungsten foil. As mentioned in Chapter 1, the typical fracture mode
of tungsten at intermediate temperature is intergranular cracking. It was
especially pronounced in experiments on fracture toughness of thin foils [40],
where the initial notch was perpendicular to thin, pancake-like grains, as shown
in Figure 4.22a. Being loaded in mode I, the foil experienced delamination of thin
grains (Figure 4.22b), indicating two main characteristics of this test:
4. Thermomechanical fatigue of tungsten at the microscopic level
130
i) GBs were weaker than the material in the transgranular plane ahead
of the notch,
ii) plane strain state switched to the plane stress, once constraints
were lost due to delamination. The change of loading state induced
relatively high fracture toughness.
a) b)
c) d)
Figure 4.22. a) EBSD maps of pure 0.1 mm tungsten foil projected on a cuboid to better visualize the pancake-like microstructure. Black lines denote the initial notch [40]. b) An example of the foil delamination occurred at 400 °C [40]. c) A polycrystal composed of prismatic grains to represent the microstructure of the foil in CPFEM simulations. Colour highlights separate grains. d) Embedded cohesive elements which have different strength, according to their role: GBs (green) are weaker than the transgranular crack plane (highlighted with red).
4. Thermomechanical fatigue of tungsten at the microscopic level
131
We tested the CPFEM framework trying to reproduce the key features of the cited
experiment. A simplified finite element mesh was created to represent three
layers of flat grains with periodic boundary conditions in all three directions.
Figure 4.22c shows the six grains with different colours. The crystal orientation
of the two grains in blue corresponded to the rotated-cube component
{001}<110>, which was dominant in the experimental texture. The other four
grains were assigned orientations representative of a BCC cold rolling texture
({111}<123>, {113}<110>, {111}<110> and {111}<112>).
Cohesive elements were embedded in the model to represent the crack path
ahead of the notch (the vertical plane in Figure 4.22d), with a small initial notch,
obtained by removing a narrow strip of cohesive elements at its front. GBs were
represented by cohesive elements as well (horizontal planes in Figure 4.22d),
whose strength was set lower than that of the transgranular crack.
The mesh was loaded in mode I, i.e. in the direction Y up to 2% of strain, and was
restrained in the direction Z to achieve plane strain condition. The strength of
GBs varied in a wide range, and that of the crack path was fixed at 950 MPa. The
goal of the simulation was to find out the dependency of delamination on GB
strength and whether delamination is promoted by the crystalline anisotropy.
To that end simulations were launched in pairs — either using the developed CP
model, or assuming the J2 plasticity, i.e. without consideration of crystalline
anisotropy.
Delamination of grains can be assessed by the value of normal strain in the
cohesive elements representing GBs. Colour maps of a few indicative simulations
grouped in Figure 4.23 confirm that if GBs are weak (50 MPa and 250 MPa),
delamination takes place in the CP simulations despite the fact that they were
parallel to the loading direction. The value of normal strain in the GBs became
comparable to the applied strain, almost 0.02 locally. The strain across strong GB
is very low (Figure 4.23f) and no delamination takes place.
Note that delamination was not observed in the J2 simulations even with the
weakest GBs. Instead, the strain accumulates in a thin strip at the crack tip in the
cohesive elements forming the crack plane, which were not able to open thanks
to higher strength. A few simulations with lower strength of the crack plane were
numerically unstable and halted before the sample reached 2% of strain. The
uneven distribution of normal strain in the weak GB in the CP simulations
indicates that local concentration of stress (due to the grain anisotropy)
promoted opening of a few cohesive elements locally, which was subsequently
spread further in the GB.
4. Thermomechanical fatigue of tungsten at the microscopic level
132
a) [GB] = 50 MPa; J2 b) [GB] = 50 MPa; CP
c) [GB] = 250 MPa; J2 d) [GB] = 250 MPa; CP
e) [GB] = 550 MPa; J2 f) [GB] = 550 MPa; CP
Figure 4.23. Maps of normal strain inside cohesive elements (LE33) in simulations with the J2 (a, c, e) and CP (b, d, f) models. The strength of GBs increases from top to bottom: 50 MPa (a, b), 250 MPa (c, d) and 550 MPa (e, f).
4. Thermomechanical fatigue of tungsten at the microscopic level
133
On top of that, to check whether the plane stress condition was achieved due to
delamination, the distribution of the out-of-plane stress (S33) in the 3D elements
of the grain interior was recorded at the end of deformation. The boxplot of the
distributions shown in Figure 4.24 provides the following insights:
A sudden drop of the out-of-plane stress takes place in the CP
simulations at the GB strength between 250 MPa and 350 MPa. The
distribution becomes symmetric with respect to zero, being considered
a clear indicator of achieving plane stress due to crystal anisotropy.
On the contrary, the decrease of the GB strength in the J2 simulations
gradually shifts the distribution of stress towards zero, keeping it
essentially tensile, even for the weakest GBs.
The scatter of stress is much lower in the J2 simulations, which is
expected in the homogeneous, isotropic material.
The difference between median stress observed at high GB strength can
be explained by low number of grains involved, as their mechanical
response is expected to differ from that of an RVE (around 100 grains)
which provided the constitutive law for the J2 simulations.
Figure 4.24. Distribution of the out-of-plane stress S33 in the grain interior in simulations with different GB strength.
The series of simulations clearly show the difference between J2 and CP models
at the grain level and the necessity of the latter when grain anisotropy is
essential. In the considered example the presence of weak GBs alone was not
sufficient to promote delamination of grains parallel to the loading direction.
However, when the crystal anisotropy was taken into account with the help of
4. Thermomechanical fatigue of tungsten at the microscopic level
134
the CP model, heterogeneous distribution of stress in grains built up in the
beginning of plastic deformation caused high stress in GBs locally, initiating the
delamination. This justifies the use of the CP model in the analysis of damage
accumulation at the grain level in tungsten exposed to thermal shocks, discussed
further.
4.6 Discussion
4.6.1 Taylor-based CP and CPFEM simulations of thermal shock
Chapters 3 and 4 are devoted to the mechanical response of IGP tungsten
subjected to ITER-relevant thermal shocks. The Taylor-based CP simulations in
Chapter 3 considered a “virtual” polycrystal where every grain deformed in the
same manner as the whole polycrystal, and development of intragranular stress
heterogeneity was not possible. Simulations of this type are fast, can predict the
stress-strain response and the evolution of crystallographic texture, but they
assume that every state variable is distributed uniformly in every grain. These
simulations were performed first of all to estimate the effect of the chosen
hardening model (isotropic or kinematic) on the shape of stress-strain loops, i.e.
the typical outcome of fatigue experiments. Without consideration of
heterogeneous distribution of stress, it was not possible to properly estimate
damage accumulation.
The framework of CPFEM was utilized in this chapter to go to a finer level, and
to take account of heterogeneous distributions of stress, strain, dislocation
density and other variables within grains, which occur in real polycrystals where
conditions of both strain compatibility and stress equilibrium have to be fulfilled
at GBs, thus avoiding unrealistic overlaps and gaps at GBs.
A microscopic quantity, an FIP, equal to the density of dissipated energy was
chosen to assess the probability of material cracking in the simulations with the
help of CPFEM, reported in this chapter. Its more rapid accumulation in case of
kinematic hardening indicates sooner reaching the threshold and lower fatigue
life of material with high share of kinematic hardening.
4.6.2 Cohesive elements and fatigue indicator
Along with the two approaches to characterise the impact of kinematic
hardening on the material resistance to thermal shocks, the influence of grain
shape was also assessed in two ways. Both of them were applied in the CPFEM
simulations, where the grain shape can be defined explicitly.
The distribution of FIP turned out to be almost unaffected by the grain shape and
their orientation with respect to thermal flux. However, experiments on thermal
shocks confirmed that cracks appear sooner in the samples with the transversal
orientation, i.e. when the grains are perpendicular to the heated surface. It
appeared that the heterogeneous distributions of stress and strain in grains
4. Thermomechanical fatigue of tungsten at the microscopic level
135
alone (which was taken into account in the CPFEM simulations) did not affect the
tendency to accumulate fatigue damage, and, consequently, could not predict the
difference in fracture of material with different grain orientation.
On the contrary, the simulations incorporating cohesive elements showed that
the normal stress at GBs (chosen as an indicator of the crack formation under
thermal shocks) significantly depended on the grain orientation with respect to
the heat flux. Initially considered as a purely geometrical effect, and even an
undesired artefact, which forced us to find another criterion for the crack
initiation, the difference in normal stresses at GBs appeared to be the actual
cause of the sooner formation of cracks in the tungsten with transversal
orientation of grains.
Thus, the conclusion can be made that the crack formation in tungsten exposed
to thermal shocks is controlled by the strength of GBs, rather than the strain
heterogeneity within a grain. And indeed, unfavourable orientation of grains, i.e.
unfavourable orientation of GBs, when most of them are perpendicular to the
heated surface and experience normal stress during the cooling phase of thermal
pulses, leads to much sooner material failure under plasma instabilities. Then, to
be able to predict the fatigue life of tungsten under thermal shocks, the TSL at
the grain level should be adjusted based on experimental data, introducing
critical stress and strain. Further enhancing the model, the TSL can be made
dependent on the value of FIP in a nearest 3D element, rendering the model
nonlocal.
4.6.3 The use of tensile tests to derive the threshold fatigue
indicator
We can also propose a way to estimate the number of thermal cycles, that the
material can sustain before cracking. It should be possible to estimate the
threshold FIP based on the energy density dissipated in tensile tests. Its
dependency on the tungsten grade and grain orientation can be taken into
account. An example of dissipated energy density for IGP tungsten is shown in
Figure 4.25. It was calculated as the area under true stress-strain curves
obtained in Chapter 2, in the range of strain limited by the reduction of sample’s
cross-section area measured at fracture experimentally. The scatter of individual
points in Figure 4.25 gives an idea of the uncertainty of the threshold FIP.
Taking this value as an FIP threshold, and relying on the rate of increase of FIP
obtained in simulations, we could estimate that IGP tungsten is able to sustain
~100–200 thermal shocks 1 ms long at 380 MW m-2 without cracking at the
grain level. This is a preliminary upper boundary, since the information on the
threshold dissipated energy is not available in the temperature range of thermal
shock tests, where it is expected to be lower. Experimentally, small cracks were
observed in IGP tungsten exposed to 100 thermal shocks at base temperature
above 400 °C, and crack network appeared on the surface of tungsten exposed at
4. Thermomechanical fatigue of tungsten at the microscopic level
136
room base temperature [26], where the threshold FIP tends to decrease
according to Figure 4.25.
Figure 4.25. The density of energy dissipated in tensile tests of the as-received IGP tungsten.
4.7 Conclusion
The crystal plasticity model developed in Chapter 3 was implemented in the
CPFEM framework in the present chapter, driven by the interest in intragranular
heterogeneity of stress in deformed material, which is considered responsible
for crack initiation in cyclically loaded material. The sensitivity analysis has been
performed, identifying the best choice of element type and mesh density,
necessary for simulations of thermal shocks, after which the CPFEM model was
benchmarked in uniaxial tension. The advantage of CPFEM model —
consideration of the grain anisotropy — was proven useful at the microscopic
level, where the two models (CP and J2) were compared in a FE analysis to
reproduce experimentally observed delamination of thin tungsten foil, loaded in
the direction parallel to the plane of grains. Delamination appeared only in the
CPFEM analysis, due to concentration of stress at GBs caused by the crystal
anisotropy.
In simulations of thermal shocks, we have found that the tungsten surface
exhibited different mechanical response depending on the proportion between
kinematic and isotropic hardening mechanisms. The presence of kinematic
hardening resulted in the accelerated growth of FIP in the material, thus, the
ability of material (under given loading conditions) to exhibit kinematic
hardening should have negative effect with respect to the accumulation of stress
concentration and eventual crack formation under cyclic thermal shocks.
4. Thermomechanical fatigue of tungsten at the microscopic level
137
As-received IGP tungsten exposed to thermal shocks 1 ms long with power
density 190 MW m-2 experienced elastic shakedown, and its lifetime should be
assessed from the point of view of high cycle fatigue. Whereas exposure to higher
power density 380 MW m-
2 clearly caused cyclic plastic strain.
The effect of orientation of elongated grains with respect to the heated surface
was not captured by the FIP, but was predicted by another characteristic of
fatigue damage — the normal stress at GBs, which nevertheless should be taken
with care due to geometrical considerations.
Consideration of kinematic hardening contribution is shown to be essential in
the FEA of stress state in tungsten, since the accumulation of dislocation pile-ups
at GBs reduces the lifetime of plasma-facing components under conditions of
ITER. The model with mixed hardening will suit the best to this end. The
proposed method provides a qualitative measure of the impact of hardening
modes, while rigorous calculations would require dedicated experimental data
on the actual value of kinematic hardening for the studied material. In addition,
the performed analysis helps to rationalize the conditions for the appearance of
surface roughness caused by the residual plastic deformation induced by ELM
pulses.
A possible link with the energy dissipated in tensile tests is discussed, giving a
preliminary estimate of the endurance of the as-received IGP tungsten as 100–
200 ELM thermal shocks before crack formation, which agrees with the
experiment by the order of magnitude.
139
Chapter 5.
Conclusions and perspectives
5.1 Summary and conclusions
Plasma-facing components in ITER — the largest fusion device under
construction nowadays — will have to withstand severe operational conditions:
high-amplitude oscillations of temperature due to plasma instabilities (ELMs)
and high-energy neutron flux. Appearance of surface cracks in plasma-facing
components made of tungsten is considered an issue from the point of view of
stable operation of ITER, thus the qualification of tungsten has to be performed
by numerous experiments, including thermal shock tests.
In these tests samples of tungsten are exposed to short pulses of particle flux
(such as electrons) depositing power density typical for the plasma instabilities,
while the bottom face of the sample is kept at constant temperature. A series of
tests, performed on ITER-specification tungsten and recrystallized tungsten in a
range of base temperature and thermal power density, was reported in literature
[26]. Appearance of cracks, roughness, or no damage at all was observed
depending on the experimental conditions.
In the present work we have set the goal to reproduce the experiments with the
help of finite element simulations, to rationalize the different experimental
observations of the surface modification, and to investigate the mechanisms at
the microscopic scale leading to the damage accumulation in cyclically loaded
tungsten.
The material of research was the ITER-specification tungsten fabricated by
Plansee AG (Austria). According to the specification, this grade of tungsten has
elongated refined grains. On top of that, recrystallized tungsten with increased
grain size and reduced dislocation density was tested as well.
A series of tensile tests of as-received and recrystallized tungsten provided their
mechanical properties, necessary for the planned finite element simulations. A
physically-based model was used to characterize the experimental deformation
curves of tungsten in as-received and recrystallized state, and to extrapolate the
mechanical response outside the temperature- and strain rate ranges used in
tensile tests to the ITER-relevant values. The model by Kocks and Mecking, in
which plasticity is controlled by thermally-activated motion of dislocations, was
used to this end. The typical form of the model was applicable to as-received
5. Conclusions and perspectives
140
tungsten, however, an extra term had to be added to the equations in order to
take account of non-saturating stress and dislocation density observed in the
recrystallized tungsten.
Non-saturating true stress-strain curves were observed in tensile tests of
recrystallized tungsten by other authors as well, where the linear growth of
stress began around 10% of strain. This feature can indicate the presence of
deformation stage IV. Dislocation tangles and cells were observed in
recrystallized tungsten with the help of TEM at 20%–28% of strain, which can
serve as microstructural evidence of stage IV at large strain, but in order to
confirm stage IV at the onset of linear stress growth, new interrupted tensile
tests and TEM investigation would be needed.
A new method has been proposed to obtain true material properties from
experimental curves of material with low uniform elongation and early onset of
deformation instability, like as-received tungsten. The method is based on
inverse finite element analysis and is used to find the parameters of the Kocks-
Mecking model by fitting to a set of experimental curves obtained at different
temperature and strain rate. This approach respected the theoretically defined
temperature- and rate-dependency of material plasticity and resulted in a single
set of parameters, valid in a wide range of temperature and strain rate.
Since the formation of cracks is defined by stress and strain heterogeneity at the
grain level, we have to use a microscopic model in simulations, operating at the
level of grains. Crystal plasticity model was selected to this end, as long as it
properly considers crystal anisotropy — the main cause of stress heterogeneity.
An existing CP model, previously developed at UCLouvain, was improved to
properly take into account athermal stress, typical for BCC materials. Another
significant improvement of the model is the consideration of backstresses, which
play a major role in cyclic deformation, causing, for instance, the Bauschinger
effect due to kinematic hardening.
Three hypothetical material laws with different share of kinematic hardening
were parameterized to represent experimental deformation curves of ITER-
specification tungsten. The model is shown to be applicable at strain rate up to
~10–100 s-1, and temperature up to ~1700 °C, where plasticity is controlled by
thermally-activated dislocation motion, thus, covering the conditions expected
in ITER in plasma-facing components including the surface region. An original
approach to simulate thermal shocks has been proposed, in which firstly
temperature- and strain field is assessed at the macroscopic scale, where the
mesh represents the whole tungsten sample exposed to thermal shocks.
Secondly, the temperature profile and strain path typical for the heated surface
are applied at the microscopic level to a polycrystal in order to find its
mechanical response and identify the influence of the chosen material law.
Full potential of the CP model was unlocked in CPFEM simulations, in which not
only intergranular, but also intragranular heterogeneity of stress and strain can
be captured due to grain anisotropy. The important role of consideration of grain
5. Conclusions and perspectives
141
anisotropy in simulations at the microscopic level was proven in a FE analysis of
tungsten foil delamination, observed experimentally [40]. In this study,
delamination was provoked only when the crystalline nature of grains was taken
into account in CPFEM simulations, as opposed to the J2 plasticity model.
The three material laws were used in simulations of thermal shock with the help
of the crystal plasticity model coupled with the standard finite element solver
Abaqus by means of a user-defined material subroutine UMAT. The finite
element meshes represented polycrystals with either elongated or with
equiaxed grains, corresponding to as-received and recrystallized tungsten.
Correlation was found between the sample deformation state characterized in
the simulations and the surface features observed experimentally [26].
Permanent residual plastic deformation was observed in all conditions, which
could explain the appearance of surface roughness in exposed samples.
Dissipated energy density served as an FIP, whose evolution with the number of
thermal shocks was monitored. The rate of its growth provided an idea on the
material resistance to thermal shocks of a given power density. The ability of
tungsten to exhibit kinematic hardening was shown to have a negative effect on
its lifetime under conditions of cyclic thermal load, as it accelerated the growth
of fatigue indicator.
5.2 Perspectives
The ways to estimate the material resistance to thermal shocks, considered in
the present work, have their advantages and drawbacks. The fatigue indicator
can take account of backstresses, whose development is inevitable in
polycrystalline materials subjected to cyclic loading, but it fails to account for the
grain shape and orientation with respect to the thermal flux — the factors
playing an important role in thermal shock experiments. The normal stress at
grain boundaries, measured in cohesive elements placed along them, clearly
predicts a sooner failure of material with the transversal orientation of grains,
but lacks information on the backstresses due to dislocation pile-ups in the
current implementation. Developing an approach where both quantities would
play a role and interact with each other would bring the assessment of the
material resistance to thermal shocks to a more physically-justified level with a
possibility of quantitative characterisation.
It is also important to find an appropriate and physically-sound way to define the
threshold value of fatigue indicator, at which a crack is formed. As a first guess,
it should be based on the total mechanical energy dissipated in a uniaxial tensile
test, as shown in the end of Chapter 4. However, care must be taken when
comparing the energy dissipated in material in complex stress state and at
constantly evolving temperature to the value measured in isothermal uniaxial
test.
5. Conclusions and perspectives
142
For both mechanical response and the threshold fatigue indicator the effect of
texture must be taken into account. As-received tensile samples tested in two
perpendicular orientations showed different stress-strain curves at 600 °C
which means that high-temperature mechanical response can also be different.
This effect has not been included in the present model, because as-received
tungsten in the transversal orientation broke in the brittle mode and we did not
have enough experimental data for the plasticity model parameterization.
However, the threshold fatigue indicator should be parameterized in the two
sample orientations in the whole range of temperature. The main factor affecting
the threshold is the difference of grain boundaries at the sample surface which
controls the chance of a critical crack formation which can propagate into the
sample and lead to the sample fracture.
An essential step is to characterize neutron-irradiated tungsten, which will
definitely have different mechanical properties and resistance to thermal shocks.
Tensile tests and thermal shock tests of tungsten irradiated up to 1 dpa are being
performed at the moment of finalization of the thesis and will provide
information for the construction of constitutive law, the plasticity model
parameterization and its validation in simulations of thermal shocks. It is
interesting to rationalize the shift of the threshold of fatigue indicator, or the
number of thermal cycles to crack formation in neutron-irradiated tungsten.
As a side application, the model might be found useful in finite element analysis
of rotating X-ray anodes, if provided with sufficient input in terms of mechanical
test results. The anodes experience similar thermomechanical load and similar
failure modes, including the formation of surface crack network.
The procedure developed to extract true material properties with the help of
inverse finite element analysis will especially be valuable for the irradiated
tungsten, in which the deformation instability occurs at even lower strain than
in non-irradiated material.
143
Bibliography
[1] I. Uytdenhouwen, Degradation of first wall materials under ITER relevant loading conditions, Universiteit Gent, 2011.
[2] European Climate Foundation, Roadmap 2050: a practical guide to a prosperous, low-carbon Europe. Volume I: technical and economic assesment, 2010.
[3] J.L. Sawin, J. Rutovitz, F. Sverrisson, H.E. Murdock, R. Adib, Renewables 2018 Global Status Report in perspective, Paris, 2018.
[4] International Energy Agency, (n.d.). https://www.iea.org/ (accessed September 18, 2019).
[5] The Nuclear Energy Institute, (n.d.). https://www.nei.org/ (accessed September 18, 2019).
[6] Y. Zayachuk, Deuterium retention in tungsten and tungsten-tantalum alloys under high-flux plasma exposure, Universiteit Gent, 2014.
[7] R. Bonomo, Inertial Electrostatic Confinement Fusion, Univ. Wisconsin-Madison. (2014). https://iec.neep.wisc.edu/operation.php (accessed September 18, 2019).
[8] NASA/Marshall Solar Physics, (n.d.). https://solarscience.msfc.nasa.gov/interior.shtml (accessed September 18, 2019).
[9] D.R. Williams, Earth Fact Sheet, NASA/Goddard Sp. Flight Cent. (2019). https://nssdc.gsfc.nasa.gov/planetary/factsheet/earthfact.html (accessed September 18, 2019).
[10] P. Grigorev, Assessment of Retention of Plasma Components in Tungsten under High Flux Plasma Exposure: Multi-Scale Modelling Approach, Universiteit Gent, 2017.
[11] P.-H. Rebut, The JET preliminary tritium experiment, Plasma Phys. Control. Fusion. 34 (1992) 1749–1758. doi:10.1088/0741-3335/34/13/002.
[12] 60 Years of Progress, (n.d.). https://www.iter.org/sci/BeyondITER (accessed September 18, 2019).
[13] 6.5-minute pulse in Tore Supra, (2003). https://www.iter.org/proj/itermilestones#18 (accessed September 18, 2019).
[14] X. Gong, EAST Achieves 100s World Record Steady-state High Performance Plasma, (2017). http://english.cas.cn/head/201707/t20170705_179373.shtml
Bibliography
144
(accessed September 18, 2019).
[15] I. Milch, Successful second round of experiments with Wendelstein 7-X, (2018). https://www.ipp.mpg.de/4550215/11_18 (accessed September 18, 2019).
[16] Q4-24: Close up the cryostat, (2019). https://www.iter.org/proj/itermilestones#166 (accessed September 18, 2019).
[17] Q4-25: First Plasma!, (2019). https://www.iter.org/proj/itermilestones#168 (accessed September 18, 2019).
[18] G. McCracken, P. Stott, Fusion. The Energy of the Universe, 2nd ed., Elsevier Inc., 2013.
[19] J. Paméla, F. Romanelli, M.L. Watkins, A. Lioure, G. Matthews, V. Philipps, T. Jones, A. Murari, A. Géraud, F. Crisanti, R. Kamendje, The JET programme in support of ITER, Fusion Eng. Des. 82 (2007) 590–602. doi:10.1016/j.fusengdes.2007.03.003.
[20] T. Hirai, S. Panayotis, V.R. Barabash, C. Amzallag, F. Escourbiac, A. Durocher, M. Merola, J. Linke, T. Loewenhoff, G. Pintsuk, M. Wirtz, I. Uytdenhouwen, Use of tungsten material for the ITER divertor, Nucl. Mater. Energy. 9 (2016) 616–622. doi:10.1016/j.nme.2016.07.003.
[21] R.A. Pitts, S. Bardin, B. Bazylev, M.A. van den Berg, P. Bunting, S. Carpentier-Chouchana, J.W. Coenen, Y. Corre, R. Dejarnac, F. Escourbiac, J. Gaspar, J.P. Gunn, T. Hirai, S.-H. Hong, J. Horacek, D. Iglesias, M. Komm, K. Krieger, C. Lasnier, G.F. Matthews, T.W. Morgan, S. Panayotis, S. Pestchanyi, A. Podolnik, R.E. Nygren, D.L. Rudakov, G. De Temmerman, P. Vondracek, J.G. Watkins, Physics conclusions in support of ITER W divertor monoblock shaping, Nucl. Mater. Energy. 12 (2017) 60–74. doi:10.1016/j.nme.2017.03.005.
[22] T. Hirai, S. Carpentier-Chouchana, F. Escourbiac, S. Panayotis, A. Durocher, L. Ferrand, M. Garcia-Martinez, J.P. Gunn, V. Komarov, M. Merola, R.A. Pitts, G. De Temmerman, Design optimization of the ITER tungsten divertor vertical targets, Fusion Eng. Des. 127 (2018) 66–72. doi:10.1016/j.fusengdes.2017.12.007.
[23] H. Greuner, B. Böswirth, M. Lipa, M. Missirlian, M. Richou, Results of high heat flux qualification tests of W monoblock components for WEST, Phys. Scr. T170 (2017) 014001.
[24] M.R. Wade, Physics and engineering issues associated with edge localized mode control in ITER, Fusion Eng. Des. 84 (2009) 178–185. doi:10.1016/j.fusengdes.2009.01.063.
[25] G. Federici, P. Andrew, P. Barabaschi, J. Brooks, R. Doerner, A. Geier, A. Herrmann, G. Janeschitz, K. Krieger, A. Kukushkin, A. Loarte, R. Neu, G. Saibene, M. Shimada, G. Strohmayer, M. Sugihara, Key ITER plasma edge and plasma–material interaction issues, J. Nucl. Mater. 313–316 (2003) 11–22. doi:10.1016/S0022-3115(02)01327-2.
Bibliography
145
[26] M. Wirtz, J. Linke, T. Loewenhoff, G. Pintsuk, I. Uytdenhouwen, Thermal shock tests to qualify different tungsten grades as plasma facing material, Phys. Scr. T167 (2016) 014015. doi:10.1088/0031-8949/T167/1/014015.
[27] R.L. Heath, Handbook of Chemistry and Physics, Chemical Rubber Publ., New York, 1969.
[28] G.D. Rieck, Tungsten and Its Compounds, Pergamon Press, Oxford, 1967.
[29] G. Pintsuk, Tungsten as a plasma-facing material, in: Compr. Nucl. Mater., Elsevier Inc., Julich, 2012: pp. 551–581. doi:10.1016/B978-0-08-056033-5.00118-X.
[30] O. Gruber, A.C.C. Sips, R. Dux, T. Eich, J.C. Fuchs, A. Herrmann, A. Kallenbach, C.F. Maggi, R. Neu, T. Pütterich, J. Schweinzer, J. Stober, Compatibility of ITER scenarios with full tungsten wall in ASDEX Upgrade, Nucl. Fusion. 49 (2009) 115014. doi:10.1088/0029-5515/49/11/115014.
[31] T. Hirai, F. Escourbiac, V.R. Barabash, A. Durocher, A. Fedosov, L. Ferrand, T. Jokinen, V. Komarov, M. Merola, S. Carpentier-Chouchana, N. Arkhipov, V. Kuznetcov, A. Volodin, S. Suzuki, K. Ezato, Y. Seki, B. Riccardi, M. Bednarek, P. Gavila, Status of technology R&D for the ITER tungsten divertor monoblock, J. Nucl. Mater. 463 (2015) 1248–1251. doi:10.1016/j.jnucmat.2014.12.027.
[32] A. Dubinko, Plastic Deformation of Tungsten under Fusion-Plasma Exposure Conditions, Universiteit Gent, 2018.
[33] E. Guk, N. Kalkan, The importance of nuclear energy for the expansion of world’s energy demand, Adv. Energy Res. 3 (2015) 71–80. doi:10.12989/eri.2015.3.2.071.
[34] G. Pintsuk, M. Bednarek, P. Gavila, S. Gerzoskovitz, J. Linke, P. Lorenzetto, B. Riccardi, F. Escourbiac, Characterization of ITER tungsten qualification mock-ups exposed to high cyclic thermal loads, Fusion Eng. Des. 98–99 (2015) 1384–1388. doi:10.1016/j.fusengdes.2015.01.037.
[35] ASM Handbook Committee, Metals Handbook, 10th ed., 1995.
[36] R. Lowrie, A.M. Gonas, Single-Crystal Elastic Properties of Tungsten from 24° to 1800°C, J. Appl. Phys. 38 (1967) 4505. doi:10.1063/1.1709158.
[37] J.W. Davis, V.R. Barabash, A. Makhankov, L. Plöchl, K.T. Slattery, Assessment of tungsten for use in the ITER plasma facing components, J. Nucl. Mater. 258–263 (1998) 308–312. doi:10.1016/S0022-3115(98)00285-2.
[38] V. Nikolić, S. Wurster, D. Firneis, R. Pippan, Improved fracture behavior and microstructural characterization of thin tungsten foils, Nucl. Mater. Energy. 9 (2016) 181–188. doi:10.1016/j.nme.2016.06.003.
[39] D. Terentyev, J. Riesch, S. Lebediev, T. Khvan, A. Dubinko, A. Bakaeva, Strength and deformation mechanism of tungsten wires exposed to high temperature annealing: Impact of potassium doping, Int. J. Refract. Met. Hard Mater. 76 (2018) 226–233. doi:10.1016/j.ijrmhm.2018.07.002.
Bibliography
146
[40] V. Nikolić, S. Wurster, D. Firneis, R. Pippan, Fracture toughness evaluation of UFG tungsten foil, Int. J. Refract. Met. Hard Mater. 76 (2018) 214–225. doi:10.1016/j.ijrmhm.2018.06.008.
[41] B. Gludovatz, S. Wurster, A. Hoffmann, R. Pippan, Fracture toughness of polycrystalline tungsten alloys, Int. J. Refract. Met. Hard Mater. 28 (2010) 674–678. doi:10.1016/j.ijrmhm.2010.04.007.
[42] B. Gludovatz, S. Wurster, T. Weingärtner, A. Hoffmann, R. Pippan, Influence of impurities on the fracture behaviour of tungsten, Philos. Mag. 91 (2011) 3006–3020. doi:10.1080/14786435.2011.558861.
[43] C. Ren, Z.Z. Fang, M. Koopman, B. Butler, J. Paramore, S. Middlemas, Methods for improving ductility of tungsten - A review, Int. J. Refract. Met. Hard Mater. 75 (2018) 170–183. doi:10.1016/j.ijrmhm.2018.04.012.
[44] D. Rupp, S.M. Weygand, Loading rate dependence of the fracture toughness of polycrystalline tungsten, J. Nucl. Mater. 417 (2011) 477–480. doi:10.1016/j.jnucmat.2010.12.118.
[45] E. Gaganidze, D. Rupp, J. Aktaa, Fracture behaviour of polycrystalline tungsten, J. Nucl. Mater. 446 (2014) 240–245. doi:10.1016/j.jnucmat.2013.11.001.
[46] ASTM Int., E399-12e3 Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness KIC of Metallic Materials, 2012. doi:10.1520/E0399-12E03.2.
[47] C. Yin, D. Terentyev, T. Pardoen, R.H. Petrov, Z. Tong, Ductile to brittle transition in ITER specification tungsten assessed by combined fracture toughness and bending tests analysis, Mater. Sci. Eng. A. 750 (2019) 20–30. doi:10.1016/j.msea.2019.02.028.
[48] S. Wurster, B. Gludovatz, R. Pippan, High temperature fracture experiments on tungsten-rhenium alloys, Int. J. Refract. Met. Hard Mater. 28 (2010) 692–697. doi:10.1016/j.ijrmhm.2010.03.002.
[49] A. Elsas, T. Zimmer, Höhere Belastung von Drehanodenröhren durch Verwendung von legierten Anoden, RöFo - Fortschritte Auf Dem Gebiet Der Röntgenstrahlen Und Der Bildgeb. Verfahren. 97 (1962) 511–514. doi:10.1055/s-0029-1227099.
[50] R. Behling, Modern Diagnostic X-Ray Sources, CRC Press, 2015. doi:10.1201/b18655.
[51] A. Hasegawa, M. Fukuda, K. Yabuuchi, S. Nogami, Neutron irradiation effects on the microstructural development of tungsten and tungsten alloys, J. Nucl. Mater. 471 (2016) 175–183. doi:10.1016/j.jnucmat.2015.10.047.
[52] M. Fukuda, T. Tabata, A. Hasegawa, S. Nogami, T. Muroga, Strain rate dependence of tensile properties of tungsten alloys for plasma-facing components in fusion reactors, Fusion Eng. Des. 109–111 (2016) 1674–1677. doi:10.1016/j.fusengdes.2015.10.032.
[53] M. Faleschini, Severe Plastic Deformation of Tungsten Alloys and its Influence on Fracture Behaviour, Erich Schmid Institut für
Bibliography
147
Materialwissenschaft der Österreichischen Akademie der Wissenschaften, 2006.
[54] B.G. Butler, J.D. Paramore, J.P. Ligda, C. Ren, Z.Z. Fang, S.C. Middlemas, K.J. Hemker, Mechanisms of deformation and ductility in tungsten – A review, Int. J. Refract. Met. Hard Mater. 75 (2018) 248–261. doi:10.1016/j.ijrmhm.2018.04.021.
[55] J. Reiser, S. Wurster, J. Hoffmann, S. Bonk, C. Bonnekoh, D. Kiener, R. Pippan, A. Hoffmann, M. Rieth, Ductilisation of tungsten (W) through cold-rolling: R-curve behaviour, Int. J. Refract. Met. Hard Mater. 58 (2016) 22–33. doi:10.1016/j.ijrmhm.2016.03.006.
[56] H. Sheng, G. Van Oost, E.E. Zhurkin, D. Terentyev, V.I. Dubinko, I. Uytdenhouwen, J. Vleugels, High temperature strain hardening behavior in double forged and potassium doped tungsten, J. Nucl. Mater. 444 (2014) 214–219. doi:10.1016/j.jnucmat.2013.09.057.
[57] C. Yin, D. Terentyev, T. Pardoen, A. Bakaeva, R.H. Petrov, S. Antusch, M. Rieth, M. Vilémová, J. Matějíček, T. Zhang, Tensile properties of baseline and advanced tungsten grades for fusion applications, Int. J. Refract. Met. Hard Mater. 75 (2018) 153–162. doi:10.1016/j.ijrmhm.2018.04.003.
[58] S. Panayotis, T. Hirai, V.R. Barabash, A. Durocher, F. Escourbiac, J. Linke, T. Loewenhoff, M. Merola, G. Pintsuk, I. Uytdenhouwen, M. Wirtz, Self-castellation of tungsten monoblock under high heat flux loading and impact of material properties, Nucl. Mater. Energy. 12 (2017) 200–204. doi:10.1016/j.nme.2016.10.025.
[59] J. Habainy, S. Iyengar, Y. Lee, Y. Dai, Fatigue behavior of rolled and forged tungsten at 25°, 280° and 480 °C, J. Nucl. Mater. 465 (2015) 438–447. doi:10.1016/j.jnucmat.2015.06.032.
[60] T. Shen, Y. Dai, Y. Lee, Microstructure and tensile properties of tungsten at elevated temperatures, J. Nucl. Mater. 468 (2016) 348–354. doi:10.1016/j.jnucmat.2015.09.057.
[61] A. Elsas, T. Zimmer, Belastbarkeit von Drehanodenröhren, RöFo - Fortschritte Auf Dem Gebiet Der Röntgenstrahlen Und Der Bildgeb. Verfahren. 101 (1964) 420–425. doi:10.1055/s-0029-1227575.
[62] A. Müller, A Spinning Target X-ray Generator, Nature. 124 (1929) 128–128. doi:10.1038/124128a0.
[63] R.E. Clay, A 5-kilowatt X-ray generator with a spinning target, Proc. Phys. Soc. 46 (1934) 703–712. doi:10.1088/0959-5309/46/5/312.
[64] S. Whitaker, X-Ray Anode Surface Temperatures: The Effect Of Volume Heating, Med. Imaging II. 914 (1988) 565. doi:10.1117/12.968682.
[65] A. Plankensteiner, P. Rödhammer, Finite Element Analysis of X-Ray Targets, Proc. 15th Int. Plansee Semin. (2001) 9–22.
[66] H. Greuner, B. Boeswirth, J. Boscary, P. McNeely, High heat flux facility GLADIS:. Operational characteristics and results of W7-X pre-series target tests, J. Nucl. Mater. 367-370 B (2007) 1444–1448. doi:10.1016/j.jnucmat.2007.04.004.
Bibliography
148
[67] T.W. Morgan, J.J. Zielinski, B.J. Hensen, H.Y. Xu, L. Marot, G. De Temmerman, Reduced damage threshold for tungsten using combined steady state and transient sources, J. Nucl. Mater. 438 (2013) 784–787. doi:10.1016/j.jnucmat.2013.01.168.
[68] V. Kuznetsov, A. Gorbenko, V. Davydov, A. Kokoulin, A. Komarov, I. Mazul, B. Mudyugin, I. Ovchinnikov, N. Stepanov, R. Rulev, A. Volodin, Status of the IDTF high-heat-flux test facility, Fusion Eng. Des. 89 (2014) 955–959. doi:10.1016/j.fusengdes.2014.04.064.
[69] Z. Sun, Q. Li, W. Wang, J.C. Wang, X. Wang, R. Wei, C. Xie, G. nan Luo, T. Hirai, F. Escourbiac, S. Panayotis, Post examination of tungsten monoblocks subjected to high heat flux tests of ITER full-tungsten divertor qualification program, Fusion Eng. Des. 121 (2017) 60–69. doi:10.1016/j.fusengdes.2017.06.009.
[70] I. Uytdenhouwen, M. Decréton, T. Hirai, J. Linke, G. Pintsuk, G. Van Oost, Influence of recrystallization on thermal shock resistance of various tungsten grades, J. Nucl. Mater. 363–365 (2007) 1099–1103. doi:10.1016/j.jnucmat.2007.01.146.
[71] M. Wirtz, J. Linke, T. Loewenhoff, G. Pintsuk, I. Uytdenhouwen, Transient heat load challenges for plasma-facing materials during long-term operation, Nucl. Mater. Energy. 12 (2017) 148–155. doi:10.1016/j.nme.2016.12.024.
[72] V.A. Makhlaj, I.E. Garkusha, N.N. Aksenov, B. Bazylev, I. Landman, J. Linke, S. V. Malykhin, A.T. Pugachov, M.J. Sadowski, E. Skladnik-Sadowska, M. Wirtz, Tungsten damage and melt losses under plasma accelerator exposure with ITER ELM relevant conditions, Phys. Scr. T159 (2014) 014024. doi:10.1088/0031-8949/2014/T159/014024.
[73] R. Courant, Variational methods for the solution of problems of equilibrium and vibrations, Bull. Am. Math. Soc. 49 (1943) 1–24. doi:10.1090/S0002-9904-1943-07818-4.
[74] O.C. Zienkiewicz, R.L. Taylor, J.Z. Zhu, The Finite Element Method: Its Basis and Fundamentals, 6th ed., Butterworth-Heinemann, Oxford, 2005.
[75] F. Roters, P. Eisenlohr, T.R. Bieler, D. Raabe, Crystal Plasticity Finite Element Methods, 2010. doi:10.1002/9783527631483.
[76] Dassault Systèmes Simulia Corp., Abaqus Theory Guide, n.d.
[77] M. Kuna, Finite Elements in Fracture Mechanics. Theory - Numerics - Applications, Springer Netherlands, Dordrecht, 2013. doi:10.1007/978-94-007-6680-8_4.
[78] M. Li, E. Werner, J.-H. You, Fracture mechanical analysis of tungsten armor failure of a water-cooled divertor target, Fusion Eng. Des. 89 (2014) 2716–2725. doi:10.1016/j.fusengdes.2014.07.011.
[79] M. Li, J.-H. You, Interpretation of the deep cracking phenomenon of tungsten monoblock targets observed in high-heat-flux fatigue tests at 20 MW/m2, Fusion Eng. Des. 101 (2015) 1–8. doi:10.1016/j.fusengdes.2015.09.008.
Bibliography
149
[80] M. Li, J.-H. You, Design options to mitigate deep cracking of tungsten armor, Fusion Eng. Des. 124 (2017) 468–472. doi:10.1016/j.fusengdes.2017.01.015.
[81] S. Nogami, W.H. Guan, T. Hattori, K. James, A. Hasegawa, Improved structural strength and lifetime of monoblock divertor targets by using doped tungsten alloys under cyclic high heat flux loading, Phys. Scr. T170 (2017) 014011. doi:10.1088/1402-4896/aa864d.
[82] M. Fukuda, S. Nogami, W. Guan, A. Hasegawa, T. Muroga, Analysis of the temperature and thermal stress in pure tungsten monoblock during heat loading and the influences of alloying and dispersion strengthening on these responses, Fusion Eng. Des. 107 (2016) 44–50. doi:10.1016/j.fusengdes.2016.04.013.
[83] S. Huang, S. Liu, Numerical Analysis of Fatigue Behavior of ITER-Like Monoblock Divertor Interlayer Under Coupled Heat Loads, J. Fusion Energy. 37 (2018) 177–186. doi:10.1007/s10894-018-0164-3.
[84] M. Fursdon, T. Barrett, F. Domptail, L.M. Evans, N. Luzginova, N.H. Greuner, J.-H. You, M. Li, M. Richou, F. Gallay, E. Visca, The development and testing of the thermal break divertor monoblock target design delivering 20 MW m-2 heat load capability, Phys. Scr. T170 (2017) 014042. doi:10.1088/1402-4896/aa8c8e.
[85] S. Panayotis, T. Hirai, V.R. Barabash, C. Amzallag, F. Escourbiac, A. Durocher, V. Komarov, J.M. Martinez, M. Merola, Fracture modes of ITER tungsten divertor monoblock under stationary thermal loads, Fusion Eng. Des. 125 (2017) 256–262. doi:10.1016/j.fusengdes.2017.08.009.
[86] S.D. Antolovich, R.W. Armstrong, Plastic strain localization in metals: origins and consequences, Prog. Mater. Sci. 59 (2014) 1–160. doi:10.1016/j.pmatsci.2013.06.001.
[87] S.L. Zang, M.G. Lee, L. Sun, J.H. Kim, Measurement of the Bauschinger behavior of sheet metals by three-point bending springback test with pre-strained strips, Int. J. Plast. 59 (2014) 84–107. doi:10.1016/j.ijplas.2014.03.015.
[88] J.D.H. Paul, R. Hoppe, F. Appel, On the Bauschinger effect in TiAl alloys, Acta Mater. 104 (2016) 101–108. doi:10.1016/j.actamat.2015.10.036.
[89] W.F. Hosford, Mechanical behavior of materials, 2nd ed., Cambridge University Press, Cambridge, UK, 2010.
[90] S.K. Paul, S. Sivaprasad, S. Dhar, S. Tarafder, Key issues in cyclic plastic deformation: Experimentation, Mech. Mater. 43 (2011) 705–720. doi:10.1016/j.mechmat.2011.07.011.
[91] H. Mecking, U.F. Kocks, Kinetics of Flow and Strain-hardening, Acta Metall. 29 (1981) 1865–1875. doi:Doi 10.1016/0001-6160(81)90112-7.
[92] A. Abel, Historical perspectives and some of the main features of the Bauschinger effect, Mater. Forum. 10 (1987) 11–26.
[93] A.A. Mamun, R.J. Moat, J. Kelleher, P.J. Bouchard, Origin of the Bauschinger effect in a polycrystalline material, Mater. Sci. Eng. A. 707 (2017) 576–
Bibliography
150
584. doi:10.1016/j.msea.2017.09.091.
[94] G. Masing, Zur Heynschen Theorie der Verfestigung der Metalle durch verborgene elastische Spannungen (= on Heyn’s theory of stiffening of metals by hidden elastic stress), Wissenschaftliche Veroffentlichungen Asu Dem Siemens-Konzern. 3 (1923).
[95] L.M. Brown, W.M. Stobbs, The work-hardening of copper-silica, Philos. Mag. 23 (1971) 1185–1199. doi:10.1080/14786437108217405.
[96] J.D. Atkinson, L.M. Brown, W.M. Stobbs, The work-hardening of copper-silica: IV. The Bauschinger effect and plastic relaxation, Philos. Mag. 30 (1974) 1247–1280. doi:10.1080/14786437408207280.
[97] J. da Costa Teixeira, L. Bourgeois, C.W. Sinclair, C.R. Hutchinson, The effect of shear-resistant, plate-shaped precipitates on the work hardening of Al alloys: Towards a prediction of the strength–elongation correlation, Acta Mater. 57 (2009) 6075–6089. doi:10.1016/j.actamat.2009.08.034.
[98] J.K. Mahato, P.S. De, A. Sarkar, A. Kundu, P.C. Chakraborti, Effect of deformation mode and grain size on Bauschinger behavior of annealed copper, Int. J. Fatigue. 83 (2016) 42–52. doi:10.1016/j.ijfatigue.2015.04.023.
[99] J.H. Kim, D. Kim, F. Barlat, M.G. Lee, Crystal plasticity approach for predicting the Bauschinger effect in dual-phase steels, Mater. Sci. Eng. A. 539 (2012) 259–270. doi:10.1016/j.msea.2012.01.092.
[100] D. Hull, D.J. Bacon, Introduction to dislocations, 4th ed., Butterworth-Heinemann, Oxford, 2001.
[101] R.D. McGinty, Multiscale Representation of Polycrystalline Inelasticity, Georgia Institute of Technology, 2001.
[102] F. Roters, P. Eisenlohr, L. Hantcherli, D.D. Tjahjanto, T.R. Bieler, D. Raabe, Overview of constitutive laws, kinematics, homogenization and multiscale methods in crystal plasticity finite-element modeling: Theory, experiments, applications, Acta Mater. 58 (2010) 1152–1211. doi:10.1016/j.actamat.2009.10.058.
[103] V.V.C. Wan, D.W. Maclachlan, F.P.E. Dunne, A stored energy criterion for fatigue crack nucleation in polycrystals, Int. J. Fatigue. 68 (2014) 90–102. doi:10.1016/j.ijfatigue.2014.06.001.
[104] T.R. Bieler, P. Eisenlohr, F. Roters, D. Kumar, D.E. Mason, M.A. Crimp, D. Raabe, The role of heterogeneous deformation on damage nucleation at grain boundaries in single phase metals, Int. J. Plast. 25 (2009) 1655–1683. doi:10.1016/j.ijplas.2008.09.002.
[105] F.P.E. Dunne, A.J. Wilkinson, R. Allen, Experimental and computational studies of low cycle fatigue crack nucleation in a polycrystal, Int. J. Plast. 23 (2007) 273–295. doi:10.1016/j.ijplas.2006.07.001.
[106] B. Lin, L.G. Zhao, J. Tong, A crystal plasticity study of cyclic constitutive behaviour, crack-tip deformation and crack-growth path for a polycrystalline nickel-based superalloy, Eng. Fract. Mech. 78 (2011) 2174–2192. doi:10.1016/j.engfracmech.2011.04.006.
Bibliography
151
[107] D.F. Li, R.A. Barrett, P.E. O’Donoghue, C.J. Hyde, N.P. O’Dowd, S.B. Leen, Micromechanical finite element modelling of thermo-mechanical fatigue for P91 steels, Int. J. Fatigue. 87 (2016) 192–202. doi:10.1016/j.ijfatigue.2015.11.025.
[108] Y. Estrin, H. Mecking, A unified phenomenological description of work hardening and creep based on one-parameter models, Acta Metall. 32 (1984) 57–70. doi:10.1016/0001-6160(84)90202-5.
[109] S. Kok, A.J. Beaudoin, D.A. Tortorelli, On the development of stage IV hardening using a model based on the mechanical threshold, Acta Mater. 50 (2002) 1653–1667. doi:10.1016/S1359-6454(02)00002-2.
[110] G. Angella, R. Donnini, M. Maldini, D. Ripamonti, Combination between Voce formalism and improved Kocks-Mecking approach to model small strains of flow curves at high temperatures, Mater. Sci. Eng. A. 594 (2014) 381–388. doi:10.1016/j.msea.2013.11.088.
[111] M. Delincé, Y. Bréchet, J.D. Embury, M.G.D. Geers, P.J. Jacques, T. Pardoen, Structure-property optimization of ultrafine-grained dual-phase steels using a microstructure-based strain hardening model, Acta Mater. 55 (2007) 2337–2350. doi:10.1016/j.actamat.2006.11.029.
[112] E.I. Galindo-Nava, P.E.J. Rivera-Díaz-del-Castillo, Modelling plastic deformation in BCC metals: Dynamic recovery and cell formation effects, Mater. Sci. Eng. A. 558 (2012) 641–648. doi:10.1016/j.msea.2012.08.068.
[113] O. Bouaziz, Revisited storage and dynamic recovery of dislocation density evolution law: Toward a generalized Kocks-Mecking model of strain-hardening, Adv. Eng. Mater. 14 (2012) 759–761. doi:10.1002/adem.201200083.
[114] I.J. Beyerlein, C.N. Tomé, A dislocation-based constitutive law for pure Zr including temperature effects, Int. J. Plast. 24 (2008) 867–895. doi:10.1016/j.ijplas.2007.07.017.
[115] D. Terentyev, X. Xiao, A. Dubinko, A. Bakaeva, H. Duan, Dislocation-mediated strain hardening in tungsten: Thermo-mechanical plasticity theory and experimental validation, J. Mech. Phys. Solids. 85 (2015) 1–15. doi:10.1016/j.jmps.2015.08.015.
[116] W. Zhou, R. Apkarian, Z.L. Wang, D. Joy, Fundamentals of Scanning Electron Microscopy (SEM), in: Scanning Microsc. Nanotechnol., Springer New York, New York, NY, 2006: pp. 1–40. doi:10.1007/978-0-387-39620-0_1.
[117] B.L. Adams, S.R. Kalidindi, D.T. Fullwood, Electron Backscatter Diffraction Microscopy and Basic Stereology, in: Microstruct. Sensitive Des. Perform. Optim., Elsevier, 2013: pp. 341–371. doi:10.1016/B978-0-12-396989-7.00016-2.
[118] A. Bakaeva, Deuterium and Helium Retention in ITER Specification Tungsten before and after Plastic Deformation, Ghent University, 2018.
[119] R. Villari, V. Barabash, F. Escourbiac, L. Ferrand, T. Hirai, V. Komarov, M. Loughlin, M. Merola, F. Moro, L. Petrizzi, S. Podda, E. Polunovsky, G.
Bibliography
152
Brolatti, Nuclear analysis of the ITER full-tungsten divertor, Fusion Eng. Des. 88 (2013) 2006–2010. doi:10.1016/j.fusengdes.2013.02.156.
[120] A. Zinovev, D. Terentyev, A. Dubinko, L. Delannay, Constitutive law for thermally-activated plasticity of recrystallized tungsten, J. Nucl. Mater. 496 (2017) 325–332. doi:10.1016/j.jnucmat.2017.09.044.
[121] J. Du, Y. Yuan, M. Wirtz, J. Linke, W. Liu, H. Greuner, FEM study of recrystallized tungsten under ELM-like heat loads, J. Nucl. Mater. 463 (2015) 219–222. doi:10.1016/j.jnucmat.2014.10.044.
[122] C.C. Zhu, Y.T. Song, X.B. Peng, Y.P. Wei, X. Mao, W.X. Li, X.Y. Qian, The dynamical mechanical properties of tungsten under compression at working temperature range of divertors, J. Nucl. Mater. 469 (2016) 120–124. doi:10.1016/j.jnucmat.2015.11.045.
[123] A. Giannattasio, Z. Yao, E. Tarleton, S.G. Roberts, Brittle–ductile transitions in polycrystalline tungsten, Philos. Mag. 90 (2010) 3947–3959. doi:10.1080/14786435.2010.502145.
[124] M. Knezevic, I.J. Beyerlein, M.L. Lovato, C.N. Tomé, A.W. Richards, R.J. McCabe, A strain-rate and temperature dependent constitutive model for BCC metals incorporating non-Schmid effects: Application to tantalum-tungsten alloys, Int. J. Plast. 62 (2014) 72–92. doi:10.1016/j.ijplas.2014.07.007.
[125] H. Lim, C.C. Battaile, J.L. Brown, C.R. Weinberger, Physically-based strength model of tantalum incorporating effects of temperature, strain rate and pressure, Model. Simul. Mater. Sci. Eng. 24 (2016) 55018. doi:10.1088/0965-0393/24/5/055018.
[126] J. Wang, G. Zhao, L. Chen, J. Li, A comparative study of several constitutive models for powder metallurgy tungsten at elevated temperature, Mater. Des. 90 (2016) 91–100. doi:10.1016/j.matdes.2015.10.114.
[127] G.Z. Voyiadjis, F.H. Abed, Microstructural based models for bcc and fcc metals with temperature and strain rate dependency, Mech. Mater. 37 (2005) 355–378. doi:10.1016/j.mechmat.2004.02.003.
[128] E. Voce, The Relationship Between Stress and Strain for Homogeneous Deformation, J. Inst. Met. 74 (1948) 537–562.
[129] F.B. Prinz, A.S. Argon, The Evolution of Plastic Resistance in Large Strain Plastic Flow of Single Phase Subgrain Forming Metals, Acta Metall. Mater. 32 (1984) 1021–1028.
[130] M. Mahler, J. Aktaa, Approach for Determining Fracture Mechanical Properties from Tests on Small Size Specimens at Room Temperature, Procedia Mater. Sci. 3 (2014) 434–439. doi:10.1016/j.mspro.2014.06.073.
[131] F. Hajy Akbary, M.J. Santofimia, J. Sietsma, Elastic Strain Measurement of Miniature Tensile Specimens, Exp. Mech. 54 (2014) 165–173. doi:10.1007/s11340-013-9785-7.
[132] K. Li, J. Peng, C. Zhou, Construction of whole stress-strain curve by small punch test and inverse finite element, Results Phys. 11 (2018) 440–448.
Bibliography
153
doi:10.1016/j.rinp.2018.09.024.
[133] J. Kajberg, G. Lindkvist, Characterisation of materials subjected to large strains by inverse modelling based on in-plane displacement fields, Int. J. Solids Struct. 41 (2004) 3439–3459. doi:10.1016/j.ijsolstr.2004.02.021.
[134] D. Yao, L. Cai, C. Bao, A new approach on necking constitutive relationships of ductile materials at elevated temperatures, Chinese J. Aeronaut. 29 (2016) 1626–1634. doi:10.1016/j.cja.2016.10.011.
[135] P. Knysh, Y.P. Korkolis, Identification of the post-necking hardening response of rate- and temperature-dependent metals, Int. J. Solids Struct. 115–116 (2017) 149–160. doi:10.1016/j.ijsolstr.2017.03.012.
[136] H. Liu, Y. Shen, S. Yang, P. Zheng, L. Zhang, A comprehensive solution to miniaturized tensile testing: Specimen geometry optimization and extraction of constitutive behaviors using inverse FEM procedure, Fusion Eng. Des. 121 (2017) 188–197. doi:10.1016/j.fusengdes.2017.07.016.
[137] E. Burman, D. Elfverson, P. Hansbo, M.G. Larson, K. Larsson, Shape optimization using the cut finite element method, Comput. Methods Appl. Mech. Eng. 328 (2018) 242–261. doi:10.1016/j.cma.2017.09.005.
[138] C. Geuzaine, J.-F. Remacle, Gmsh: A 3-D finite element mesh generator with built-in pre- and post-processing facilities, Int. J. Numer. Methods Eng. 79 (2009) 1309–1331. doi:10.1002/nme.2579.
[139] ASTM Int., E8/E8M-16a Standard Test Methods for Tension Testing of Metallic Materials, 2016. http://www.astm.org/Standards/E8.htm.
[140] W.H. Chen, Necking of a bar, Int. J. Solids Struct. 7 (1971) 685–717. doi:10.1016/0020-7683(71)90088-6.
[141] Z.L. Zhang, M. Hauge, J. Ødegård, C. Thaulow, Determining material true stress-strain curve from tensile specimens with rectangular cross-section, Int. J. Solids Struct. 36 (1999) 3497–3516. doi:10.1016/S0020-7683(98)00153-X.
[142] J.A. Nelder, R. Mead, A Simplex Method for Function Minimization, Comput. J. 7 (1965) 308–313. doi:10.1093/comjnl/7.4.308.
[143] S. Bihorel, M. Baudin, neldermead: R Port of the “Scilab” Neldermead Module, (2018). https://cran.r-project.org/package=neldermead (accessed September 18, 2019).
[144] K. Ono, Temperature Dependence of Dispersed Barrier Hardening, J. Appl. Phys. 39 (1968) 1803–1806. doi:10.1063/1.1656434.
[145] M. Knezevic, R.J. McCabe, C.N. Tomé, R.A. Lebensohn, S.R. Chen, C.M. Cady, G.T. Gray III, B. Mihaila, Modeling mechanical response and texture evolution of α-uranium as a function of strain rate and temperature using polycrystal plasticity, Int. J. Plast. 43 (2013) 70–84. doi:10.1016/j.ijplas.2012.10.011.
[146] A.M. Lennon, K.T. Ramesh, The thermoviscoplastic response of polycrystalline tungsten in compression, Mater. Sci. Eng. A. 276 (2000) 9–21. doi:10.1016/S0921-5093(99)00517-1.
Bibliography
154
[147] I. Kovács, The mechanism of the work-hardening in F.C.C. metals, Acta Metall. 15 (1967) 1731–1736. doi:10.1016/0001-6160(67)90064-8.
[148] P. Les, H.P. Stuwe, M. Zehetbauer, Hardening and strain rate sensitivity in stage IV of deformation in f.c.c. and b.c.c. metals, Mater. Sci. Eng. A. 234–236 (1997) 453–455.
[149] A.S. Argon, P. Haasen, A New Mechanism of Work Hardening in the Late Stages of Large Strain Plastic Flow in F.C.C. and Diamond Cubic Crystals, Acta Metall. Mater. 41 (1993) 3289–3306. doi:10.1016/0956-7151(93)90058-Z.
[150] Y. Estrin, L.S. Tóth, A. Molinari, Y. Bréchet, A dislocation-based model for all hardening stages in large strain deformation, Acta Mater. 46 (1998) 5509–5522. doi:10.1016/s1359-6454(98)00196-7.
[151] C.Y. Chiem, W.S. Lee, The influence of dynamic shear loading on plastic deformation and microstructure of tungsten single crystals, Mater. Sci. Eng. A. 186 (1994) 43–50. doi:10.1016/0921-5093(94)90329-8.
[152] A. Dubinko, D. Terentyev, A. Bakaeva, K. Verbeken, M. Wirtz, M. Hernández-Mayoral, Evolution of plastic deformation in heavily deformed and recrystallized tungsten of ITER specification studied by TEM, Int. J. Refract. Met. Hard Mater. 66 (2017) 105–115. doi:http://dx.doi.org/10.1016/j.ijrmhm.2017.03.004.
[153] J.R. Stephens, Dislocation Structures in Single-Crystal Tungsten and Tungsten Alloys, Metall. Trans. 1 (1970) 1293–1301. doi:10.1007/BF02900246.
[154] G. Lemoine, L. Delannay, H. Idrissi, M.-S. Colla, T. Pardoen, Dislocation and back stress dominated viscoplasticity in freestanding sub-micron Pd films, Acta Mater. 111 (2016) 10–21. doi:10.1016/j.actamat.2016.03.038.
[155] G.I. Taylor, Plastic strain in metals, Twenty-Eighth May Lect. to Inst. Met. (1938) 307–325.
[156] J.L. Chaboche, A review of some plasticity and viscoplasticity constitutive theories, Int. J. Plast. 24 (2008) 1642–1693. doi:10.1016/j.ijplas.2008.03.009.
[157] G. Pintsuk, A. Prokhodtseva, I. Uytdenhouwen, Thermal shock characterization of tungsten deformed in two orthogonal directions, J. Nucl. Mater. 417 (2011) 481–486. doi:10.1016/j.jnucmat.2010.12.109.
[158] T. Hirai, G. Pintsuk, J. Linke, M. Batilliot, Cracking failure study of ITER-reference tungsten grade under single pulse thermal shock loads at elevated temperatures, J. Nucl. Mater. 390–391 (2009) 751–754. doi:10.1016/j.jnucmat.2009.01.313.
[159] M. Li, E. Werner, J.-H. You, Cracking behavior of tungsten armor under ELM-like thermal shock loads: A computational study, Nucl. Mater. Energy. 2 (2015) 1–11. doi:10.1016/j.nme.2014.10.001.
[160] C. Bohnert, S.M. Weygand, N.J. Schmitt, R. Schwaiger, O. Kraft, Numerical Investigation of the Fracture Behavior of Tungsten at the Micro Scale, in:
Bibliography
155
13th Int. Conf. Fract., Beijing, 2013.
[161] L. Delannay, Observation and modelling of grain interactions and grain subdivision in rolled cubic polycrystals, Katholieke Universiteit Leuven, 2001.
[162] E.B. Marin, P.R. Dawson, On modelling the elasto-viscoplastic response of metals using polycrystal plasticity, Comput. Methods Appl. Mech. Eng. 165 (1998) 1–21. doi:10.1016/S0045-7825(98)00034-6.
[163] U.F. Kocks, A.S. Argon, M.F. Ashby, Thermodynamics and kinetics of slip, 1975.
[164] H.J. Frost, M.F. Ashby, Deformation mechanism maps: the plasticity and creep of metals and ceramics, 1982.
[165] P.S. Follansbee, U.F. Kocks, A constitutive description of the deformation of copper based on the use of the mechanical threshold stress as an internal state variable, Acta Metall. 36 (1988) 81–93. doi:10.1016/0001-6160(88)90030-2.
[166] A. Zinovev, D. Terentyev, L. Delannay, Finite element analysis of heat load of tungsten relevant to ITER conditions, Phys. Scr. T170 (2017) 014002. doi:10.1088/0031-8949/2017/T170/014002.
[167] V.A. Makhlaj, I.E. Garkusha, S. V. Malykhin, A.T. Pugachov, I. Landman, J. Linke, S. Pestchanyi, V. V. Chebotarev, V.I. Tereshin, Residual stresses in tungsten under exposures with ITER ELM-like plasma loads, Phys. Scr. T138 (2009) 014060. doi:10.1088/0031-8949/2009/T138/014060.
[168] R. Coppola, F. Crescenzi, W. Gan, M. Hofmann, M. Li, E. Visca, J.-H. You, Neutron diffraction measurement of residual stresses in an ITER-like tungsten-monoblock type plasma-facing component, Fusion Eng. Des. 146 (2019) 701–704. doi:10.1016/j.fusengdes.2019.01.059.
[169] W.A. Curtin, R.E. Miller, Atomistic/continuum coupling in computational materials science, Model. Simul. Mater. Sci. Eng. 11 (2003) R33–R68. doi:10.1088/0965-0393/11/3/201.
[170] A. Arsenlis, On the evolution of crystallographic dislocation density in non-homogeneously deforming crystals, J. Mech. Phys. Solids. 52 (2004) 1213–1246. doi:10.1016/j.jmps.2003.12.007.
[171] V. Vitek, M. Mrovec, J.L. Bassani, Influence of non-glide stresses on plastic flow: from atomistic to continuum modeling, Mater. Sci. Eng. A. 365 (2004) 31–37. doi:10.1016/j.msea.2003.09.004.
[172] Z. Zhao, W. Mao, F. Roters, D. Raabe, A texture optimization study for minimum earing in aluminium by use of a texture component crystal plasticity finite element method, Acta Mater. 52 (2004) 1003–1012. doi:10.1016/j.actamat.2003.03.001.
[173] D. Peirce, R.J. Asaro, A. Needleman, An analysis of nonuniform and localized deformation in ductile single crystals, Acta Metall. 30 (1982) 1087–1119. doi:10.1016/0001-6160(82)90005-0.
[174] M. Sachtleber, Z. Zhao, D. Raabe, Experimental investigation of plastic
Bibliography
156
grain interaction, Mater. Sci. Eng. A. 336 (2002) 81–87. doi:10.1016/S0921-5093(01)01974-8.
[175] D. Raabe, M. Sachtleber, H. Weiland, G. Scheele, Z. Zhao, Grain-scale micromechanics of polycrystal surfaces during plastic straining, Acta Mater. 51 (2003) 1539–1560. doi:10.1016/S1359-6454(02)00557-8.
[176] D. Raabe, P. Klose, B. Engl, K.-P. Imlau, F. Friedel, F. Roters, Concepts for Integrating Plastic Anisotropy into Metal Forming Simulations, Adv. Eng. Mater. 4 (2002) 169–180. doi:10.1002/1527-2648(200204)4:4<169::AID-ADEM169>3.0.CO;2-G.
[177] A.M. Korsunsky, D. Dini, F.P.E. Dunne, M.J. Walsh, Comparative assessment of dissipated energy and other fatigue criteria, Int. J. Fatigue. 29 (2007) 1990–1995. doi:10.1016/j.ijfatigue.2007.01.007.
[178] E. Charkaluk, A. Bignonnet, A. Constantinescu, K. Dang Van, Fatigue design of structures under thermomechanical loadings, Fatigue Fract. Eng. Mater. Struct. 25 (2002) 1199–1206. doi:10.1046/j.1460-2695.2002.00612.x.
[179] R.P. Skelton, C.J. Rees, G.A. Webster, Energy damage summation methods for crack initiation and growth during block loading in high-temperature low-cycle fatigue, Fatigue Fract. Eng. Mater. Struct. 19 (1996) 287–297. doi:10.1111/j.1460-2695.1996.tb00967.x.
[180] R.P. Skelton, Cyclic hardening, softening, and crack growth during high temperature fatigue, Mater. Sci. Technol. 9 (1993). doi:10.1179/mst.1993.9.11.1001.
[181] A. Manonukul, F.P.E. Dunne, High- and low-cycle fatigue crack initiation using polycrystal plasticity, Proc. R. Soc. A Math. Phys. Eng. Sci. 460 (2004) 1881–1903. doi:10.1098/rspa.2003.1258.
[182] C.A. Sweeney, B. O’Brien, P.E. McHugh, S.B. Leen, Experimental characterisation for micromechanical modelling of CoCr stent fatigue, Biomaterials. 35 (2014) 36–48. doi:10.1016/j.biomaterials.2013.09.087.
[183] C.A. Sweeney, W. Vorster, S.B. Leen, E. Sakurada, P.E. McHugh, F.P.E. Dunne, The role of elastic anisotropy, length scale and crystallographic slip in fatigue crack nucleation, J. Mech. Phys. Solids. 61 (2013) 1224–1240. doi:10.1016/j.jmps.2013.01.001.
[184] K.S. Cheong, M.J. Smillie, D.M. Knowles, Predicting fatigue crack initiation through image-based micromechanical modeling, Acta Mater. 55 (2007) 1757–1768. doi:10.1016/j.actamat.2006.10.038.
[185] D.L. McDowell, F.P.E. Dunne, Microstructure-sensitive computational modeling of fatigue crack formation, Int. J. Fatigue. 32 (2010) 1521–1542. doi:10.1016/j.ijfatigue.2010.01.003.
[186] H. Lim, C.C. Battaile, J.D. Carroll, B.L. Boyce, C.R. Weinberger, A physically based model of temperature and strain rate dependent yield in BCC metals: Implementation into crystal plasticity, J. Mech. Phys. Solids. 74 (2015) 80–96. doi:10.1016/j.jmps.2014.10.003.
[187] N. Kowalski, L. Delannay, P. Yan, J.-F. Remacle, Finite element modeling
Bibliography
157
of periodic polycrystalline aggregates with intergranular cracks, Int. J. Solids Struct. 90 (2016) 60–68. doi:10.1016/j.ijsolstr.2016.04.010.
[188] A.S. Krausz, K. Krausz, Unified Constitutive Laws of Plastic Deformation, Academic Press, Ontario, Canada, 1996.
[189] D.F. Li, R.A. Barrett, P.E. O’Donoghue, N.P. O’Dowd, S.B. Leen, A multi-scale crystal plasticity model for cyclic plasticity and low-cycle fatigue in a precipitate-strengthened steel at elevated temperature, J. Mech. Phys. Solids. 101 (2017) 44–62. doi:10.1016/j.jmps.2016.12.010.
[190] W.D. Nix, H. Gao, Indentation size effects in crystalline materials: A law for strain gradient plasticity, J. Mech. Phys. Solids. 46 (1998) 411–425. doi:Doi 10.1016/S0022-5096(97)00086-0.
[191] R.J. Dorgan, G.Z. Voyiadjis, Nonlocal dislocation based plasticity incorporating gradients of hardening, Mech. Mater. 35 (2003) 721–732. doi:10.1016/S0167-6636(02)00202-8.
[192] G.Z. Voyiadjis, Handbook of Nonlocal Continuum Mechanics for Materials and Structures, Springer International Publishing, Cham, 2019. doi:10.1007/978-3-319-58729-5.
[193] T.J. Massart, T. Pardoen, Strain gradient plasticity analysis of the grain-size-dependent strength and ductility of polycrystals with evolving grain boundary confinement, Acta Mater. 58 (2010) 5768–5781. doi:10.1016/j.actamat.2010.06.052.
[194] C. Brugger, M. Coulombier, T.J. Massart, J.-P. Raskin, T. Pardoen, Strain gradient plasticity analysis of the strength and ductility of thin metallic films using an enriched interface model, Acta Mater. 58 (2010) 4940–4949. doi:10.1016/j.actamat.2010.05.021.
[195] M. Mahler, E. Gaganidze, J. Aktaa, Simulation of anisotropic fracture behaviour of polycrystalline round blank tungsten using cohesive zone model, J. Nucl. Mater. 502 (2018) 213–219. doi:10.1016/j.jnucmat.2018.02.001.
[196] L. Delannay, P. Yan, J.F.B. Payne, N. Tzelepi, Predictions of inter-granular cracking and dimensional changes of irradiated polycrystalline graphite under plane strain, Comput. Mater. Sci. 87 (2014) 129–137. doi:10.1016/j.commatsci.2014.02.008.
[197] A. Cornec, I. Scheider, K.-H. Schwalbe, On the practical application of the cohesive model, Eng. Fract. Mech. 70 (2003) 1963–1987. doi:10.1016/S0013-7944(03)00134-6.
[198] M. Wirtz, A. Kreter, J. Linke, T. Loewenhoff, G. Pintsuk, G. Sergienko, I. Steudel, B. Unterberg, E. Wessel, High pulse number thermal shock tests on tungsten with steady state particle background, Phys. Scr. T170 (2017) 014066. doi:10.1088/1402-4896/aa909e.
[199] S. Wurster, B. Gludovatz, A. Hoffmann, R. Pippan, Fracture behaviour of tungsten-vanadium and tungsten-tantalum alloys and composites, J. Nucl. Mater. 413 (2011) 166–176. doi:10.1016/j.jnucmat.2011.04.025.